Evolution of ferronickel particles during the reduction of low-grade saprolitic laterite nickel ore by coal in the temperature range of 900–1250℃with the addition of CaO–CaF2–H3BO3

The method of producing ferronickel at low temperature(1250–1400℃)has been applied since the 1950s at Nippon Yakin Kogyo,Oheyama Works,Japan.Limestone was used as an additive to adjust the slag composition for lowering the slag melting point.The ferronickel product was recovered by means of a magnetic separator from semi-molten slag and metal after water quenching.To increase the efficiency of magnetic separation,a large particle size of ferronickel is desired.Therefore,in this study,the influences of CaO,CaF₂,and H₃BO₃ additives on the evolution of ferronickel particle at≤1250℃were investigated.The experiments were conducted at 900–1250℃with the addition of CaO,CaF₂,and H₃BO₃.The reduction processes were carried out in a horizontal tube furnace for 2 h under argon atmosphere.At 1250℃,with the CaO addition of 10 wt%of the ore weight,ferronickel particles with size of 20μm were obtained.The ferronickel particle size increased to 165μm by adding 10 wt%CaO and 10 wt%CaF₂.The addition of boric acid further increased the ferronickel particle size to 376μm,as shown by the experiments with the addition of 10 wt%CaO,10 wt%CaF₂,and 10 wt%H₃BO₃.     

稻砂土吸附铜镍铅砷能力的比较

通过对砂壤水稻土中Cu,Ni,Pb,As4种元素的单元及复合吸附试验,表明其吸附热力学符合Freundlich方程,吸附能力为Pb Cu>As>Ni.共存元素对土壤吸附某一元素的能力影响不大;用Langmuir方程粗略地估算出这4种元素在土壤中的化学容量.     

Electrocatalytic Oxidation of H_2 O_ 2 at a Carbon Paste Electrode Modified with a Nickel (Ⅱ)-5,11,17,23-Tetra-Tert-Butyl-25,27-Bis(Diethylcarbamoylmethoxy)Calix[4] Arene Complex and Its Application

0　IntroductionThegreatimportanceofnickelelectrochemistryinalkalinemedium ,especiallyforpotentialapplication ,hasattractedmuchattetionofresearcherseithertostudythebehaviorofnickel basedelectrodeitselforitsactivitytowardsothermolecules.Manyreportsshowedthatthenickelbasedelectrodeshaveelectro catalyticactivityforreactionsofappliedinterest,suchaselectro chemicaldeterminationofantioxidantsinfood[1 ] ,detectionofni tricoxide (NO )insolution[2 ] ,electrocatalyticoxidationofmethanol[1 ] ,alcohol[3] ,…     

化学镀镍过程中金属基体的引发催化特性研究

通过电位-时间曲线的特征,研究了化学镀镍反应初期不同基体材料的催化特征.在同质基体上可以瞬间诱发化学镀反应,而在异质基体上的诱导期因镀液组成不同而发生变化.在异质基体材料中,Pt无催化活性,Pd的诱发时间最长.     

高功率型镍氢电池的循环性能

由于没有镉污染,对环境友好,用于高功率设备的镍氢电池的需求量增长很快,目前每年的需求量约为5亿只.但是镍氢电池的一些性能还不能完全满足电动工具的使用要求,突出表现在电池大电流充放循环寿命较差.因此,研制高性能的高倍率镍氢电池不仅具有重要的研究意义,也有很大的应用价值.本文研究影响SC型动力电池循环寿命衰减的主要因素,测量了在大电流循环过程中镍氢电池的内阻、温度及重量变化,并运用SEM、XRD对电池内阻升高的原因进行了分析.我们认为电池内阻升高是镍氢电池大电流循环寿命差的主要原因,分析发现在镍氢电池进行大电流充放电循环时,电池正极膨胀,负极微粉化,电池内部孔隙率增加,致使电解液干涸,电池内阻升高.通过增加负极容量,抑制正极膨胀,可以有效改进镍氢电池大电流充放时的循环性能.     

NiTi合金表面氧化对镍离子释放的影响

采用原子吸收分光光度计,分别测试经机械抛光和高温氧化后的NiTi合金样品在人体生理模拟液中镍离子的释放速度,结果表明NiTi合金表面氧化膜的形成可以有效地减少镍离子的溶出.     

1-(6-硝基-2-苯并噻唑)-3-(4-硝基苯)-三氮烯与镍显色反应的研究及应用

在TritonX-100表面活性剂存在下,研究了1-(6-硝基-2-苯并噻唑)-3-(4-硝基苯)-三氮烯(NBTNPT)与镍的显色反应.在pH为10.0～11.5的Na2B4O7-NaOH缓冲溶液中,该试剂与镍生成2∶1配合物.以500nm为参比波长,440nm为测定波长的双峰双波长进行测定,表观摩尔吸光系数为1.84×105L·mol-1·cm-1.Ni2+的浓度在0～280μg/L内符合比耳定律.用拟定方法测定钢铁中的微量镍,结果满意.     

氯离子诱导的镍在硝酸溶液中的电流振荡

报道了氯了子诱导的镍在0．5mol.dm^-2硝酸溶液中活化－钝化过渡区电流振荡，在恒电位条件下，随着氯离子浓度的升高或者电极电位的降低，电流振荡由周期性振荡逐渐向非周期性振荡转变，根据实验结果，对该体系的电流振荡机理进行了讨论。     

电化学制氢联产球形氢氧化镍的研究

水电解制氢的同时,阳极电解生成副产品氢氧化镍,该工艺制氢电耗约为2.5 kW·h.研究了电解质浓度、氢氧化镍沉淀浓度等对电解电压和电流效率的影响,并对影响氢氧化镍振实密度的主要因素包括电流密度、温度、搅拌速度、滤饼含水量、烘干温度等进行了分析,从而得出了最佳实验条件.X射线衍射、原子力显微镜等表征结果表明,制得的氢氧化镍为β型,形状呈椭球形,粒度分布比较均匀.     

C60Ni(PPh3)2配合物的合成和性质研究

采用配体取代法合成出C60Ni(PPh3)2，利用元素分析、红外光谱、光电子能谱对产物进行表征，研究了产物的热稳定性和氯化还原性能。