轧制道次间插入冷却对特厚钢板组织与性能的影响

使用实验轧机旁冷却装置配合轧机进行轧制实验，研究轧制道次间不同冷却工艺对特厚钢板组织和性能的影响规律.研究结果表明:采用道次间冷却工艺可以在全厚度方向获得组织细化及强韧性提高效果，采用强冷道次间冷却实验钢1/4处晶粒尺寸可细化至10μm，强度为376MPa，-40℃冲击功为169J;心部晶粒尺寸可细化至15μm，强度为360MPa，-40℃冲击功为123J.本工艺可形成470μm厚表层细晶层，晶粒尺寸可细化至5μm;粗轧道次间插入冷却工艺轧制钢板强度和冲击韧性优于中间坯冷却工艺;随冷却强度增加，钢板内部组织明显细化且强度大幅提高.     

基于弦振动测量金属细线的线密度

提出了一种测量金属细线线密度的新方法,并对测量原理、公式进行了较为详细的推导,将测量结果与标准值进行了比较.从测量结果可知,其相对误差较小,说明利用该方法测量细线的线密度确实可行.     

Microstructure,mechanical properties and wear resistance of an Al–Mg–Si alloy produced by equal channel angular pressing

Microstructure, mechanical properties and wear resistance in an ultrafine-grained Al–Mg–Si alloy fabricated utilizing a combination of equal channel angular pressing (ECAP) and dynamic aging were investigated in this paper. The results indicated that the grain size of the ECAP alloy was significantly refined, i.e., to ~239 nm after three ECAP passes. Meanwhile, the yield and tensile strength of the ECAPed material reached 340 MPa and 445 MPa, respectively, while maintaining a significant uniform elongation of 14%. Wear resistance results demonstrated that the wear rate, wear depth and width of the ECAPed material decreased in comparison with the solution-treated (SST) and peak-aged (T6) conditions under a load range of 5–25 N. The adhesive wear that occurs in the undeformed specimens at 10 N does not appear in the ECAPed specimen at the same load, indicating that the ECAPed specimen delay the appearance of more serious wear mechanisms under certain loads. The cooperative interaction of high density nano-scale β" precipitates and dislocations resulted in a combination of super-high strength and good work hardening ability which suppressed the extension of cracks between the friction layer and the plastic deformation zone. As a consequence, the combination of ECAP and dynamic aging brings a significant improvement for antifriction performance of the 6061 aluminum alloy.     

Effect of heat treatment on microstructures and properties of a novel Al-Zn-Mg-Cu alloy for oil drilling

In view of the special requirements for strength, heat resistance and corrosion resistance of Al-Zn-Mg-Cu alloy for oil drilling, the Al-6.2 Zn-2.5 Mg-1.6 Cu alloy was prepared by increasing Cu content on basis of Russian Series 1953 alloy. The effect of heat treatment on the microstructures and properties of the alloy was characterized by optical microscope(OM), scanning electron microscope(SEM) and transmission electron microscope(TEM), and investigated by tensile test at room temperature, thermal exposure test and corrosion test. The results show that the strength after T6 aging treatment exhibit a decrease trend as an increase of the solution temperature from465 °C to 480 °C. After the solution treated by the rate of 470 °C/1 h, second phases dissolve into the matrix very well and the strength property reaches optimum. The alloy has better comprehensive properties treated by a solution treatment of 470 °C/1 h and then followed by an aging treatment of 120 °C/24 h + 170 °C/1 h + 120 °C/24 h. Under the aging state, the precipitated phases inside the grains are suitable in size, while on the grain boundary distribute discontinuously and the precipitate-free zone is obvious. Besides, the alloy still maintain high tensile properties. The yield strength, tensile strength and elongation are 650 MPa, 686 MPa,12.0%, respectively. The yield strength retention after heat exposure is 92%. The alloy has good corrosion resistance and the exfoliation corrosion degree. The average corrosion rate in the H_2S and CO_2 environment is 0.0024 mm/a, which is far less than the required 0.12 mm/a. It is insensitive to H_2S and CO_2 environments.     

La$_{{1-x}}$Sr$_{x}$TiO$_{3}$ 薄膜的高通量 X 射线衍射

高通量材料合成方法和高通量材料表征手段区别于传统低效率的 "试错法"材料发展方法, 极大地加速了材料科学的变革和发展. 通过设计程序进行了高通量 X 射线衍射实验, 在保证数据分辨率条件下, 高效地表征了 La$_{1-x}$Sr$_{x}$TiO$_{3}$ 薄膜上多个数据位点的晶体结构, 验证了其成分的连续变化性质, 为后续开展更多类型的高通量 X 射线衍射实验提供了指导.     

冷轧带钢局部高点卷取过程起筋控制的建模与仿真

为了研究带钢局部高点卷取起筋的控制方法，利用三维弹塑性变形基本理论，并引入带钢塑性流动因子，建立了弹塑性卷取应力和起筋量模型.基于应力函数假设、S. Timoshenko最小功原理和伽辽金虚位移法建立了起筋带钢的应力场分布和可用于在线计算的起筋临界卷取张力设定模型.仿真结果表明：局部高点在径向累积叠加所引起的带钢张力不均匀分布和轴向压应力是导致带钢起筋的主要原因；起筋量随局部高点高度、卷径和卷取张力增加而增大，薄带钢比厚带钢起筋量增幅明显；临界卷取张力随卷径、带钢厚度和局部高点高度增大而减小.     

智能高速罐身电阻焊机数字化控制系统

提出了以国产MCT80 0 0F8运动控制器为核心的智能高速罐身电阻焊机数字化控制系统 ,并介绍了系统的组成、工作原理、硬件接口、电机控制方法以及伺服电机的运动关系数学模型 .新的系统有利于提高罐身电阻焊机的制罐生产速度 ,并具有功能全面、可靠性高、控制精确、开放性好以及成本较低等优点     

碳钢在NaHCO3+NaCl溶液中的亚稳态孔蚀特征

用动电位极化和恒电位极化法研究了A3碳钢在不同浓度NaCl的0.5mol/LNaHCO₃溶液中亚稳态孔蚀行为。实验发现亚稳态电流波动峰具有快速上升、缓慢下降的特点。亚稳孔出现电位E_m 服从正态分布,随着Cl^-浓度的提高,E_m 值向负方向移动。亚稳孔的峰频变化规律与电位关系不大。恒电位极化时,当电位高于E_m而大大低于孔蚀电位E_b 时,电流波动保持一定时间后会最终消失,并产生直径为微米级的小蚀孔。当电位接近孔蚀电位时,一段时间的电流波动后电流往往迅速上升,最终转变为稳定蚀孔.     

焊接过程的RBF神经网络建模

介绍了RBF神经网络的性能和算法结构 ,建立了RBF神经网络在船舶焊接过程中用于焊接变形预测分析的模型 ,并探讨了其应用和发展趋势     

NIPA类共聚温敏水凝胶中水的状态和耐热性

用N-异丙基丙烯酰胺（NIPA）与丙烯酸钠（SA）及甲基丙烯酸钠（SMA）共聚合成了两个系列的水凝胶，研究了共聚组成与水凝胶基本性质的关系，并用示差扫描量热法（DSC）和热失重法（TG）研究了此类水凝胶中水的状态和耐热性。