强直电流伸展弧CVD硬质合金金刚石涂层工具

采用自行研制的强电流直流扩展电弧设备对酸浸和渗硼预处理的YG6刀片进行了金刚石薄膜涂层沉积，并对放于不同位置的沉积刀片表面涂层的激光Raman谱和SEM形貌进行了分析、研究。结果表明：渗硼预处理工艺优于酸浸预处理工艺；在渗硼处理的GY6刀片上，沉积的金刚石薄膜涂层具有大面积、均匀性好和质量高的特点。     

Fabrication and Application of High Quality Diamond-coated Tools

Diamond-coated tools were fabricated using Co-cemented carbide inserts as substrates by the electronically aided hot filament chemical vapor deposition (EACVD). An amount of additive in an acid solution was used to promote the Co etching of the substrate surface. The surface of the WC-Co substrate was decarburized by microwave plasma with Ar-H 2 gas. Effect of the new substrate pretreatment on the adhesion of diamond films was investigated. A boron-doped solution was brushed on the tool surface to diffuse ...     

WC—Co硬质合金刀片热丝法金刚石薄膜涂层附着力

用热丝法研究了ＷＣ－６％Ｃｏ硬质合金刀片金刚石薄膜涂层附着力。结果表明：采用温度为８０℃,（ＨＣｌ：ＨＮＯ３：Ｈ２Ｏ）（体积比）为１∶１∶１溶液对硬质合金刀片表面去Ｃｏ１５ｍｉｎ后,经４０ｕｍ金刚石粉及１．５ｕｍ金刚石加２０ｕｍＴａＣ混合粉进行超声预处理,结果表明,沉积的金刚石薄膜与硬质合金刀片基底具有良好的附着力,而经４０ｕｍ金刚石粉处理的薄膜涂层组织与附着力要好一些。     

Diamond synthesis from a system of chromium-carbide and Ni70Mn25Co5 alloy

In order to ascertain the mechanism of interaction between carbide and metallic catalyst and formation of diamond under high pressure and high temperature, and find a new method to synthesize diamond with special properties, it is necessary to investigate the reaction behavior of different carbides and metallic solvent_catalysts under high pressure and high temperature. A system of Cr-3C-2 powder and Ni 70Mn 25Co 5 alloy in weight ratio of 1∶6 was treated under 6 0 GPa and 1 500℃ for 20, 30 or 60 min respectively. X_ray diffraction of the samples indicated the Cr 3C 2 decomposed partially after high pressure and temperature treatment, and Cr 7C 3, Cr and diamond formed respectively. There was not any trace of graphite in the samples. The result suggested that the separated carbon atoms could form diamond directly without conversion process of graphite into diamond. The observation of SEI, WDX and EDX also showed that diamond crystals were synthesized in the system, which have perfect surfaces and shapes, with the average grain size of about 40 μm. The properties of the crystals are being investigated.     

用参数变换方法研究—族钻石分形晶格上Ising模型的相变

采用英国著名学者Stinchcombe提出的理论方法——参数变换，研究了一族钻石分形晶格上Ising模型的相变和临界性质，结果表明：与实空间部分格点消约(decimation)RG变换的结果完全一致．这似乎暗示着用该方法精确求解其他等级晶格上的离散自旋模型是有效的．     

P型掺杂金刚石电极双电层电容器研究

金刚石具有的一系列优良特性使其成电极材料的重要选择之一，采用P型掺杂金刚石薄膜电极可制备具有一定应用价值的双电层电容器．本文介绍了金刚石薄膜电极电化学双层电容器的基本原理、结构和主要参数．并通过对实验制备出的电容器进行相关参数的测定，证明了以P型掺杂金刚石为电极材料的双电层电容器具有优良的特性和良好的应用前景．     

磁透镜技术及其在沉积金刚石/类金刚石薄膜中的应用

阐明了磁透镜原理，依照磁透镜理论和几何光学理论，给出一种确定磁透镜位置的方法。并将磁透镜技术应用到直流等离子射流化学沉积金刚石薄膜／类金刚石薄膜装置中，很好地消除了边界效应，实现高速大面积沉积高纯度金刚石薄膜／类金刚石薄膜的目标。     

等离子体离子注入类金刚石多层膜机械特性

采用非平衡磁控溅射及等离子体离子混合注入方法在奥氏体不锈钢 1 Cr1 8Ni9Ti基体上制备 N/ Ti N/ Ti(N,C) / DLC梯度膜 .研究了类金刚石 (DLC)梯度膜的结构特征和力学性能 .试验结果表明 ,N/ Ti N/ Ti(N,C) / DLC梯度膜最外层为典型的 DLC层 .梯度膜的硬度、弹性模量、断裂韧性以及界面结合强度值分别为 1 9.84GPa、1 90 .0 3GPa、3.75MPa· m1/ 2和 5.68MPa·m1/ 2 .试验所制备的 DLC多层膜比 DLC单层膜具有更好的综合机械性能 .     

金刚石磨粒切削运动分析及切削厚度计算

在分析金刚石锯片刀头运动轨迹的基础上，根据金刚石锯片的切削运动方程，得出了金刚石磨粒最大切削厚度的计算公式，提出了切削过程中两个新的观点：（１）单颗粒金刚石锯切掉的岩石其水平距离是不变的；（２）切削厚度是按正弦规律变化的，这给锯片设计和正确使用提供了可靠的依据     

用热激发电流法研究金刚石薄膜中的陷阱

对微波等离子体化学气相沉积（ＭＰＣＶＤ）的硅衬底金刚石薄膜，做了在液氮温区注入载流子，升温测其电流－温度关系的实验，观察到ａｓ－ｇｒｏｗｎ样品有明显的热激发电流峰，重复实验时，峰基本消失，经氢等离子体在￣９００℃处理２．５ｈ后，再重复实验，该峰又出现，推断热激发电流峰是由硅衬底金刚石薄膜内氢致陷阱中的载流子撤空引起的，这些能级在金刚石禁带中的陷阱是可以通过热处理消除的。