Evolution of ferronickel particles during the reduction of low-grade saprolitic laterite nickel ore by coal in the temperature range of 900–1250℃with the addition of CaO–CaF2–H3BO3

The method of producing ferronickel at low temperature(1250–1400℃)has been applied since the 1950s at Nippon Yakin Kogyo,Oheyama Works,Japan.Limestone was used as an additive to adjust the slag composition for lowering the slag melting point.The ferronickel product was recovered by means of a magnetic separator from semi-molten slag and metal after water quenching.To increase the efficiency of magnetic separation,a large particle size of ferronickel is desired.Therefore,in this study,the influences of CaO,CaF₂,and H₃BO₃ additives on the evolution of ferronickel particle at≤1250℃were investigated.The experiments were conducted at 900–1250℃with the addition of CaO,CaF₂,and H₃BO₃.The reduction processes were carried out in a horizontal tube furnace for 2 h under argon atmosphere.At 1250℃,with the CaO addition of 10 wt%of the ore weight,ferronickel particles with size of 20μm were obtained.The ferronickel particle size increased to 165μm by adding 10 wt%CaO and 10 wt%CaF₂.The addition of boric acid further increased the ferronickel particle size to 376μm,as shown by the experiments with the addition of 10 wt%CaO,10 wt%CaF₂,and 10 wt%H₃BO₃.     

燃料添加剂对柴油机烟粒燃烧的影响

考察了燃料添加剂对降低柴油机烟粒燃点温度的效应。含金属添加剂的柴油机烟粒被收集在金属纤维过滤器上,把原状烟粒样品移入实验室反应器,用模拟柴油机排气进行燃烧试验。实验结果表明,当烟粒中含有Pd或Cu时,烟粒的燃点温度可降至430℃左右(普通柴油机烟粒的燃点温度约600℃);Pd的添加还可大大降低烟粒一次燃烧产物中CO的分率。文中还对金属(催化剂)/烟粒接触程度和添加剂溶液中可燃性部分对烟粒燃烧的影响作了讨论。     

稻砂土吸附铜镍铅砷能力的比较

通过对砂壤水稻土中Cu,Ni,Pb,As4种元素的单元及复合吸附试验,表明其吸附热力学符合Freundlich方程,吸附能力为Pb Cu>As>Ni.共存元素对土壤吸附某一元素的能力影响不大;用Langmuir方程粗略地估算出这4种元素在土壤中的化学容量.     

偏硼酸钠与镁和氢反应的硼氢化钠生成

高的氢压和反应温度有利于片硼酸钠与镁和氢反应生成硼氢化钠，但温度接近镁的熔点时不利于硼氢化钠的生成。在反应物中添加铁、镍和钴将加速硼氢化钠的生成，而铜的加入却阻碍硼氢化钠的生成。     

纳米固体超强酸SO42-/ZnO催化合成乙酸异戊酯的研究

本文利用纳米固体超强酸SO4^2-/ZnO催化合成乙酸异戊酯的最佳反应条件,既反应时间2.0h,催化剂用量为酸质量的1.0%,酸醇比为1∶2,验证实验产率为96.7%,且该实验反应时间短,无腐蚀无污染,催化剂可回收可重复利用.     

选择性催化氧化H2S的催化剂研究

在考察了几种单组分氧化物把硫化氢催化氧化为单质硫的基础上，采用共沉淀法合成了3种复合氧化物催化剂A，B，C，并考察了它们的催化活性和选择性．结果表明，在一定条件下，催化剂B的转化率和选择性分别在90％和97％以上，在40h的催化性能稳定性测试中，其转化率和选择性均能保持稳定，具有良好的催化性能．     

固体超强酸催化剂研究进展

概括介绍了固体超强酸催化剂的合成进展，并对固体超强酸催化剂在有机合成反应中的应用做了简要评述．     

Electrocatalytic Oxidation of H_2 O_ 2 at a Carbon Paste Electrode Modified with a Nickel (Ⅱ)-5,11,17,23-Tetra-Tert-Butyl-25,27-Bis(Diethylcarbamoylmethoxy)Calix[4] Arene Complex and Its Application

0　IntroductionThegreatimportanceofnickelelectrochemistryinalkalinemedium ,especiallyforpotentialapplication ,hasattractedmuchattetionofresearcherseithertostudythebehaviorofnickel basedelectrodeitselforitsactivitytowardsothermolecules.Manyreportsshowedthatthenickelbasedelectrodeshaveelectro catalyticactivityforreactionsofappliedinterest,suchaselectro chemicaldeterminationofantioxidantsinfood[1 ] ,detectionofni tricoxide (NO )insolution[2 ] ,electrocatalyticoxidationofmethanol[1 ] ,alcohol[3] ,…     

甲醇催化脱氢制甲酸甲酯反应中Cu－ZnO－ZrO_2／SiO_2催化剂的特性

Ｃｕ－ＺｎＯ－ＺｒＯ２／ＳｉＯ２催化剂对甲醇催化脱氢制甲酸甲酯的反应具有良好的活性和选择性．应用连续微反、差示热分析、Ｘ射线衍射、程序升温还原、Ｘ射线光电子能谱分析和红外光谱等技术，对该催化剂的活性中心本质、ＺｎＯ及ＺｒＯ２的助催化作用、可能的反应机理以及催化剂的失活原因进行了探讨．     

磷酸钙催化剂上二异丁基乙缩醛裂解法合成乙烯基异丁醚的研究

研究了在磷酸钙催化剂上二异丁基乙缩醛裂解制乙烯基异丁醚反应的活性和选择性，其中较好的催化剂是在500度焙烧的Ca3(PO4)2(1)。考察了工艺条件对反应结果的影响，表明在反应温度约300度，缩醛的LHSV＝1．0h^-1时得到最佳反应结果：转化率约98．6％，选择性接近100％，用TPD法测定了催化剂表面的酸度和碱度，并与活性和选择性进行了关联。