A new model for the life prediction of GH4133 under TMF conditions

Thermal mechanical cyclic strain tests were carried out under in-phase and out-of-phase conditions on a Nickel-base Superalloy GH4133 in the temperature range of 571-823℃. Based on analyzing the present models of TMF (thermal mechanical fatigue) life prediction, a new model for predicting nickel-base superalloy TMF lifetime was proposed.TMF life of superalloy GH4133 was calculated accurately based on the new model. Experimental TMF life has been compared with the calculatedresults and all results fall in the scatter band of 1.5. The calculating results show that the new model is not only simple, but also precise. This model will play great roles in life prediction of the metal materials and the engineering components subjected to non-isothermal service conditions.     

粉末高温合金平衡相析出行为的热力学对比

利用热力学平衡相计算方法及相应的高温合金数据库对René95,Rene88DT和эп741нп三种合金在平衡相析出温度范围和析出量以及之间的关联性进行了系统的热力学计算对比分析.结果表明:三种粉末高温合金的平衡相种类基本相同,主要平衡相为γ,γ'和碳化物M23C6,MC,M6C.René95合金中的碳化物含量要高于其他两种合金.3п741нп有着较高的γ'相析出温度和较大的析出量.随温度降低,Co和Nb从γ'相中析出,在其周围富集,其中3п741нп合金中尤为明显.合金元素的偏聚度也和合金的初熔点与终熔点之差的大小有关,其熔解区间越大即初熔点和终熔点之差越大,合金元素的偏聚度越大.     

带中心孔的镍基高温合金GH4049的高温疲劳短裂纹扩展规律

对疲劳试样GH4049镍基高温合金在同一载荷与不同温度下的疲劳短裂纹扩展进行了试验，利用复型技术和光学显微镜观测了裂纹形态演化全过程。发现应力集中条件下的高温疲劳短裂纹扩展主要是单裂系统破坏，随着温度升高，短裂纹逐渐变为多裂系统，并以多裂纹的合并形式进行最终破坏；扩展方式由穿晶到沿晶和穿晶的混合方式进行，温度越高，短裂纹起裂越早，裂纹平均长度越短，短裂纹扩展速率反而越慢。     

铸造镍基高温合金K35的氧化动力学

用静态增重法研究了K35镍基铸造高温合金的800℃氧化动力学·结果表明,K35合金的氧化动力学遵循抛物线规律,属于完全抗氧化级·利用X射线衍射、扫描电镜和能谱分析确定K35合金氧化膜组成以Cr2O3为主,含有NiCr2O4及TiO·TiO2·由于钛氧化物的存在,在高温氧化期间,K35合金发生了内氧化·     

高温合金涡轮盘材料的裂纹扩展速率

用直流电位研究了高温合金涡轮盘材料的裂纹扩展速率，结果表明：高温合金涡轮盘材料的裂纺展速率快慢，不完全取决于材料强度，更主要地取决于持久塑性，在考察高温合金涡轮盘材料的裂纹扩展时，不能认速率值ｄａ／ｄＮ的绝对值来衡量，还应看裂纹扩展速率曲线的斜率是否锐减或曲线出现明显的拐点，以及曲线所对应的应力强度因子△Ｋ的范围。     

阿扑吗啡对LHRH—A促进鲤鱼GtH和GH分泌的影响

腹腔注射ＤＡ激动剂ＡＰＯ和ＬＨＲＨ－Ａ，研究ＡＰＯ对ＬＨＲＨ－Ａ促进鲤鱼ＧｔＨ和ＧＨ分泌的影响．结果表明：①ＬＨＲＨ－Ａ单独注射能极显著刺激ＧｔＨ分泌，且具有明显的剂量依存关系；ＡＰＯ单独注射显著抑制基础ＧｔＨ分泌，没有明显的剂量依存关系；两者结合注射，ＡＰＯ能显著抑制ＬＨＲＨ－Ａ促进ＧｔＨ的分泌；②ＬＨＲＨ－Ａ单独注射，能显著刺激ＧＨ分泌，且具有明显的剂量依存关系；ＡＰＯ单独注射，也能显著刺激ＧＨ的分泌；两者结合注射，ＡＰＯ不能有效增强ＬＨＲＨ－Ａ刺激的ＧＨ分泌的作用     

定向凝固技术制取高温合金单晶铸件的思考

回顾了单晶高温合金的发展历史，结合晶体学知识系统总结与分析了制取高温合金单晶的两种定向凝固技术的原理与晶体竞争生长机制．对两种方法现有工艺的优缺点进行了深入思考与比较，提出了两种制取任何所希望取向理想单晶的新方法，旨在为完善单晶高温合金的制取工艺提供新思路．     

硼对第二代镍基单晶高温合金显微组织的影响

硼(B)是强化镍基单晶合金小角度晶界的重要微量元素,但目前关于B对镍基单晶合金显微组织影响的系统报道非常有限。通过对3种不同B含量(质量分数分别为0、0.01%、0.02%)的第二代镍基单晶合金DD11铸态及热处理态组织定量表征,研究了B对相转变温度、(γ+γ′)共晶组织、硼化物的影响。结果表明:B显著降低合金的固液相线,提高铸态共晶组织体积分数;0.01%B的加入,合金中未出现M3B2型硼化物相;而0.02%B的加入,显著促进了骨架状硼化物的形成,降低合金初熔点,引起残余共晶含量的大幅度提高;骨架状硼化物吸收较多的Cr、Mo和W等元素,降低合金的固溶强化效果,可导致单晶合金基体的蠕变性能大幅度降低。研究结果对认识单晶合金中微量元素B的作用机理及优化B成分范围具有理论指导意义。     

Effect of Mo content on microstructure and stress-rupture properties of a Ni-base single crystal superalloy

The additional 1.5 wt% Mo was added in a Ni-base single crystal(SC) alloy with the composition of Ni–6.5Al–8.0Mo–2.4Cr–6.2Ta–4.9Co–1.5Re–(0.01–0.05)Y(wt%) to study the effect of Mo content on the microstructure and stress-rupture properties. The creep and stress-rupture tests under the conditions of 850 °C/500 MPa and 1100 °C/130 MPa were conducted, and the microstructure of as-cast, heat treated and stress ruptured specimens were analyzed. It was found that the 1.5 wt% Mo addition enhanced the stress-rupture lives at both intermediate(850 °C) and high(1100 °C)temperatures. The microstructure analysis showed that adding 1.5 wt% Mo in the basic alloy affected the microstructure dramatically, i.e., the Mo-rich phases formed in the specimens of as-cast and stress-ruptured specimens. It is considered that the improvement of the stress-rupture lives is duo to the strengthening effect of Mo to both γ and γ'phases and the decrease of stacking fault energy, diffusion constant and dislocation spacing. The Mo-rich phases precipitated under condition of 1100 °C/130 MPa did not affect the creep and stress-rupture properties obviously in the present study.     

NiCoCrAlYTa粘结层与镍基高温合金基体的界面高温互扩散行为

采用真空等离子体喷涂技术(vacuum plasma spraying, VPS)在镍基高温合金GH3128基体表面沉积NiCoCrAlYTa粘结层,并在1 100 ℃进行不同时间的热处理。采用扫描电子显微镜（scanning electron microscopy,SEM）、能谱仪（energy dispersive spectrometer,EDS）等分析NiCoCrAlYTa粘结层与GH3128高温合金界面元素的互扩散行为。结果表明,在热处理过程中,互扩散区(interdiffusion zone,IDZ)和二次反应区(secondary reaction zone,SRZ)的厚度随着热处理时间延长而增大,且在SRZ中明显观察到拓扑密堆(topological close-packed,TCP)相晶粒的生长。Al、Ta、Co元素由NiCoCrAlYTa粘结层向GH3128高温合金扩散,Ni、W、Mo元素由GH3128高温合金向NiCoCrAlYTa粘结层扩散。依据EDS检测的粘结层/基体界面处元素成分,计算出上述元素在界面处的扩散系数,掌握了各元素在高温热处理过程中的扩散速率,揭示了VPS制备的NiCoCrAlYTa粘结层与GH3128高温合金界面处元素在高温下的互扩散规律。