硼对12Ni3CrMoV高强度钢焊接接头冷裂敏感性的影响

低碳调质高强度钢中添加硼对焊接冷裂敏感性的影响较少有人研究,并存在两种不同意见.本文对含硼量分别为0.005%,0.0014%,0.0028%,0.0035%的12Ni3CrMoV调质高强度钢焊接冷裂敏感性进行研究.试验结果表明:1.插销试验临界应力:含硼钢比无硼钢(含硼0.0005%)高;含硼钢中,临界应力按含硼量0.0014%,0.0028%,0.0035%的顺序递减.2.扫描电镜断口分析:无硼钢有沿晶断裂区、准介理断裂区和韧窝断裂区.含硼钢没有沿晶断裂区,只有准介理断裂区和韧窝断裂区.3.焊条未烘干时,无硼和含硼钢的插销临界应力都降低,无硼钢沿晶断裂区扩大,含硼钢仍无沿晶断裂区.4.硼在HAZ粗晶区中沿奥氏体晶界形成偏聚带,硼相主要沿奥氏体晶界呈不连续点状析出.含硼愈多,沿奥氏体晶界偏聚和硼相析出也愈多.5.C.D.Beachem提出的断口形貌发展过程示意图可以解释无硼钢断裂,不能完全解释含硼钢断裂过程.6.裂纹敏感性成分Pcm值表达式中,硼项系数为" 5"值得商榷.就本文钢材而言,硼项函数应为"负变数".本文对含硼钢延迟裂纹机理作了探讨.     

活性粉末钢纤维混凝土受压应力-应变全曲线的研究

采用普通压力试验机附加刚性辅助架的方法对活性粉末混凝土进行了单轴压缩试验,分析和研究了不同水胶比和钢纤维掺量下的应力-应变全曲线的特征.通过对不同曲线进行比较,给出了活性粉末混凝土棱柱体抗压强度、峰值应变、弹性模量、受压韧性指数与钢纤维掺量和水胶比的关系,并在试验分析的基础上建立起RPC受压应力-应变全曲线的数学表达式.     

影响管线钢在近中性pH值环境中应力腐蚀开裂的力学因素

以X-65管线钢近中性pH值溶液（实际土壤溶液）为研究对象,通过慢应变速率拉伸（SSRT）和应力波动的实验研究,评价X-65管线钢在近中性pH值环境中力学因素对SCC（应力腐蚀开裂）的作用和影响。实验表明,应变速率及应力波动R值（最小和最大应力的比值）对SCC的发生有重要的作用。     

广州国际体育演艺中心钢屋盖支撑卸载模拟分析及监控

大跨度钢屋盖施工过程中受力情况与成型后是不同的,须考虑施工过程中结构体系的变化;结合广州国际体育演艺中心钢屋盖支撑卸载工程的施工特点,给出其支撑卸载的总体方案,应用ANSYS有限元分析其卸栽过程。确定卸栽过程中应力和变形的变化范围,并与实测数据对比分析,积累的经验和数据可为类似结构的卸载提供借鉴．     

钢管混凝土圆弧拱平面内非线性稳定承载力

采用考虑屈曲前变形的弹性稳定公式,基于统一理论的钢管混凝土截面抗压承载力计算方法,研究了均布径向荷载作用下钢管混凝土圆弧拱的平面内非线性稳定承载力,并在分析中考虑了几何非线性、材料非线性和拱肋初始缺陷的影响.通过对比有限元结果和各国典型设计规范提供的稳定系数公式,提出了适合钢管混凝土圆弧拱的平面内非线性稳定系数,为钢管混凝土拱桥的设计提供依据.     

大跨度斜拉桥钢塔制振方案与参数分析

以南京长江第三大桥为例研究了大跨度斜拉桥钢塔施工阶段所需的制振目标及制振措施．参考相关资料确立了主塔制振所需的制振目标，并依据风洞试验结果建立制振器的设计目标值．根据该桥的固有频率范围和实际安装空间等条件选择了合理的制振方案，分别采用调谐质量阻尼器（TMD）和调谐液体阻尼器（TLD）完成不同施工状态和风速时对涡激振动的制振，进而进行了制振器的参数优化和装置设计．对制振器参数完成了敏感性分析，最终确认了使用环境下制振器对钢塔的不同施工阶段制振时的制振效果和鲁棒性能．     

Experimental and numerical study on plasma nitriding of AISI P20 mold steel

In this study, plasma nitriding was used to fabricate a hard protective layer on AISI P20 steel, at three process temperatures (450°C, 500°C, and 550°C) and over a range of time periods (2.5, 5, 7.5, and 10 h), and at a fixed gas N₂:H₂ ratio of 75vol%:25vol%. The morphology of samples was studied using optical microscopy and scanning electron microscopy, and the formed phase of each sample was determined by X-ray diffraction. The elemental depth profile was measured by energy dispersive X-ray spectroscopy, wavelength dispersive spectroscopy, and glow dispersive spectroscopy. The hardness profile of the samples was identified, and the microhardness profile from the surface to the sample center was recorded. The results show that ε-nitride is the dominant species after carrying out plasma nitriding in all strategies and that the plasma nitriding process improves the hardness up to more than three times. It is found that as the time and temperature of the process increase, the hardness and hardness depth of the diffusion zone considerably increase. Furthermore, artificial neural networks were used to predict the effects of operational parameters on the mechanical properties of plastic mold steel. The plasma temperature, running time of imposition, and target distance to the sample surface were all used as network inputs; Vickers hardness measurements were given as the output of the model. The model accurately reproduced the experimental outcomes under different operational conditions; therefore, it can be used in the effective simulation of the plasma nitriding process in AISI P20 steel.     

薄带连铸取向硅钢的热轧孪生行为

薄带连铸流程下取向硅钢粗大λ晶粒(〈100〉//ND,normal direction)的“遗传”会导致磁性能恶化.为解决这一问题,针对取向硅钢的热轧孪生行为开展研究,结果表明:凝固组织粗大的取向硅钢在650℃热轧时可产生大量112〈111〉形变孪晶,这与具有高层错能的硅钢在较高温度下难以孪生变形的传统认知不同.热轧过程中复杂的应力状态降低了变形孪晶的取向依赖性,由于具有更高的储存能,孪晶界/孪晶界及孪晶界/晶界交叉点成为再结晶形核的优先位置,大大提高了常化过程中的再结晶率,受沿孪晶界应变分布及孪晶间距离的限制,沿孪晶界形核的再结晶晶粒通常呈“饼状”,最终形成以细小且取向漫散的再结晶晶粒为主的常化组织,消除了初始凝固组织中有害的粗大λ晶粒.     

50Mn18Cr4V无磁钢的热变形行为

通过高温压缩热模拟实验,研究了50Mn18Cr4V高锰无磁钢在变形温度为900~1100℃、应变速率为01~10s-1条件下的热变形行为.结果表明,VC第二相的应变诱导析出对50Mn18Cr4V的热变形行为产生重要影响.当变形温度为900~1000℃,应变速率为5s-1时,VC第二相不能充分析出,与应变速率为1s-1相比,对动态再结晶的阻碍作用减弱.应尽量使实验钢在高温段完成热加工,并适当提高应变速率.随着变形温度降低到950℃以下,材料的塑性变差,若以较低的应变速率变形,容易造成晶界开裂;应变速率过高,容易造成流变失稳,因此,以5s-1的应变速率变形,较为适宜.确定了50Mn18Cr4V无磁钢的再结晶激活能为7769kJ/mol.通过实验数据回归,建立了实验钢的高温变形抗力模型.     

HCl中咪唑衍生物复配对碳钢的缓蚀作用研究

研制了一种咪唑衍生物(BBIM),利用失重法、动电位扫描极化法及SEM研究了BBIM与碘化钾和甲醛在质量分数5% HCl中按一定比例复配对碳钢的缓蚀效果,讨论了浓度、温度对缓蚀性能的影响,同时对缓蚀机理进行了探讨。结果表明两种复配缓蚀剂在5%HCl腐蚀环境中对碳钢均具有良好的缓蚀作用,是一种混合型缓蚀剂,缓蚀作用机理为协同机理。