Polarized Emission of Molecular Film With Lanthanide (Ⅲ) Complex

1 Results In the coordination system by using complexation with organic ligand, the ff emission of lanthanide(Ⅲ) (Ln(Ⅲ)) is induced the excitation energy transfer form the organic chromophore under the light-irradiation. However, there are not so much number of reports to discuss the energy relaxation mechanism in such complexes with Ln(Ⅲ). Recently, we succeeded firstly to estimate the rate constant of the energy transfer between the ligand and Ln(Ⅲ) in Pr(Ⅲ)-phenanthroline analogs[1]. Here, we will di...     

我国最薄炉墙焦炉的设计、施工与生产

减薄炭化室炉墙是提高焦炉产量,节约能源,减少投资的重要途径之一。本文介绍我国厚80毫米炉墙焦炉的设计、施工与生产情况。     

平面汞膜电极恒电位阳极溶出极限电流方程式的推导和实验验证

本文推导出膜电极恒电位阳极溶出极限电流方程式,以平面厚汞膜电极对该式进行了实验验证。实验结果与理论式基本相符。     

Fabrication and Application of High Quality Diamond-coated Tools

Diamond-coated tools were fabricated using Co-cemented carbide inserts as substrates by the electronically aided hot filament chemical vapor deposition (EACVD). An amount of additive in an acid solution was used to promote the Co etching of the substrate surface. The surface of the WC-Co substrate was decarburized by microwave plasma with Ar-H 2 gas. Effect of the new substrate pretreatment on the adhesion of diamond films was investigated. A boron-doped solution was brushed on the tool surface to diffuse ...     

非晶硒化镉超快光电探测器瞬态响应

报道淀积条件对以非晶态硒化镉（ａ－ＣｄＳｅ）为光敏介质的超快光电探测器瞬态响应特性的影响．     

GDX—硅胶混合薄层色谱板的效率和定量性能

对用ＧＤＸ－１０２－硅胶Ｇ、有机粘合剂研制出的混合薄层板进行性能测试，评价了其在硝基苯胺异构体、酸性食品染料分离测试方面的应用，得到好的结果。     

射频溅射金属前驱体硫化法制备的Cu2ZnSnS4薄膜

采用射频溅射技术沉积Cu／Sn／Zn金属前驱体叠层结合硫化技术在玻璃衬底上成功制备了Cu2ZnSnS4薄膜。X-射线衍射分析表明，通过优化制备条件可以获得单一黝锡矿结构且具有（221）择优取向的Cu2ZnSnS4薄膜。霍尔效应和紫外可见透过谱测量表明，样品的薄膜电阻、吸收系数和光学带隙分别达到0．073Ω·cm，10^4cm^-1和1．53eV，具有适合作为薄膜太阳电池吸收层应用的可能性。     

软土中薄硬夹层的夯扩桩工程实践

结合工程实践对夯扩桩在软土中薄硬夹层的应用进行了探讨,提出薄硬夹层作为桩端持力层的加固方法.     

Preparation and properties of the SmOx/Rh(100) model surface

The preparation of SmOx/Rh(100) and CO adsorption on this model surface have been investigated with Auger electron spectroscopy (AES), X-ray photoelectron spectroscopy (XPS) and temperature programmed desorption spectroscopy (TDS). The oxygen adsorption on the SmRh alloy surface leads to the aggregation of Sm on the surface. The thermal treatment of this oxidized surface induces the further agglomeration of SmOx on the Rh(100) surface. Compared with CO TDS on the clean Rh(100) surface, three additional CO desorption peaks can be observed at 176, 331 and 600 K on the SmOx/Rh(100) surface. The CO desorption peak at 176 K may originate from CO adsorbed on SmOx islands, while the appearance of the CO adsorption peaks at 331 and 600 K, depending on the oxidation state of Sm, is attributed to CO species located at the interface of SmOx/Rh(100).