在充分考虑温度载荷、机械载荷、硬质涂层膨胀锥硬度、套管硬度对膨胀锥与套管之间屈服挤毁压强影响的基础上,根据分形理论和接触力学推导出膨胀锥与套管之间屈服挤毁压强的计算公式.数值分析表明:膨胀锥与套管之间的屈服挤毁压强随最终温度、分形粗糙度、线膨胀系数、硬质涂层膨胀锥布氏硬度、中间主应力系数、套管壁厚的增大而增大;当分形维数从1增大时,膨胀锥与套管之间的屈服挤毁压强随分形维数的增大而减小;当分形维数增大到接近于2时,膨胀锥与套管之间的屈服挤毁压强随分形维数的增大而增大;随拉压强度比的增大,膨胀锥与套管之间的屈服挤毁压强减小.屈服挤毁压强的计算值与试验测试值之间的相对误差为-8.9253%～-0.9901%.     

YAG:Ce~(3+)的包膜及其改性

溶胶-凝胶法合成了YAG:Ce3+荧光粉,测定了合成荧光粉的激发和发射光谱,研究发现包膜对荧光粉热稳定性有影响。用氧化铝和氧化镧对荧光粉包膜,会降低荧光粉的发射强度,但可明显提高荧光粉的高温稳定性。     

GH220合金渗Al层的逐层相分析

通过物理—化学相分析及其它物理手段对经900℃不同时间时效的GH220合金的渗铝层进行了逐层相分析。用联立方程分别求出离表面不同深度范围内β—NiAl相γ′相的含量。通过修正比重,对取层厚度进行了合理计算。提供了渗铝层中相变趋势。本文把计算过程全部编成程序。对微处理机在相分析中的运用作了初步尝试。     

High precision topographic data on Lop Nor basin's Lake "Great Ear" ? and the timing of its becoming a dry salt lake

High precision elevation measurements using DGPS were carried out along three representative tran- sects for the "Great Ear" area, a dry salt lake within the Lop Nor basin. Results indicate that the Lop Nor basin is only 5.2 m deep and its lowest point occurs at the center of the "Great Ear". In addition, the basin is asymmetric - steeper in the southwest (0.19‰) and gentler in the northeast (0.09‰). Points along the same "Great Ear" ring were found to have an identical elevation value, but different when from different ones (lower towards the center). The spacing of the "Great Ear" rings was found to be closely related with the surface steepness. The closer the "Great Ear" rings are spaced, the steeper the ground surface, and vice versa. These findings support the argument that the "Great Ear" rings are the former shoreline trails left behind by Lop Nor water during the last few episodes of recession towards its total dry up. A comprehensive analysis of the high precision elevation data, historical accounts, aerial and satellite photographs and imagery, and official topographic maps of the study area suggests that the "Great Ear" area in the Lop Nor basin was incorrectly mapped as being covered by a great body of water on the 1963 topographic maps. A re-interpretation of the 1958 aerial photographs and newer remote sensing imagery indicated that the "Great Ear" ring structure was already in place in 1958 and it continued to appear on the subsequent remote sensing data without any major changes. It is estimated that lake water in the "Great Ear" area of the Lop Nor basin disappeared between the late 1930s and early 1940s.     

强化传热生物质燃料热风炉研究

研制出用于粮食及其它农副产品干燥的新型热风炉。此炉型采用生物质燃料洁净燃烧技术及高强化传热技术,具有低污染、高效率、长寿命等优点。     

真空冷冻干燥机凝结器的改进

分析了真空冷冻干燥机水汽凝结器存在容易造成"冰塞"的原因,并提出了安装气流扩散器的改进方法,对改进前后的凝结器捕水性能进行了比较.由于气流扩散器的安装,捕水周期得以延长,捕水能力及工作效率显著提高,实用性较好,而且扩散器的制作费用低,性价比高,有推广价值.     

强直电流伸展弧CVD硬质合金金刚石涂层工具

采用自行研制的强电流直流扩展电弧设备对酸浸和渗硼预处理的YG6刀片进行了金刚石薄膜涂层沉积，并对放于不同位置的沉积刀片表面涂层的激光Raman谱和SEM形貌进行了分析、研究。结果表明：渗硼预处理工艺优于酸浸预处理工艺；在渗硼处理的GY6刀片上，沉积的金刚石薄膜涂层具有大面积、均匀性好和质量高的特点。     

活塞环表面碳化铌镀覆新工艺试验研究

用化学液相沉积方法，在高强度灰铸铁活塞环表面实现了Ｎｂｃ覆层，盘销磨擦磨损试验表明，无论在无润滑的情况时，Ｎｂｃ镀层表面要比镀Ｃｒ表面或铸铁原始表面具有更高的耐磨性，可以延长活塞环使用寿命，而Ｎｂｃ镀层与铸铁之间低的磨擦系数可使Ｓ１９５柴油机磨擦损失降低０．３５ｋＷ，降低比油耗９－５ｇ／（ｋＷ．ｈ）。     

端羟基聚二甲基硅氧烷缩聚固化涂膜的“等当点”特性

实验发现,线型端羟基聚二甲基硅氧烷与固化剂发生聚缩反应而固化成膜时,在“等当点”膜表面有最强的疏水性。且对同一种端羟基聚二甲基硅氧烷,“等当点”随固化剂官能度而改变。     

涂层对热电偶热电性能及大气中寿命的影响

在难熔金属热电偶表而施加涂层的目的,旨在使原仅限和真空、中性及还原气氛中测量的热电偶能在大气中使用.本文讨论涂层对难熔金属热电偶在氧化气氛的"热电势—温度","热电势—时间"的关系及其寿命的影响.具有涂层的W/M.热电偶在氧化气氛(常压下1500℃取得263小时±1%t的最高记录,而W-Re热电偶存1500℃试验的前70小时偏差也在1%t内.而没有涂层的热电偶仅支持数分钟便破坏.