汽车板用钢Si含量控制技术研究

为解决国产汽车板用钢在冶炼过程中因钢水增硅导致的钢板性能下降的问题,本文对钢板冶炼各阶段Si含量的产生及变化情况进行了研究。影响各阶段钢水增硅的原因主要包括钢包渣碱度、钢水Al含量、中包渣和中包绝热板的材质等,通过选用Si质量分数小于1.5%的脱氧剂、采用钢包渣改质剂提高钢包渣的渣碱度、选用全碱性中间包或不含硅的大包保护渣等控制措施,能够将精炼-连铸过程中钢液增硅质量分数控制在0.01%以下。     

采用双等离子体制备非晶态碳膜的研究

采用直流金属磁过滤阴极真空弧(FCVA)制造出Ti和乙炔(C2H2)气体的双等离子体在单晶硅(100)上制备非晶态碳膜.重点研究了乙炔气体和过滤线圈电流对非晶态碳膜的结构、形貌和机械性能的影响.研究结果表明,薄膜中主要成分是TiC,并以(111)作为主晶向;随着过滤线圈电流的增大,薄膜的晶粒度越来越小;薄膜表面的粗糙度逐渐减小,变得更加平整;薄膜的应力减小,可以下降到2.5 GPa.薄膜的显微硬度和弹性模量随着C2H2体积流qV(C2H2)的增大而降低,硬度和弹性模量分别可以达到33.9 GPa和237.6 GPa.非晶态碳膜的摩擦因数在0.1～0.25之间,大大低于衬底材料单晶硅片的摩擦因数0.6.随着过滤线圈电流增大,摩擦因数减小.     

SnAgCu合金粉末的真空蒸镀涂层机理

对SnAgCu合金粉末的真空蒸镀涂层硬脂酸的成膜机理进行了研究.采用扫描电镜(SEM)和透射电镜(TEM)对涂覆后合金粉末的形貌及结构进行观测,采用傅里叶红外光谱仪(FTIR)和X射线光电子能谱仪(XPS)对涂覆后粉末的透射吸收谱和光电子能量进行测试.结果表明:硬脂酸在合金粉末表面形成一层均匀致密、厚度为5～10 nm的薄膜,硬脂酸涂层SnAgCu合金粉末的行为属于物理吸附行为,其生长方式遵循岛状生长机理模式,其过程实质是一个气--固转换、晶体生长的过程.     

玉米秸秆稀酸预水解液两种脱毒方法的研究

以玉米秸秆稀酸预水解液为原料,研究了减压蒸发和络合萃取两种脱毒方法对乙酸等抑制物的去除情况。结果表明:玉米秸秆稀酸预水解液减压蒸发脱毒,糠醛完全被去除,而5-羟甲基糠醛则基本不能被去除;当水解液浓缩5.80倍时,其浓缩液中乙酸质量浓度和去除率分别为4.06 g/L和60.45%。络合萃取脱毒的最佳条件:络合萃取剂的组成为30%三烷基胺+50%正辛醇+20%煤油,油水相比2∶1,温度25℃,时间60 min,此时脱毒液中乙酸质量浓度和去除率分别为1.43 g/L和52.33%,糠醛完全被去除,5-羟甲基糠醛的去除率为27.78%。     

增光子压缩真空态的压缩特性

利用玻色湮没算符的逆算符-a∧1及玻色产生算符a∧ 分别作用于压缩真空态来构造增光子压缩真空态,并对它们的压缩特性进行了讨论.结果表明,a-∧1作用于压缩真空态所得到的增光子压缩真空态不产生压缩效应,而a∧ 作用于压缩真空态所得到的增光子压缩真空态则产生压缩效应,其压缩区间与压缩参数的取值有关.从而显示了增光子压缩真空态的压缩特性与算符a-∧1及a∧ 之间的密切关系.     

RH精炼钢中全氧量变化与操作改进

为了使钢中全氧量控制在一个适当的水平,在武钢炼钢总厂RH真空脱气装置对低碳、超低碳钢进行了脱氧净化试验.结果表明,影响全氧去除的因素按作用高低依次是出钢溶解氧水平,溶解氧与钢包渣的交互作用,钢包渣,和真空处理净化时间.通过改进工艺生产了全氧量≤10×10-6,非金属夹杂物尺寸<10μm的清洁钢水,建立了一个钢包内钢水全氧浓度随时间变化的新方程,该方程考虑了全氧的表观平衡含量及环流、扩散传质对去除氧化物夹杂速率的影响.     

SiCl_4制备正硅酸乙酯的工艺研究

为寻找一条工序简单、耗价低、易于工业放大路线,实现多晶硅副产物四氯化硅(SiCl4)废物资源化制备正硅酸乙酯(TEOS),本文以多晶硅副产物SiCl4和无水乙醇为原料制备TEOS,在半连续化生产工艺的基础上研究了SiCl4与乙醇的摩尔比、反应温度、反应时间等因素对TEOS产率及纯度的影响。正交实验优化结果表明:15℃下,以恒定速率滴加14.21 g无水乙醇于15 g四氯化硅中,反应35 min,补加8.12 g无水乙醇;55℃下恒温40 min,经减压蒸馏,除去低沸点的乙醇和氯化氢,TEOS产率达到86.61%。对正交实验优水平下制得的产物进行红外光谱(IR)和气相色谱(GC)分析,结果表明:产物中TEOS结构正确,其纯度大于99.0%,达到市售分析纯纯度。     

Magnetoresistance of the thin film ferromagnetic nanoconstrictions

The magnetoresistance and I-V characteristics at different temperatures of the thin film ferromagnetic nanoconstrictions of variable width (from 20 to 250 nm) and 10 nm thicknesses, fabricated by electron beam lithography and vacuum thin film deposition are compared. The magnetoresistance and resistance of the thin film ferromagnetic nanoconstrictions are not related to the width of the nanoconstrictions. Instead the resistance of the local nano-region in the middle of the thin film ferromagnetic nanoconstriction has only a minor role compared to that of the two microscale thin film ferromagnetic electrodes, which contribute the majority of the measured resistance. The magnetoresistances of the thin film ferromagnetic nanoconstrictions and a 0.2 cm × 0.8 cm thin ferromagnetic film deposited under the same conditions were also compared; the thin film ferromagnetic nanoconstrictions have higher magnetoresistances than the thin ferromagnetic film, which implies that the measured magnetoresistance of the thin film ferromagnetic nanoconstrictions comes mainly from the local nano-region in their centers. In conclusion, the measured magnetoresistance of the whole sample is similar to the anisotropic magnetoresistance, because the resistance of the two microscale thin film ferromagnetic electrodes is much higher than that of the local nano-region in the middle of the samples. Comparing the experimental results for the thin film ferromagnetic nanoconstrictions and the thin ferromagnetic film reveals that the magnetoresistance of the local nano-region in the middle of the sample is much higher than that of the two microscale thin film ferromagnetic electrodes attached to it.     

Deep levels,transport and THz emission properties of SiGe/Si quantum-well structures

In coal mines in such countries as China and Russia,most of the coal mine methane(CMM) generated during mining is emitted to the atmosphere without any effective usage,because the methane concentration of CMM is relatively low and not allowed to be used as fuel for safety reasons.Methane is one of the greenhouse gases.Therefore,if it becomes possible to concentrate CMM to an acceptable level for use as fuel,this will greatly contribute to reduction of greenhouse gas emissions.With the aim of gaining approva...     

晶粒尺寸和热处理对Sm2Fe17N3/Fe3N/BN软磁/硬磁复合材料的合成及磁性能影响

采用高能球磨和真空热处理方法制备Sm2Fe17N3/Fe3N/BN复合材料, 并研究球磨过程中晶粒尺寸变化对固态相变和磁性能的影响.  结果表明: Sm2Fe17N3和Fe3N相产生的条件是Fe的晶粒尺寸达到纳米量级（D＜80 nm）并形成Fe(Sm)固溶体; 随着退火时间的增加, 300 ℃真空退火的球磨样品中Sm2Fe17N3的结晶物增多, 矫顽力提高, 表明样品的磁性能与Sm2Fe17N3的结晶程度有关.