Evolution of ferronickel particles during the reduction of low-grade saprolitic laterite nickel ore by coal in the temperature range of 900–1250℃with the addition of CaO–CaF2–H3BO3

The method of producing ferronickel at low temperature(1250–1400℃)has been applied since the 1950s at Nippon Yakin Kogyo,Oheyama Works,Japan.Limestone was used as an additive to adjust the slag composition for lowering the slag melting point.The ferronickel product was recovered by means of a magnetic separator from semi-molten slag and metal after water quenching.To increase the efficiency of magnetic separation,a large particle size of ferronickel is desired.Therefore,in this study,the influences of CaO,CaF₂,and H₃BO₃ additives on the evolution of ferronickel particle at≤1250℃were investigated.The experiments were conducted at 900–1250℃with the addition of CaO,CaF₂,and H₃BO₃.The reduction processes were carried out in a horizontal tube furnace for 2 h under argon atmosphere.At 1250℃,with the CaO addition of 10 wt%of the ore weight,ferronickel particles with size of 20μm were obtained.The ferronickel particle size increased to 165μm by adding 10 wt%CaO and 10 wt%CaF₂.The addition of boric acid further increased the ferronickel particle size to 376μm,as shown by the experiments with the addition of 10 wt%CaO,10 wt%CaF₂,and 10 wt%H₃BO₃.     

金属间化合物(Mg,Zn)_(12)Ce与(Mg,Zn)_(11)Ce的研究

对300℃时Mg-Zn-Ce系富镁侧化合物的成分特征、结构和相平衡关系进行了研究.结果表明,Mg-Zn-Ce富镁角存在一个Mg12Ce的二元置换固溶体(Mg,Zn)12Ce,还存在一个三元线性化合物(Mg,Zn)11Ce(τ相).(Mg,Zn)12Ce中Zn的范围为0~7.3%(原子分数),其晶体结构为体心四方晶格.三元线性化合物τ相含Zn为8.5%~43.5%(原子分数),其晶体结构为C底心正交晶格.(Mg,Zn)12Ce和τ相均与α(Mg)存在稳定的两相平衡,且在Mg-Zn-Ce系富镁角还存在三相平衡Mg+(Mg,Zn)12Ce+τ.     

稻砂土吸附铜镍铅砷能力的比较

通过对砂壤水稻土中Cu,Ni,Pb,As4种元素的单元及复合吸附试验,表明其吸附热力学符合Freundlich方程,吸附能力为Pb Cu>As>Ni.共存元素对土壤吸附某一元素的能力影响不大;用Langmuir方程粗略地估算出这4种元素在土壤中的化学容量.     

Electrocatalytic Oxidation of H_2 O_ 2 at a Carbon Paste Electrode Modified with a Nickel (Ⅱ)-5,11,17,23-Tetra-Tert-Butyl-25,27-Bis(Diethylcarbamoylmethoxy)Calix[4] Arene Complex and Its Application

0　IntroductionThegreatimportanceofnickelelectrochemistryinalkalinemedium ,especiallyforpotentialapplication ,hasattractedmuchattetionofresearcherseithertostudythebehaviorofnickel basedelectrodeitselforitsactivitytowardsothermolecules.Manyreportsshowedthatthenickelbasedelectrodeshaveelectro catalyticactivityforreactionsofappliedinterest,suchaselectro chemicaldeterminationofantioxidantsinfood[1 ] ,detectionofni tricoxide (NO )insolution[2 ] ,electrocatalyticoxidationofmethanol[1 ] ,alcohol[3] ,…     

铝合金变形抗力的实验研究

采用恒应变速率凸轮式形变压缩试验机试验了四种铝合金材料的变形抗力 ,分析了应变率和应变速率对变形抗力的影响 ,结果表明随应变的增加 ,变形抗力以近似幂函数关系增加 ,在此基础上建立了简单、适用的变形抗力计算模型     

化学镀镍过程中金属基体的引发催化特性研究

通过电位-时间曲线的特征,研究了化学镀镍反应初期不同基体材料的催化特征.在同质基体上可以瞬间诱发化学镀反应,而在异质基体上的诱导期因镀液组成不同而发生变化.在异质基体材料中,Pt无催化活性,Pd的诱发时间最长.     

高功率型镍氢电池的循环性能

由于没有镉污染,对环境友好,用于高功率设备的镍氢电池的需求量增长很快,目前每年的需求量约为5亿只.但是镍氢电池的一些性能还不能完全满足电动工具的使用要求,突出表现在电池大电流充放循环寿命较差.因此,研制高性能的高倍率镍氢电池不仅具有重要的研究意义,也有很大的应用价值.本文研究影响SC型动力电池循环寿命衰减的主要因素,测量了在大电流循环过程中镍氢电池的内阻、温度及重量变化,并运用SEM、XRD对电池内阻升高的原因进行了分析.我们认为电池内阻升高是镍氢电池大电流循环寿命差的主要原因,分析发现在镍氢电池进行大电流充放电循环时,电池正极膨胀,负极微粉化,电池内部孔隙率增加,致使电解液干涸,电池内阻升高.通过增加负极容量,抑制正极膨胀,可以有效改进镍氢电池大电流充放时的循环性能.     

NiTi合金表面氧化对镍离子释放的影响

采用原子吸收分光光度计,分别测试经机械抛光和高温氧化后的NiTi合金样品在人体生理模拟液中镍离子的释放速度,结果表明NiTi合金表面氧化膜的形成可以有效地减少镍离子的溶出.     

激光辐照Fe81.5P18.4Yb0.1非晶合金的晶化特征

本文用扫描电镜（ＳＥＭ）和示差扫描量热法（ＤＳＣ）研究了ＸｅＣｌ准分子激光辐照Ｆｅ＿（８１．５）Ｐ＿（１８．４）Ｙｂ＿（０．１）非晶合金的晶化特征。结果发现，辐照样品的断面上有类冲击波纹样的层状规则的晶粒分布，其晶粒尺寸由辐照表面向样品内部逐渐减小，最后是近纳米尺度的微晶排布，样品的热稳定性也明显改善。     

1-(6-硝基-2-苯并噻唑)-3-(4-硝基苯)-三氮烯与镍显色反应的研究及应用

在TritonX-100表面活性剂存在下,研究了1-(6-硝基-2-苯并噻唑)-3-(4-硝基苯)-三氮烯(NBTNPT)与镍的显色反应.在pH为10.0～11.5的Na2B4O7-NaOH缓冲溶液中,该试剂与镍生成2∶1配合物.以500nm为参比波长,440nm为测定波长的双峰双波长进行测定,表观摩尔吸光系数为1.84×105L·mol-1·cm-1.Ni2+的浓度在0～280μg/L内符合比耳定律.用拟定方法测定钢铁中的微量镍,结果满意.