Conductive and corrosion behaviors of silver-doped carbon-coated stainless steel as PEMFC bipolar plates

Ni–Cr enrichment on stainless steel SS316L resulting from chemical activation enabled the deposition of carbon by spraying a stable suspension of carbon nanoparticles; trace Ag was deposited in situ to prepare a thin continuous Ag-doped carbon film on a porous carbon-coated SS316L substrate. The corrosion resistance of this film in 0.5 mol·L-1 H₂SO₄ solution containing 5 ppm F- at 80℃ was investigated using polarization tests. The results showed that the surface treatment of the SS316L strongly affected the adhesion of the carbon coating to the stainless steel. Compared to the bare SS316L, the Ag-doped carbon-coated SS316L bipolar plate was remarkably more stable in both the anode and cathode environments of proton exchange membrane fuel cell (PEMFC) and the interface contact resistance between the specimen and Toray 060 carbon paper was reduced from 333.0 mΩ·cm2 to 21.6 mΩ·cm2 at a compaction pressure of 1.2 MPa.     

等离子喷涂熔滴的瞬时碰撞压力研究

采用数值模拟,研究了等离子喷涂熔滴碰撞基体后,作用在基体表面的瞬时压力分布变化过程和影响因素．研究表明,碰撞压力和熔滴的初始动能存在正比关系,碰撞压力集中作用在基体表面熔滴直径为２ ．５ 倍以内的区域．在该区域以外,碰撞压力值很小,这是造成扁平粒子与基体表面接触不完善的直接原因     

静电喷雾研究与应用综述

综述了静电喷雾研究与应用现状,主要就液体雾化、雾滴充电、荷电雾滴输运流场及雾滴在目标物上的沉积性能等几方面的研究进展作了回顾     

μm级钨粉材料在高能炸药爆炸加载作用下实现基体涂覆的新技术研究

爆炸喷涂技术是材料表面加工领域的研究热点。总结了现有爆炸喷涂技术,并在现有基础上提出了一种新技术——高能炸药爆炸加载喷涂技术。详细阐述了高能炸药爆炸加载喷涂技术的原理,分析了该技术在涂层制备方面的优缺点,并利用该技术进行了μm级钨粉材料涂层的制备。通过对钨涂层的检测,表明高能炸药爆炸喷涂制备的钨涂层具有较好的均匀性和致密性,制备过程热损失小,认为该技术具有宽广的应用前景。     

电弧喷涂铁基减摩涂层磨损性能的分析

在铝制发动机缸体内壁喷涂铁基减摩涂层代替在其内嵌套铸铁缸套,是实现汽车发动机缸体轻量化的一条重要途径。采用两种铁基合金制作铝制缸体内壁的减摩涂层,在干摩擦、浸油条件下分别进行磨损实验,并与耐磨性较好灰铸铁进行对比,结果显示干摩擦时金属氧化物的润滑效果较石墨差,而油液润滑条件下涂层耐磨性均优于灰铸。观察涂层发现其主要由扁平化粒子堆叠而成,粒子之间夹杂着带状氧化物,还存在一些未熔颗粒、孔隙,表明涂层的孔隙结构的储油效应和表面氧化物起到了明显的减摩作用。     

碳氮强化电弧喷涂涂层合金组织与耐磨性能

研制一种新型的碳氮合金化喷涂丝材,通过高速电弧喷涂设备在Q235低碳钢板表面制备耐磨合金。用扫描电镜观察合金涂层形貌,用EDS分析涂层化学成分,并用显微硬度仪检测涂层显微硬度及磨粒磨损试验机测量涂层磨损失重。研究涂层的成形、耐磨损性能及其机制。结果表明:使用添加N替代部分C进行碳氮强化的喷涂丝材所制备的涂层合金成形良好,涂层组织均匀,结构致密;涂层显微硬度平均值为568HV0.1,最高值达593HV0.1;涂层结合强度达到45.8MPa; 细小的碳氮化物硬质相颗粒使涂层具有良好的耐磨损性能,其耐磨性是4Cr13不锈钢涂层的1.58倍。     

超音速火焰喷涂WC-12Co涂层的磨粒磨损行为研究

对超音速火焰WC-12Co涂层进行了磨粒磨损试验,研究了磨粒磨损试验参数对涂层性能的影响,并通过SEM对涂层表面的显微形貌进行了观察分析,探讨了WC-12Co涂层的磨粒磨损失效机制.结果表明:涂层的失重随试验载荷及磨料直径的增加而增加;在载荷或磨料粒度较大时.涂层的磨损失效形式为晶粒剥落及犁沟切削相结合;当载荷或磨料粒度较小时,其失效形式主要为晶粒剥落方式.     

浅谈高空机械喷撒天敌在农林害虫防治中的应用

探讨了飞行器及机械喷撒天敌在农林害虫防治上的应用,观察、研究了肿腿蜂、赤眼蜂、蒲螨、瓢虫等喷剂天敌的成活率和防治率。结果表明：高空机械喷撒天敌喷剂有很高的成活率,防治效率和防治效果高于传统的天敌防治。     

Experiment on Gas Hydrates Formation by Water Spraying

An experimental investigation of natural gas hydrate formation has been conducted in a high-pressure water spraying reactor,which is cooled by the circulation water through an external cooling jacket.The results show that the morphology of hydrates formed by water spraying is like ice-slurry,which depends on the initial pressure and temperature.At a certain reaction pressure,the rate of hydrate formation is increasing with lower temperature.And also,the induction time of hydrate formation can be greatly sho...     

天然气水合物在喷雾装置中的制备

采用雾流强化实验装置对天然气水合物的合成进行实验研究,发现该方法能增加气-水接触面积、强化传热传质以及加速水合物生成.实验数据验证了反应压力与系统过冷度是水合物快速形成的重要影响因素.当反应温度一定时,初始压力越大,反应压降速率越大;过冷度越大,对应的压降速率越大.