基于多材质复合管柱的裸眼井壁支撑工艺及应用

已完钻超深裸眼水平井侧钻技术是经济、高效开发油藏剩余油的主要手段之一，传统的磨铣钢套管开窗侧钻技术存在下入摩阻大、磨铣耗时长导致开窗失败等问题。为此，提出了基于多材质复合管柱的超深水平井裸眼井壁支撑工艺，结合中国西北油田已完钻超深裸眼水平井井况，首先，提出了基于“铝合金+碳钢”的多材质复合管柱组合及设计方法；其次，开展了基于管柱实物屈曲实验数据的管柱临界屈曲载荷计算模型适用性评价，并优选出了适合于“铝合金+碳钢”多材质复合管柱的屈曲临界载荷计算模型；最后，研究了综合考虑管柱扭矩、摩阻、刚性、井眼条件、管柱强度及材质的多材质复合管柱下入性分析方法，并利用下入性分析软件对西北油田顺北X1井、X2井、X3井、X4井复合管柱进行了下入可行性评价。该方法在X1井和X2井得到成功应用，进一步论证了该工艺现场应用的可行性。研究成果可为超深水平井裸眼井壁支撑的复合管柱设计和下入可行性评价提供理论参考。     

轧制道次间插入冷却对特厚钢板组织与性能的影响

使用实验轧机旁冷却装置配合轧机进行轧制实验，研究轧制道次间不同冷却工艺对特厚钢板组织和性能的影响规律.研究结果表明:采用道次间冷却工艺可以在全厚度方向获得组织细化及强韧性提高效果，采用强冷道次间冷却实验钢1/4处晶粒尺寸可细化至10μm，强度为376MPa，-40℃冲击功为169J;心部晶粒尺寸可细化至15μm，强度为360MPa，-40℃冲击功为123J.本工艺可形成470μm厚表层细晶层，晶粒尺寸可细化至5μm;粗轧道次间插入冷却工艺轧制钢板强度和冲击韧性优于中间坯冷却工艺;随冷却强度增加，钢板内部组织明显细化且强度大幅提高.     

Effect of Al on microstructure and mechanical properties of as-extruded Mg–1Mn alloy sheet

The effect of Al addition on microstructure and mechanical properties of hot extruded Mg–1 Mn alloy sheet was investigated. The results revealed that the dynamic recrystallization was promoted by increasing Al content. The ultimate tensile strength and yield strength of the alloy increased with the increase of Al content. The Mg–9 Al–1 Mn alloy exhibited the highest strength, with tensile strength of 308 MPa, 307 MPa, 319 MPa, yield strength of 199 MPa, 207 MPa, 220 MPa and the elongation of 20.9%, 20.1%, 19.2% in 0°, 45°, 90°, respectively.The high strength was mainly attributed to the formation of fine dynamically recrystallized grains and large amounts of the second phase. The strengthening mechanism of the alloys was explained.     

Effect of heat treatment on microstructures and properties of a novel Al-Zn-Mg-Cu alloy for oil drilling

In view of the special requirements for strength, heat resistance and corrosion resistance of Al-Zn-Mg-Cu alloy for oil drilling, the Al-6.2 Zn-2.5 Mg-1.6 Cu alloy was prepared by increasing Cu content on basis of Russian Series 1953 alloy. The effect of heat treatment on the microstructures and properties of the alloy was characterized by optical microscope(OM), scanning electron microscope(SEM) and transmission electron microscope(TEM), and investigated by tensile test at room temperature, thermal exposure test and corrosion test. The results show that the strength after T6 aging treatment exhibit a decrease trend as an increase of the solution temperature from465 °C to 480 °C. After the solution treated by the rate of 470 °C/1 h, second phases dissolve into the matrix very well and the strength property reaches optimum. The alloy has better comprehensive properties treated by a solution treatment of 470 °C/1 h and then followed by an aging treatment of 120 °C/24 h + 170 °C/1 h + 120 °C/24 h. Under the aging state, the precipitated phases inside the grains are suitable in size, while on the grain boundary distribute discontinuously and the precipitate-free zone is obvious. Besides, the alloy still maintain high tensile properties. The yield strength, tensile strength and elongation are 650 MPa, 686 MPa,12.0%, respectively. The yield strength retention after heat exposure is 92%. The alloy has good corrosion resistance and the exfoliation corrosion degree. The average corrosion rate in the H_2S and CO_2 environment is 0.0024 mm/a, which is far less than the required 0.12 mm/a. It is insensitive to H_2S and CO_2 environments.     

激光快速成型TC4合金显微组织及力学性能

采用金相显微镜、扫描电镜、电子拉伸机等，研究了激光快速成型TC4合金沉积态在平行沉积方向和垂直沉积方向的组织和力学性能.结果表明:激光快速成型TC4合金沉积态宏观组织沿沉积方向生长的粗大β柱状晶呈明暗相间的条带状结构，具备典型的魏氏组织特征;垂直沉积方向的强度比平行沉积方向的强度高，但塑性低;合金断口为韧窝状断口，垂直沉积方向的断口韧窝尺寸比平行沉积方向的小.     

冷轧带钢局部高点卷取过程起筋控制的建模与仿真

为了研究带钢局部高点卷取起筋的控制方法，利用三维弹塑性变形基本理论，并引入带钢塑性流动因子，建立了弹塑性卷取应力和起筋量模型.基于应力函数假设、S. Timoshenko最小功原理和伽辽金虚位移法建立了起筋带钢的应力场分布和可用于在线计算的起筋临界卷取张力设定模型.仿真结果表明：局部高点在径向累积叠加所引起的带钢张力不均匀分布和轴向压应力是导致带钢起筋的主要原因；起筋量随局部高点高度、卷径和卷取张力增加而增大，薄带钢比厚带钢起筋量增幅明显；临界卷取张力随卷径、带钢厚度和局部高点高度增大而减小.     

运用试验设计法优化某军品压铸弹尾工艺

根据某军品部件出现的问题，应用试验设计法成功地找出了最优组合，提高了该部件的强度，解决了该强度问题，使生产得以正常进行。     

碳钢在NaHCO3+NaCl溶液中的亚稳态孔蚀特征

用动电位极化和恒电位极化法研究了A3碳钢在不同浓度NaCl的0.5mol/LNaHCO₃溶液中亚稳态孔蚀行为。实验发现亚稳态电流波动峰具有快速上升、缓慢下降的特点。亚稳孔出现电位E_m 服从正态分布,随着Cl^-浓度的提高,E_m 值向负方向移动。亚稳孔的峰频变化规律与电位关系不大。恒电位极化时,当电位高于E_m而大大低于孔蚀电位E_b 时,电流波动保持一定时间后会最终消失,并产生直径为微米级的小蚀孔。当电位接近孔蚀电位时,一段时间的电流波动后电流往往迅速上升,最终转变为稳定蚀孔.     

矩形型钢弯曲回弹曲率半径r值的确定

文章在分析矩形型钢弯曲变形过程及应力与应变等方面的关系的基础上，推导出工件曲率半径与工件回弹后曲率半径之间的关系，从而确定了凸模半径。     

45钢固体粉末法稀土、硼、铬、铝共渗工艺研究

研究了RE_Mg合金对固体粉末法硼、铬、铝共渗层成分、组织和性能的影响 .发现随着RE_Mg合金加入量的增加 ,渗层中Al2 O3的量不断增多 ,当RE_Mg合金加入量为 5 %时 ,渗层中出现连续致密分布的Al2 O3黑区组织 ,对此进行了性能测试和机理探讨