Microstructure,mechanical properties and formability of friction stir welded dissimilar materials of IF-steel and 6061 Al alloy
下载免费PDF全文
![点击此处可从《矿物冶金与材料学报》网站下载免费的PDF全文](/ch/ext_images/free.gif)
Semih Mahmut Aktarer Dursun Murat Sekban Tevfik Kucukomeroglu Gencaga Purcek 《矿物冶金与材料学报》2019,26(6):722-731
AA 6061 alloy and interstitial-free(IF)steel plates were joined by the friction stir welding(FSW)method,and the microstructure,mechanical properties,and biaxial stretch formability of the friction stir welded(FSWed)parts were investigated.The results indicate that the FSWed parts showed optimum tensile strength during FSW with the 0.4-mm offset position of the tool.The Fe4Al13 intermetallic compound formed in the defect-free intersection of AA 6061 and IF-steel plates during FSW.The hardness of the IF-steel part of the FSWed region increased almost 90%relative to its initial hardness of HV0.2 105.The tensile and yield strengths of FSWed regions were approximately 170 MPa and 145 MPa,respectively.According to the formability tests,the Erichsen Index(EI)of the IF-steel,AA 6061,and the FSWed samples were determined to be 2.9 mm,1.9 mm,and 2.1 mm,respectively.The EI of the FSWed sample was almost the same as that of the AA 6061 alloy.However,it decreased compared with that of the IF-steel.The force at EI(FEI)was approximately 1180 N for the FSWed condition.This value is approximately 70%higher than that of AA 6061 alloy. 相似文献
2.
The aim of this work is to investigate the mechanical properties and microstructures of friction-stir welded (FSWed) St52 structural steel joints. In this study, St52 steel plates with a thickness of 4 mm were butt-welded by friction-stir welding (FSW) using a tungsten carbide tool having a conical pin. The microstructure of the welded zone consists of equiaxed fine ferrite, grain boundary ferrite, Widmanstatten ferrite, and aggregates of ferrite + cementite. The microhardness measurements showed that the hardness of the welded zone was significantly higher than that of the base metal. The FSWed St52 joint exhibited a significant strength overmatching in the weld region and a strength performance similar to or slightly higher than that of the base plate. 相似文献
1