Analysis of Pyrolysates for Phenol Formaldehyde Resin by Py-GC/MS

Pyrolysis of phenol formaldehyde resin has been investigated by Pyrolysis Gas Chromatography-Mass Spectroscopy at the different temperatures from 500℃ to 750℃. Its composition of pyrclysates has been analyzed. Several compounds, especially benzene, toluene, p-xylene could only be formed above 500-550℃. Howerver, peak intensities for some pbend derivatives were decreased at the higher temperature. During pyrolysis, for thermo-setting phenol formaldehyde resins, polymeric chain scissions take place as a successive removal of the monomer units from the polymeric chain. The chain scissions are followed by secondary reactions, which leads to a variety of compounds. Addition reactions can also take place among the double-bond compounds during pyrolysis.     

乙烷—丙烷混合裂解模型及产率预计

本文研究了乙烷和丙烷的混合裂解,并与乙烷、丙烷单独裂解进行了比较。解决了微分方程组的刚性问题,提出了混合裂解反应动力学模型。明确了三种选择性的概念,即;真实选择性、迭加选择性和总选择性,从而澄清了国际上对于选择性有正偏差和负偏差的不同观点。为乙烯生产提供了有效利用乙烷和丙烷的分析评价方法。     

Solid-state Synthesis of Carbon-nanostructures

1 Results In addition to single wall and multiwall carbon nanotubes[1], several structures,which are more or less related to fullerenes,including carbon nanohorns[2a], carbon nanospheres[2b] and onion like carbon structures[2c] have been reported.A new simple straight forward method to access some of these structures is the solid-state pyrolysis of different organometallic complexes in a sealed vessel,which led so far to carbon nanotubes[3a,b], carbon nanocables[3c] and onions[3d].     

1673K下BaO-BaF_2-Cr_2O_3渣系的热力学性质

１６７３Ｋ下,采用－ＭｏＣｒ＋Ｃｒ２Ｏ３ＺｒＯ２（ＭｇＯ）｛Ｃｕ＋Ｃｒ｝ａｌｏｙ＋（Ｃｒ２Ｏ３）ｓｌａｇＭｏ＋固体电解质电池测定了ＢａＯＢａＦ２Ｃｒ２Ｏ３渣系中Ｃｒ２Ｏ３的活度．研究结果表明,Ｃｒ２Ｏ３的活度随其浓度升高而升高,随ＸＢａＯ／ＸＢａＦ２升高而降低．根据实验及Ｘ射线衍射结果推测了该渣系的等温相图,并作出了该渣系中Ｃｒ２Ｏ３的等活度图．     

煤中前沥青烯与沥青烯性质的研究

煤的溶剂抽出物中前沥青烯与沥青烯的质量之比随煤化程度增加而增加。原位热解红外光谱研究结果表明,它们的热稳定性与其结构参数有关,芳香度高,甲基取代结构多的前沥青烯比沥青烯的热稳定性好。前沥青烯与沥青烯在溶剂分级过程中表现出的溶解性与其结构参数无必然联系,而与其酸碱组分间的氢键强度有关。前沥青烯中酸碱组分间的氢键强度为５．１５～３０．９ｋＪ／ｍｏｌ;沥青烯为＜５．１５ｋＪ／ｍｏｌ。     

瓶盖加工模具的失效分析

对瓶盖加工模具在生产使用中突然出现的裂纹及崩刃等现象进行了分析,指出失效的主要原因是原热处理工艺不当使其硬度偏高所致．鉴于此,本文对其进行了实验研究,并制定了新工艺．     

CO2监测分析仪在监测过程中对桥室温度的恒温控制

CO2监测分析仪在监测过程中,CO2监测值的精度是由CO2监测分析仪的桥室参比温度是否恒定而决定的.老式监测分析仪桥室温度是采用断续的双位恒温调节,其温度调节误差大,一般只能在±1℃左右,所以CO2监测值的精度低.采用微机交流调压的CO2监测分析仪桥室恒温调节,其温度调节器采用PID调节,使桥室温度误差可控制在±0.2℃,提高了CO2监测值的监测精度.     

阻燃剂聚苯基膦酸二苯偶氮酯对PET阻燃作用机理研究

用热重分析(TGA)和热裂解色谱(PGC—MS)研究了阻燃剂聚苯基膦酸二苯偶氮酯(PAPPP)对聚对苯二甲酸乙二醇酯(PET)的阻燃作用机理。TGA结果表明PAPPP／PET(15／85)共混物的起始分解温度为337℃，550℃的热解残余量为26．8％，450℃～550℃的失重为23．3％，与纯PET相比，共混物的热解温度范围变宽，残余量增加，且在PET燃点附近的可燃性挥发气体的生成量降低，表现为凝聚相阻燃机理．PGC—MS分析表明，加入PAPPP对PET的热裂解模式有一定影响，在燃烧过程中伴有酯交换反应．     

超声喷雾热分解法制备电极材料LiCoO2薄膜

以硝酸锂和乙酸钴为原料,玻璃为基片,通过超声喷雾热分解法制备了锂钴氧化物薄膜,并讨论了制备条件对形成薄膜如Li与Co摩尔比对薄膜晶型、不同溶剂对雾化效果、热分解温度对产物晶型和薄膜外观、反应时间对膜厚等的影响,经X-射线衍射分析和电镜测试,给出了制备较好晶型结构LiCoO2薄膜的条件.     

低温热解脱氧方法研究

为研究低煤化度煤含氧官能团的化学活性及其改性机理，通过对低温热解方法条件的确定，建立了实验室规模低温热解脱氧方法，进一步考察了该方法的效果。结果表明，在实验室采用此法研究低煤化度煤低温热解脱氧是可行的。