Experimental investigation and thermodynamic assessment of the yttriumhydrogen binary system

A coupled experimental investigation and thermodynamic study of the yttrium-hydrogen(Y-H) binary system were carried out to provide more comprehensive and quantitative insights into the key thermodynamic properties of this system. Y-H system in the full range of H/Y = 0–3.0 was investigated by accurate pressure composition isotherm(PCI) measurement to provide credible phase equilibria information and thermodynamic data.The phase boundaries obtained were in agreement with previous experimental data but with improved accuracy.With the guide of the crystal structures, all the solid phases were modelled using the three sublattice model. The Y-H phase diagram and thermodynamic parameters were calculated and assessed with the CALPHAD technique.The obtained results are in very good agreement with our experimental data and the published data reported in literature. The obtained thermodynamic database of Y-H system can be used to predict the hydrogenation behavior and decomposition temperatures of hydrides.     

三水合硝酸钇与冠醚18C6配合行为的研究

用改进的半微量相平衡方法研究了Y(NO_3)_3·3H_2O-18C6-CH_3OH三元体系在25℃时的溶解度,测定了饱和溶液的折光率。结果指出,在该体系中只生成一种化学计量的配合物,Y(NO_3)_3·18C6·3H_2O·1.5CH_3OH。考查了相平衡过程中水的行为。系统地比较了三水硝酸化与冠醚18C6在不同溶剂中的配合行为。考查了配合物组成与后处理条件的关系。分离中得了组成为Y(NO_3)_3·18C6·3H_2O的固态配合物,通过化学分析、红外光谱分析、DTG、TG及DSC研究了配合物的组成和性质。测得配合物的脱水和快速热分解过程的焓变值,求得了它们的表观活化能。在常量情况下,考查了配合物的热失重情况。     

6－羟基水杨酸－EDTA－溴化十六烷基三甲铵体系荧光法测定铽、镝、钐、钇、镥

探讨了６－羟基水杨酸－ＥＤＴＡ－溴化十六烷基三甲铵体系对Ｔｂ３＋、Ｄｙ３＋、Ｓｍ３＋等金属离子激发态→金属离子基态跃迁型荧光增敏及Ｙ３＋、Ｌｕ３＋对该体系配体激发态一配体基态跃迁型荧光增敏效应。开发了同时测定Ｔｂ３＋、Ｄｙ３＋Ｓｍ３＋、Ｙ３＋（Ｌｕ３＋）的新荧光体系。利用该方法成功地测定了某些稀土氧化物中的铽、、镝、钐、钇、镥含量。     

用对氯偶氮氯膦分光光度法同时测定铈与钇

本文提出了用对氯偶氮氯膦(CPApC)在0.2mol/L盐酸溶液中,于λ=678nm处测定铈与钇总量,而在同样酸度及草酸——焦磷酸钠联合掩蔽下测定铈量,由此可分别求得铈与钇的含量。测定铈与钇的表观摩尔吸光系数分别为:1.07×10~5,7.83×10~4。用此方法经过萃取分离后测定了镍基合金中的铈与钇,获得满意的结果。     

Eu~(3+)激活的La_2Na_2Sr_6(PO_4)_6Br_2和Y_2Na_2Ca_6(PO_4)_6F_2晶体中的发光中心

采用高温固相法合成了La_2Na_2Sr_6(PO_4)_6Br_2和Y_2Na_2Ca_6(PO_4)_6F_2。X射线衍射分析证明它们都为单一物相。用Sr_(10)(PO_4)_6Br_2和Ca_(10)(PO_4)_6F_2同晶指标化法进行指标化,结果表明:它们都属六方晶系的磷灰石结构,空间群为P6_3/m。计算了它们的晶胞参数。以Eu~(3+)做结构探针,研究了Eu~(3+)所处晶格的点对称性。研究表明:在La_2Na_2Sr_6(PO_4)_6Br_2中Eu~(3+)占据4f格位,为C_3点群,而在Y_2Na_2Ca_6(PO_4)_6F_2中Eu~(3+)处于6h格位,为C_6点群。     

含钇ZA—27系列合金相结构特征分析

采用Ｘ－射线衍射分析、拉伸断口扫描电镜分析及微区能谱分析方法，对添加不同钇含量的ＺＡ－２７系列锌合金的析出相进行系统分析和研究。结果表明，当钇含量在０．０３５％ｗｔ范围内，钇主要与铝生成细小、弥散的ＹＡｌ３相。当钇含量达到０．１７％ｗｔ时，合金除了生成ＹＡｌ３相外，有ＹＺｎ１２相生成，随着钇的增加，钇－锌相逐渐增多并长大，当钇含量达到或超过０．５９％ｗｔ时，合金中出现块状的钇－锌相，并有Ｙ２Ｚｎ１７相生成。     

钇在 MCrAlY 激光熔覆层中的存在形式及作用

研究了稀土元素钇（Ｙ）在激光熔覆层中的存在形式及对熔覆层抗氧化性能的影响．结果表明,Ｙ以富Ｙ粒子的形式弥散分布于基体相的晶界和晶内,净化了晶界,增强了氧化膜与基体间的粘附力,减小了氧化膜的长大速率,从而提高了熔覆层的抗氧化性能．     

压块状钇基重稀土复合球化剂的试验研究

用保温模拟法和附铸试样试验,研究了新型块状钇基重稀土复合球化剂的球化处理工艺及其球化效果和抗球衰退性。结果表明,压块状钇基重稀土复合球化剂与熔配式球化剂,按－定比率（质量分数不超过５０％）混合使用,可以获得较好的球化处理效果,可以在质量要求高的中小截面重要球铁铸件上应用。     

三水高氯酸钇与冠醚18C6间配合行为的研究

采用半微量相平衡方法研究了Y(ClO_4)_3·3H_2O-18C6-CH_3COCH_3/C_2H_5OH/CH_3OH三元体系在25℃的溶解度,测定了各饱和溶液的折光率。考察了在相平衡过程中水的行为。在3个体系中共发现了8种新配合物。系统地比较了在不同有机溶剂中的配合行为。在相平衡结果的指导下,合成制备了固态配合物,利用化学分析,IR,TG,DTG与DSc研究了固态配合物的组成和性质。