介绍了利用铅锶共沉一络合滴定法测定铜合金中的铅,试样以硝酸溶解,用硝酸锶共沉淀铅,将沉淀溶于热稀硝酸溶液中,在pH值为5．5的弱酸性介质中,以二甲酚橙为指示剂,EDTA滴定铅,结果满意．     

BaCeO3和SrCeO3基钙钛矿型固体电解质

综述了ＢａＣｅＯ３基和ＳｒＣｅＯ３基钙钛矿型固体电解质,从结构、不同气氛中导电性方面进行了介绍,对其应用方面进行了较为详细的分析。在燃料电池、电解池、薄膜反应器、气体传感器等方面的应用分析表明这２类固体电解质有广泛的应用前景。     

聚合质量比对Sr0．7La0．15Ce0．15Fe11.7Zn0．3O19／PAn复合体系微波吸收性能的影响

用原位聚合法制备了Sr0．7La0．15Ce0．15Fe11.7Zn0．3O19铁氧体／聚苯胺（PAn）复合材料。采用X射线衍射（XRD）、扫描电子显微镜（SEM）对样品的结构、微观表面形貌和粒子大小进行了表征,用微波矢量网络分析仪测量样品在2～12．4GHZ频率范围内复介电常数和复磁导率,根据测量数据计算微波反射率R与频率f的关系。研究结果表明：PAn包覆于掺杂锶铁氧体表面,PAn／Sr0．7La0．15Ce0．15Fe11.7Zn0．3O19复合材料具有良好的吸波性能,随着掺杂锶铁氧体含量的增加,微波吸收匹配厚度和吸收带宽发生变化：当Sr0．7La0．15Ce0．15Fe11.7Zn0．3O19聚合质量比为40％时,最佳匹配厚度为2．6mm,吸收峰值接近-40dB,峰值频率高于12．4GHz,大于10dB吸收带宽预计达到55GHz。     

氨化改性Sr2Ta2O7/SrTa4O11光催化剂用于光电催化性能研究

以钽酸锶同素异质结Sr₂Ta₂O₇/SrTa₄O₁₁（STO）为原始材料,采用高温氨化法对原始材料做氮掺杂改性处理,得到了新型氮掺杂钽酸锶同素异质结材料Sr₂Ta₂O_7-xN_x/SrTa₄O_11-xN_x(STO-N),并对其光电催化性能进行研究。结果显示,对比改性前的STO,STO-N具有更强的可见光吸收能力。紫外可见漫反射光谱证明,氮掺杂使得STO的吸收阈值从319 nm红移到485 nm,相应的带隙由3.97 eV减小到2.51 eV,这主要是由于N 2p和O 2p轨道的混合作用导致价带顶部上移。性能测试结果表明：STO-N₂₀的光电催化性能提升最为显著,在施加0.7 V偏压下,STO-N₂₀电极测得的光电流密度达到了570 nA/cm²,是STO电极的光电流密度（8.6 nA/cm²）的66倍。根据推算出的STO及STO-N₂₀的能带结构可知,STO-N₂₀性能提升的原因是禁带宽度变窄。     

SrTiO3中离子自扩散参数评估

评估了在未掺杂SrTiO3中氧的自扩散数据,得出:(1)在SrTiO3晶体中,氧通过氧空位扩散,扩散最快的离子为O2-,其次为Sr2+,最慢的为Ti4+.(2)在1 098~1 623 K范围,氧分压在0.2~7.6×104 Pa内变化时,得到氧在SrTiO3晶体中的自扩散系数,而位错密度和氧分压对扩散系数影响不大.     

掺杂稀土元素镧的锶铁氧体超微粉末的微波吸收特性研究

采用溶胶-凝胶法制备了掺杂稀土元素镧的锶铁氧体超微粉末,就镧元素的掺杂含量对锶铁氧体吸波性能的影响进行了对比研究.结果表明,用聚乙二醇凝胶法制备的掺杂镧的锶铁氧体S rL axF e12-xO19超微粉末,当掺杂镧含量x=0.03时,对微波吸收效果最佳.在7.5~11.9GH z测试频段内,当涂层厚度2.0 mm时,其吸收量均在17 dB以上,在11.4 GH z处,最大吸收量为33 dB.     

Effect of SrCO3 addition on the dynamic compressive strength of ZTA

Ceramic parts usually experience dynamic load in armor applications. Therefore, studying the dynamic behaviors of ceramics is important. Limited data are available on the dynamic behaviors of ceramics;thus, it is helpful to predict the dynamic strength of ceramics on the basis of their mechanical properties. In this paper, the addition of SrCO3 into zirconia-toughened alumina (ZTA) was demonstrated to improve the fracture toughness of ZTA due to the formation of the SrAl12O19 (SA6) phase. The porosity of ZTA was found to be increased by the addition of SrCO3. These newly formed pores served as the nucleation sites of cracks under dynamic load;these cracks eventually coalesced to form damaged zones in the samples. Although the KIC values of the samples were improved, the dynamic strength was not en-hanced because of the increase in porosity;in fact, the dynamic strength of ZTA ceramics decreased with the addition of SrCO3.     

三元络合物分光光度法测定锶

本文研究了在聚乙烯醇存在下,锶与碘化钾和罗丹明B形成三元缔合物的高灵敏显色反应。以摩尔比法测定缔合物中摩尔比Sr∶I：RB=1∶4∶2,缔合物水溶液的最大吸收波长为560nm,摩尔吸光系数为ε=2．42×10~6 L/mol．cm,方法简便,快速,灵敏度高。sr(Ⅱ)含量在0-10μg/25ml范围内符合Beer s定律。同时,详细研究了反应条件。并作了水中锶的回收实验。操作简便、快速、结果令人满意。     

球磨对水热法制备锰锌铁氧体纳米粉体工艺的影响

以硝酸铁、硝酸锰、硝酸锌为原料,采用传统水热法和球磨辅助水热法合成了锰锌铁氧体纳米粉体,通过xRD、TG-DSC和TEM研究了粉体的结晶性能、热性能以及粉体的形貌,分析了机械球磨的加入对纳米粉体制备的影响。研究表明,球磨的加入可以明显提高晶化反应速度,在相同时间内制得的纳米晶发育好于传统水热法制得的锰锌铁氧体纳米晶。球磨对粉体的热性能影响很小。传统水热法和球磨辅助水热法均可制得粒径10nm左右的锰锌铁氧体纳米晶,但粉体的分散性球磨辅助水热法优于传统水热法。     

碳酸锶生产中废气废水的综合利用途径

介绍了利用碳酸锶生产过程中产生的废气、废水制取硫磺、硫脲、碳酸氢铵等的综合利用方法和途径。