Preparation, structure, and properties of polyurethane foams modified by nanoscale titanium dioxide with three different dimensions

TiO2-based nanosheets (TiNSs), TiO2-based nanotubes (TiNTs) were prepared by hydrothermal processing, and polyurethane foams with TiO2 nanopowders (P25), TiNSs and TiNTs were synthesized by free-rising foaming method. The Fourier-transform infrared (FT-IR) spectra show that the addition of titanium dioxide does not affect the chemical structure of polyurethane foam. However, microscope observations show that PU/TiNSs composite foams have more uniform cells and the average aperture smaller than that of pure poly-urethane foams. According to the results of thermal analysis, the PU/TiNSs composite foams have better thermal stability, the temperature of decompostion occurring with a maximum weight loss rate is about 30 ℃ higher than that of pure PU foams. The decompostion temperatures are 167 ℃ and 148 ℃ for the PU/P25 composite foams and the PU/TiNTs composite foams respectively, which are lower than that of pure PU foams. Moreover, with the addition of the fillers, the sound absorption property also has changed; the addition of TiNSs improved the sound absorbing property efficiently. The better thermal stability and sound absorption of PU/TiNSs composite foams are mainly due to the uniform cells diffuse and smaller aperture.     

嵌段聚氨酯脲的序列分布研究

用高分辩１３ＣＮＭＲ技术研究了不同硬段浓度的聚醚型嵌段聚氨酯脲（ＰＵＵ）弹性体的序列长度和序列分布。结果表明，ＰＵＵ的硬段平均序列长度随ＰＵＵ中聚脲的摩尔浓度增加而增加；嵌段ＰＵＵ内软硬段的链结构也随聚脲摩尔浓度的增加由交替共聚向嵌段共聚变化，硬段浓度愈高，嵌入的硬段长度也愈大。     

流动注射在线聚氨酯柱富集火焰原子吸收法测定矿样中的痕量金

本文用聚氨酯泡沫塑料作为柱材料，研究制定了在线预富集流动注射火焰原子吸收测定痕量金的新方法．实验溶液含金０．０２μｇ／ｍｌ，酸度为５％～１０％王水，以甲基异丁酮为洗脱液．当流速为１６ｍｌ／ｍｉｎ时，富集倍数为进样１ｍｉｎ富集５０倍．该方法选择性好，用于地质矿样中痕量金的测定，相对误差为１．１％．     

聚丙烯-聚氨酯共混体系的结构与性质

本文对聚丙烯(PP)与热塑性聚氨酯(PU)共混体系的相容性、分散相的形态、熔体的流变性质、共混物的热性质及初生纤维的染色性等作了初步的研究。结果表明,PP与PU为不相容的两相体系,PU以分散相分布于PP基质之中,其尺寸及形状随组成而变;共混物熔体的粘度-组成曲线上呈现一个极小值:当PU含量较低时,共混物的耐热性与纯PP相近;初生纤维的染色性也随PU含量的增加,有较明显的改善。     

热塑型聚氨酯弹性体(TPUE)应力松弛过程的研究

文中以加速应力松弛法研究了热塑型聚氨酯弹性体(TPUE)的应力松弛过程,将从TPUE大形变弹性分子理论推导出的单向拉伸应力-应变关系,结合三种承受应力链的键数随时间衰减的动力学方程,建立了应力松弛过程的定量表达式,并以高温和大形变量实验数据对理论进行了验证.以二元回归法求得分子参数α,k,k_3,并进而求得松弛活化能△E_3.     

聚氨酯-聚丙烯腈共混体系的动态力学性质及其力学模型的研究

本文研究了聚氨酯(PU)-聚丙烯腈(PAN)共混体系的动态力学性质和相逆转现象。发现当PAN含量为30—40％的范围内,共混体系发生了连续相与分散相的逆转;进一步通过3个力学模型,描述了该共混体系的模量-组成关系以及动态力学温度谱。所有实验数据都落在理论预测的范围内,并与Budiansky模型符合得最好。     

邻苯二甲酸二丁酯增塑的热塑性共聚醚聚氨酯和聚氨酯脲体系

研究了不同含量的邻苯二甲酸二丁酪对基于不同相对分子质量的环氧乙烷－四氢呋喃共聚醚、二苯甲烷二异氰酸酯／异佛尔酮二异氨酸酯、１，４－丁二醇／乙二胺的各类热塑性聚氨酯和聚氨酯脲弹性体的力学性能和软段相玻璃化转变温度Ｔｇ的影响．各类弹性体具有令人满意的拉伸强度和延伸性．对邻苯二甲酸二丁酯与各类弹性的混溶能力进行了初步探讨．     

聚酯型聚氨酯化学组成的研究

本文报导了聚酯型聚氨酯水介和分离方法,经红外光谱(IR)、核磁共振氢谱和碳谱(H—NMR和~(13)C—NMR)鉴定,未知样品(系化工部二局提供进口PU型粘结剂)水介产物的化学组成是4,4′—二氨基二苯基甲烷、1.4—丁二醇和已二酸。     

塑料－玻璃粘接用UV固化胶粘剂的性能

探讨了活性单体、预聚体及偶联剂对UV固化胶粘剂的粘接强度、体积收缩的影响，结果表明，极性单体A、偶联剂B的加入有利于提高胶粘剂的粘接强度，芳香族聚氨酯预聚体胶粘剂体系的粘接强度较高，活性单体官能度越高，体积收缩越大。所研制胶粘剂的剪切强度可达5.98MPa，体积收缩为3.67％，在可见光区透光率为97％，玻璃化转变温度为88.02℃。     

聚氨酯石墨抗静电防腐涂层在高硫原油中的耐蚀性研究

针对高硫油对原油储存设备腐蚀严重的实际,选用聚氨酯树脂为成膜物质,石墨为导电介质制备抗静电防腐涂层,采用失重法研究了石墨含量、硫浓度、温度对涂层耐蚀性的影响.结果表明:不含石墨及w(石墨)在25%时,涂层质量的增加主要是由聚氨酯活性基团与介质中的硫反应引起,w(石墨)在55%时涂层质量的增加主要是由渗透引起;不含石墨及w(石墨)为25%时涂层增重较大,w(石墨)为55%时涂层增重最大.硫含量增加使不含石墨的涂层质量增加,当w(石墨)在25%~45%时,涂层质量增加与硫含量无关.温度升高使不含石墨的涂层质量增加,当w(石墨)为25%~45%时,温度升高涂层质量变化较小.因此,聚氨酯石墨抗静电防腐涂层w(石墨)为35%~45%时,其耐蚀性最好.