排序方式: 共有50条查询结果,搜索用时 218 毫秒
1.
本文对物理教学中常见的三种课型--实验教学课、知识教学课和习题教学课的基本教学方法进行了分析,参照现代教学理论的新成果,兼收并蓄,设计了一种新的课堂教学模式--系统教学法.这种教学法,能有效地减轻学生的课业负担,全面提高物理教学质量. 相似文献
2.
Six samples of linear high randomness 60PHB/ PET thermotropic liquid crystal copolyesters are made by melt copolymerization at 290℃ , whose randomness about 0.955 is measured by the discernible 'H-NMR spectrometer. High tenacity, high module fiber is prepared by melt spinning in liquid crystal phase. The effect of molecular weight, shear rate, temperature as well as spinning drawn ratio on the mechanical behavior of 60PHB / PET copolyester fiber are shown that, lower shear rate (2~ 10 s~(-1)), higher temperature melting (300℃ ), lower temperature spinning (280℃ ) and higher molecular weight are favourable to the increase of the fiber mechanical properties. With the variance of drawn ratio, fiber mechanical property has a transition point due to traversion from shear-orientation to drawn-orientation. The copolyester fiber has high crystallinity, high orientation at the crystalline region, high chain orientation and high regular fibrillar structure. 相似文献
3.
By computation and comparison of the critical spreading coefficient parameter, it was found that shaped fiber bundle is better for wetting. Liquid-air interface tension of liquid arising the shaped fiber bundle body is considered as one critical factor besides liquid viscosity, inertia force and liquid-fiber interface tension. Experimental result simulation demonstrated that the liquid-air interface tension is correlated with the geometric size of the liquid arising in body, Φ0 (x) and which is affected by the cross sectional shape of fiber and the radius of single fiber. The shaped fiber bundle model is/ntroduced to/nvestigate liquid flow in fiber assembly. The model is generated based on a random function for stochastic forming of fibers in bundle and it is necessary to combine this fundamental model with physical explanation for investigation of liquid flow in fiber assembly. 相似文献
4.
Poly[2,2-(m-phenylene)-5,5-bibenzimidazole](mPBI)were synthesized by mixing 3,3’,4,4’-tetraaminobiphenyl and isophthalic acid in 1-butyl-3-methylimidazolium chloride([BMIM]Cl).Intrinsic viscosity of mPBI polymers was 0.67 dL/g which was measured in 96%sulfuric acid.The polymer was characterized by Fourier transform infrared spectroscopy(FTIR),nuclear magnetic resonance(1H-NMR),and thermogravimetric analysis(TGA).The effects of polymerization conditions on the intrinsic viscosity of mPBI were investigated.It showed that the molecular weight of polymer mainly depended on pre-reaction time and reaction temperature.Comparison of structure and properties of mPBI synthesized in ionic liquids(ILs)and polyphosphoric acid was also reported.It indicates that the ionic liquids are a kind of good solvents in synthesis process of mPBI and ionic liquids mainly affect molecular weight of mPBI. 相似文献
5.
6.
为了研究阻燃共聚酯(flame retardant co-polyesters,FRPET)固相缩聚(solid state polymerization,SSP)反应过程中的结构变化,特别是结晶变化以及结构与反应动力学的关系,对SSP进程中不同反应时间的聚酯样品的特性黏度及端羧基含量进行了测试,并通过X-射线衍射、差... 相似文献
7.
The epoxidation reaction of propylene and hydrogen peroxide with zeolite catalyst containing titanium-silicalite (TS-1)has been studied, and the reaction in the mixed solvent of water/methanol has been discussed. It is shown that the selective of epoxidation propylene decreases while the selective of propylene glycol increases, when the water content increases in the mixed solvent of me thanol/water. 相似文献
8.
变径热管纺丝是一种新开发的纺丝工艺,通过建立纺丝动力学的模型,对不同的工艺条件进行模拟,计算出纤维沿纺程上的温度,速度及应用分布,找出纺丝工艺参数的调节规律。 相似文献
9.
在3000~5000m/min纺速下制备Fully Crystallinity Yam(FCY)纤维,利用X光衍射、密度梯度等测定了无定形区的含量;并结合声速计算得到无定形区的平均取向。在M-K理论的基础上,重新定义了结构化指数,并计算得到无定形区的微细结构分布。结果表明:在其它工艺条件不变,热板位置、温度、长度分别为544mm、200℃、1800mm时,涤纶FCY的最佳纺丝速度为3 500m/min。即在3 500 m/min纺速形成的无定形结构较均匀、致密。其无定形含量低,无定形取向高,动态力学转变温度高。从tanδ~T曲线可以计算无定形区的分布,在3 500m/min纺速n_(max)、《n》及aum from ≥4 F(n)等较高,峰面积较小,相应的无定形结构较强,无定形含量较低。所得结果与其它方法的结果一致。从tanδ~T曲线可以计算无定形区的分布,且本方法与其它方法相比,更灵敏,更有效,可获得更多的信息。 相似文献
10.
On the basis of melt-spinning, the dynamics model of polyethylene terephthalate (PET) hollow fiber is established.The effects of spinning conditions on hollow ratio are discussed and verified. Because of the different quenching conditions, there exist differences of the hollow ratio and the vitrification distances between different cycles. The important role of the quenching conditions on the melt-spinning of PET hollow fiber is also mentioned. 相似文献