Ba_(1-x)Eu_xMgF_4 复合氟化物的发光性质与结构

对于Ｂａ１－ｘＥｕｘＭｇＦ４体系，当Ｅ２＋ｕ掺杂浓度（ｘ）小于０．１０时，其发光性质与前人研究结果相同。当Ｅ２＋ｕ掺杂浓度（ｘ）大于０．１０时，样品的发射光谱、激发光谱与荧光衰减情况都发生了明显改变。ｘ射线衍射证明，这是由于结构的改变引起的。     

利用NH4CI提高Li2SrSiO4：Dy3＋的发光性能

本文研究了NH4Cl助熔剂对Li2SrSiO4：1％Dy3＋晶体结构、形貌、发光强度和色坐标的影响,并对其作用机理进行了探讨。研究表明,加入2％NH。C1可以改变Li2SrSiO4：1％Dy3＋的反应过程,形成适量液相,抑制杂相的产生并形成表面光滑的球形颗粒。加入2名NH4Cl,Li2SrSiO4：1％Dy3＋发光强度提高了110名,色坐标（0．262,0．293）位于白光区域。     

李政, 宋益善, 左思语,刘超,马晨晨

氨基酸分子首次用以制备构筑稀土介孔发光材料.L-丝氨酸通过分子修饰得到新配体2-烟酰氨基-3-羟基丙酸(L),并进一步引入MCM-41介孔基质中,最后和稀土Tb3+离子复合得发光介孔材料Tb-L-MCM-41.通过核磁共振、紫外、XRD、氮吸附和荧光光谱等对配体和杂化材料的结构和性质进行了表征.结果表明,配体L很好的引入到MCM-41介孔基质中,Tb-L-MCM-41介孔材料呈现L的特征紫外吸收.同时,稀土配合物的引入占据了MCM41基质的部分孔道,使其比表面和孔体积都有所降度.Tb-L-MCM-41呈现稀土Tb3+离子的特征光.     

Y2O2S:Eu3+,Zn2+,Ti4+荧光体的缺陷及红色长余辉发光性质

采用高温固相法合成了红色长余辉材料Y2O2S:Eu3+,Zn2+,Ti4+,实现了余辉发光中心和缺陷中心之间的能量传递。通过XRD、荧光发射和激发光谱、余辉发射光谱与衰减曲线、色坐标和热释光谱测试手段对Y2O2S:Eu3+,Zn2+、Y2O2S:Eu3+,Ti4+、Y2O2S:Eu3+,Zn2+,Ti4+和Y2O2S:Eu3+,Mg2+,Ti4+进行了结构与性能的表征,发现其荧光发射与余辉发射基本一致,红色余辉发光主峰位于625 nm附近,来源于Eu3+的5D0→7F2跃迁发射。相比而言,Y2O2S:Eu3+,Zn2+,Ti4+余辉发光性能最好,可持续1.5 h左右。     

异核高氯酸(Eu3+,Er3+)二苯亚砜配合物中Er3+对Eu3+发光的影响

合成了一系列异核 ( Eu1-x Erx) ( DPSO) 7( Cl O4 ) 3( x=0 .0 0 0 -0 .2 0 0 ,DPSO为二苯亚砜 )配合物 .对配合物进行了组成分析 ,IR谱及荧光激发和发射光谱的测定 .荧光光谱测定结果表明 :Eu3 在配合物中所处格位对称性低无对称中心 ,本身不发光的 Er3 对 Eu3 的发光有较大影响 ,随着 Er3 浓度的增大 ,对 Eu3 的发光先敏化后猝灭 .给出了在该体系中 Er3 对 Eu3 发光敏化的浓度范围以及 Eu3 荧光发射强度与 Er3 浓度变化的曲线     

Tunable and enhanced luminescence of Ba2−xCaxSiO4−yN2/3y:Eu2+ phosphors for white light-emitting diodes

Color tuning and luminescence enhancement are predominant challenges for improving the performance of white light emitting diodes(LEDs) toward commercial application. In this paper, a novel promising Ba_(2-x)Ca_xSiO_(4-y)N_(2/3y):Eu~(2+) tphosphors with tunable and enhanced luminescence for phosphors converted LEDs(pc-LEDs) have been successfully synthesized by a direct gas-reduction nitridation method. The effects of Ca and N doping on the phase purity, morphology and optical properties of Ba_(2-x)Ca_xSiO_(4-y)N_(2/3y):Eu~(2+) tphosphors were also systematically investigated. The optical results show that Ba_(2-x)Ca_xSiO_(4-y)N_(2/3y):Eu~(2+) tphosphors can be actively excited over a broad range from 250 to430 nm. With the adding of different concentrations of Ca~(2+) tions in phosphors, the emission color wavelength can be tailored from 501 to 441 nm by a 375 nm NUV LED excitation source. Furthermore, it has been found that the emission and absorption of Ba_(2-x)Ca_xSiO_(4-y)N_(2/3y) tphosphor can be significantly improved when N~(3-) ions were introduced into the host lattices. The intensity of Ba_(1.5)Ca_(0.5)SiO_(4-y)N_(2/3y):Eu~(2+) tphosphor was 3.4 times higher than the phosphor without N doping. The fabrication and characterization of pc-LEDs using Ba_(2-x)Ca_xSiO_(4-y)N_(2/3y):Eu~(2+) tphosphors-silica gel as the coating layer onto 375 nm-emitting In Ga N LED caps demonstrated the superior optical and current tolerant properties,making it a promising and competitive candidate for commercial utilization in white LED applications.     

长余辉磷光体Zn4B6O13:Dy发光特性研究

研究方钠石型结构过渡金属硼酸盐Zn4B6O13:Dy的荧光及长余辉发光性质.XRD分析结果表明,在900 ℃下烧结7 h的产物为单相,其荧光及长余辉发光来自于同一发光中心,由Dy3 的f-f跃迁产生,样品Zn3.84B6O13:0.16Dy的余辉衰减曲线由一个初始的快衰减与随后的中衰减和慢衰减过程组成.     

（Y，Gd）_2O_3·2B_2O_3：Bi~（3＋），Eu~（3＋）的发光性质

研究了荧光材料（Ｙ，Ｇｄ）_２Ｏ_３·２Ｂ_２Ｏ_３：Ｂｉ~３＋，ＥＵ~３＋的合成和晶体结构．经ＸＲＤ确定为六方晶系，晶胞参数：ａ＝３．７８６，ｃ＝８．８２４．在２５４ｎｍ紫外光激发下，荧光材料有较强的红色发光．观察到Ｂｉ~３＋→Ｇｄ~３＋→Ｅｕ~３＋的能量传递现象，Ｂｉ~３＋→Ｇｄ~３＋能量传递机理为交换作用；Ｇｄ~３＋→Ｅｕ~３＋能量传递机理为电偶极──电四极相互作用．     

用Eu~(3+)作荧光离子探针研究化合物结构的对称性

系统研究稀土Ｅｕ~(3＋)离子的荧光谱线的数目、位置和强度与其所处的周围环境对称性之间的关系,提出利用这种关系探测被取代离子周围晶场对称性及取代格位的方法,该方法为许多化合物的结构研究工作提供了一种简便、灵敏的实验手段。     

一种钾长石(KCFW01)的释光图谱及其应用

本文针对一种钾长石矿物作了其选频释光图谱的研究分析.在BG2003光释光谱仪上选择不同的激发光源对钾长石样品进行激发,获得了钾长石的释光图谱.通过对这种钾长石的研究,发现矿物随辐射剂量增加响应有很好的线性关系,可以用来做释光测年的矿物.这种钾长石的测年上限大约是84万年.它的光晒退实验指出利用这种钾长石矿物测年时要考虑光晒退的影响.