机械活化及其在湿法炼锌中的应用

本文首先概述矿物机械活化的基本原理及其对矿物强化作用。然后对其在湿法炼锌中的硫化锌精矿焙烧、锌焙砂浸出、硫化锌精矿直接浸出等方面应用取得进展进行综述。     

Nanometer properties of oceanic polymetallic nodules and cobalt-rich crusts

An ammonia leaching process was utilized to extract Co, Ni and Cu from oceanic polymetallic nodules, whereas an acid leaching process was utilized to extract Co, Ni, Cu, Zn and Mn from cobalt-rich crusts. Both processes produced nanometer materials—ammonia leaching residue and acid leaching residue. A systematic study was conducted on the phase, composition and physicochemistry properties of these residues. The result shows that both residues contain a large amount of nanometer minerals. Ammonia l eaching residue mainly consists of rhodochrosite, with the average grain diameter of 17.9 nm; whereas the acid leaching residue mainly consists of well-developed bassanite, with the average grain deameter of 9.5 nm. The bassanite also has a microporous structure, the volume of the pore space is 1.23 × 10⁻² mL/g. Both the ammonia and acid leaching residues have a large specific surface area, and they display a strong adsorption capacity to saturate sodium chloride vapour, N₂ and SO₂. Both residues have high contents of rare earth elements, and most of these elements exist in the state of ionic adsorption. The content of σ FeO is high. The P₂O₅ enrichment is observable in acid leaching residues. The unique composition and nanometer solid properties of the leaching residues displayed their potential value and promised a bright future for their application in the field of environmental protection and materials.     

污灌系统氮素在土壤中的转化与渗漏污染

通过原状土体模拟试验，以多次污灌废水浓度的Ｃ＋２Ｓ为进水浓度，揭示了污灌废水中氨氮在土壤中的转化规律以及引起地下水污染的原因，提出了污灌的农用与防止地下水污染的具体措施。     

Supergene mobility of noble metal elements in black rock series

In order to discuss the supergene mobility of noble metal elements in black rock series, measurements have been conducted with ICP-MS method for the contents of Ru, Rh, Pd, Ir, Pt, Au and Ag in the primary jordisite-rich black shale ore, in the supergene leached jordisite-rich black shale ore, in the pyrite-rich black shale ore and in the water of pit, well and stream of the mining area near Zhongnan Village, Zunyi District of Guizhou Province. The temperature, pH, electric conductivity, dissolved oxygen of the water were also measured. The pit water is acidic with high electrical conductivity and low dissolved oxygen. The total content of platinum group elements in the primary pyrite-rich black shale ore is only 1/13 of that in the primary jordisite-rich black shale ore. The Ag content in the former is only a half of that in the latter while the Au contents in the two kinds of ores are almost the same. Being leached under supergene condition, the contents of most of the noble metal elements except Au in the jordisite-rich black shale ore greatly decrease; the leaching rates of Rh, Pd, Pt, the total platinum group elements and Ag reach as high as 66.72%～74.79%, revealing that under supergene condition, platinum group elements and Ag can migrate along with water; the ratios of Ag/Au, Pd/Ru, Pt/Ir and(Pt+Pd)/(Ru+Rh+Ir) are remarkably decreased, displaying that Pt and Pd relative to Ru, Rh and Ir, Ag relative to Au bear more active mobility. The noble metal elements in the black rock series near Zhongnan Village might be mobilized and migrate under the procession of "cold water" rich in [SO4]2- with pH value being about 2.4 at a temperature below 50 ℃.     

Zn(Ⅱ)-(NH4)2SO4-H2O体系浸出锌烟尘

提出硫酸铵浸出法处理锌烟尘的新工艺。该工艺利用不同温度下锌在硫酸铵溶液中的溶解度的差别,先在高温下将锌浸入溶液然后降温冷却,使锌呈含F和Cl很低的复盐析出,然后回收。以株冶集团锌烟尘为试料,对浸出过程进行研究。研究结果表明:浸出温度和硫酸铵浓度显著影响锌的浸出率;最佳浸出条件是:液固比为16?1,硫酸铵浓度为4.0 mol/L,pH值为5.5,浸出温度为90℃,浸出时间为4 h,在该条件下,按渣含锌计算的浸出率达到85.16%。     

潘二矿煤系高岭岩脱除Fe_2O_3工艺的研究

本文通过对潘二矿煤系高岭岩脱杂工艺实验，认为较佳脱杂效果的工艺条件为焙烧温度430℃，浸出温度120℃，盐酸浓度20％，浸出时间120min。     

混联法生产氧化铝的熟料烧结问题探讨

采用贵州低品位铝土矿和溶出拜耳赤泥、碱、石灰配制的混合料烧结,在A/S=2.84±、[N]/[A]+[F]=0.97±、[C]/[S]=2.11±、t℃=1275±时,可以获得较好的效果。氧化铝标准溶出率η(?)标=94.64%,氧化铝工业溶出率=92.68%。     

真空碳热还原酸浸含钛高炉渣制备TiC分析

含钛高炉渣中含有20%~30%的TiO_2,是一种附加值较高的二次资源,但在综合利用过程中存在氧化物还原难度大,硅钛难分离,二次污染严重等问题。基于热力学理论基础,采用真空碳热还原联合酸浸工艺处理含钛高炉渣制备TiC。结果表明:真空有助于钛氧化物彻底还原,可实现渣中硅钛彻底分离,减少酸耗量,降低二次污染。真空碳热还原联合酸浸工艺处理含钛高炉渣(TiO_2含量23%左右)制备TiC的最佳条件为:炉渣粒度200目,还原温度1 673K,渣碳质量比100∶38。     

Reductive leaching of low-grade manganese ore with pre-processed cornstalk

Cornstalk is usually directly used as a reductant in reductive leaching manganese. However, low utilization of cornstalk makes low manganese dissolution ratio. In the research, pretreatment for cornstalk was proposed to improve manganese dissolution ratio. Cornstalk was preprocessed by a heated sulfuric acid solution (1.2 M of sulfuric acid concentration) for 10 min at 80°C. Thereafter, both the pretreated solu-tion and the residue were used as a reductant for manganese leaching. This method not only exhibited superior activity for hydrolyzing corn-stalk but also enhanced manganese dissolution. These effects were attributed to an increase in the amount of reductive sugars resulting from lignin hydrolysis. Through acid pretreatment for cornstalk, the manganese dissolution ratio was improved from 50.14%to 83.46%. The pre-sent work demonstrates for the first time the effective acid pretreatment of cornstalk to provide a cost-effective reductant for manganese leaching.