Improved dehydriding property of polyvinylpyrrolidone coated Mg-Ni hydrogen storage nano-composite prepared by hydriding combustion synthesis and wet mechanical milling

In this work, polyvinylpyrrolidone(PVP) coated Mg_(95)Ni_5 nano-composites were prepared by hydriding combustion synthesis(HCS) plus wet mechanical milling(WM) with tetrahydrofuran(THF) and donated as WM-x wt% PVP(x = 1, 3, 5 and 7) respectively. The phase compositions, microstructures and dehydriding property, as well as the co-effect of PVP and THF were investigated in detail. XRD results showed that the average crystal size of MgH_2 in the milled Mg_(95)Ni_5 decreased from 23 nm without PVP to 18 nm with 1 wt% PVP. The peak temperature of dehydrogenation of MgH_2 in the milled Mg_(95)Ni_5 decreased from 293.0 ℃ without THF to 250.4 ℃ with THF. The apparent activation energy for decomposition of MgH_2 in WM-7 wt% PVP was estimated to be 66.94 kJ/mol, which is 37.70 kJ/mol lower than that of milled Mg_(95)Ni_5 without THF and PVP. PVP and THF can facilitate the refinement of particle size during mechanical milling process. Attributed to small particle sizes and synergistic effect of PVP and THF, the composites exhibit markedly improved dehydriding properties.     

正火对高Cr马氏体耐热钢组织和性能的影响

通过光学显微镜、透射电镜(TEM)及扫描电镜(SEM)分析,研究了正火处理对高Cr马氏体耐热钢显微组织、力学性能及断裂机理的影响.结果表明,900~970℃正火后,晶粒尺寸十分细小,在10μm以下.1060~1200℃正火晶粒尺寸迅速增长,1060℃正火晶粒尺寸约为33μm.经过1060℃×2h正火+760℃×3h回火热处理后,室温和600℃高温拉伸屈服强度分别达到535MPa和380MPa,综合力学性能优良,而1060℃长时间正火对力学性能并无明显影响.1060℃×2h正火+760℃×3h回火热处理后得到破碎的晶粒细小回火马氏体组织,晶界上200~300nm M₂₃C₆和晶内5~50nm MX型弥散析出有效地阻碍位错运动,进而提高了材料力学性能.     

力学性能对矿柱体系破坏影响的三维数值分析

在深部高应力等复杂地质条件下开采时,由多个矿柱构成的矿柱体系的稳定性对矿山安全生产至关重要.利用RFPA^3D-Parallel程序,研究了单轴抗压强度对串行和并行矿柱体系破裂过程的影响.结果表明,串行矿柱中强度较弱部分的失稳决定整个体系的稳定,对该段加固和监测有助于体系的稳定性控制;对并行布设的矿柱体系,其压力传递与柱的抗压强度密切相关,较弱柱先破坏,应力依次向强度较高的柱转移,直到矿柱系统失稳;可将声发射数的多峰现象或声发射累积增长阶梯型弧段作为矿柱体系中弱柱失稳破裂、应力向相邻强柱转移的依据.     

Ti微合金化汽车大梁钢510L的组织性能

通过层流冷却及卷取过程模拟实验和实验室热轧实验研究了冷却工艺参数对Ti微合金化汽车大梁钢510L组织性能的影响规律,并在生产现场进行了工业试制.结果表明,大冷速有利于弥散细小的TiC粒子析出,冷速和终冷温度对实验钢强度的影响是细晶强化、析出强化和相变强化共同作用的结果,N含量显著影响Ti的析出强化效果,在冶炼时应严格控制钢中的N含量,否则将对钢板的性能产生较大的影响.实现了低成本Ti微合金化汽车大梁钢510L的批量稳定生产.     

马克思关于科学技术本质的认识及其当代价值

以历史唯物主义的基本原则——社会历史性原则来考察科学技术的本质,是马克思主义科技哲学的基本内涵。马克思在工业革命背景中认识到科学技术是生产力,是“最高意义上的革命力量”,同时以辩证的视角和历史的维度,揭示了资本主义社会的逐利特质使得科技异化在所难免。当代中国的创新驱动发展战略,正是中国共产党几代领导集体在继承和发展马克思关于科学技术本质的认识基础上形成的现代科技发展观。     

基于机械式变速器脱挡故障分析与预防

脱挡是汽车变速器的常见故障之一,笔者从机械式变速器脱挡故障现象入手,从整车和变速器两方面对脱挡故障展开分析,并提出了预防解决措施,提升机械式变速器可靠性能。     

浅谈天车“抬”吊巨大设备吊装点的精确计算

为保证设备的安全吊装,分析建立了一个数学模型,计算确定吊装点的精准设置位置,为吊装方案的细化编制和起重吊装的实际操作提供数据上的依据和支持,精确吊装方法和吊装点对制定吊装方案具有决定意义。     

Development of liquid-nitrogen-cooling friction stir spot welding for AZ31 magnesium alloy joints

A liquid-nitrogen-cooling friction stir spot welding (C-FSSW) technology was developed for welding AZ31 magnesium alloy sheets. The liquid-nitrogen cooling degraded the deformability of the welded materials such that the width of interfacial cracks increased with increasing cooling time. The grain size of the stirred zone (SZ) and the heat-affected zone (HAZ) of the C-FSSW-welded joints decreased, whereas that of the thermomechanically affected zone (TMAZ) increased with increasing cooling time. The maximum tensile shear load of the C-FSSW-welded joints welded with a cooling time of 5 or 7 s was larger than that of the friction stir spot welding (FSSW)-welded joint, and the tensile shear load decreased with increasing cooling time. The microhardness of the C-FSSW-welded joints was greater than that of the FSSW-welded joint. Moreover, the microhardness of the SZ and the HAZ of the C-FSSW-welded joints increased, whereas that of the TMAZ decreased, with increasing cooling time.     

渗碳体形态对高碳珠光体钢组织及性能的影响

为研究SWRS82B钢不同条件下进行的大过冷工艺所形成的渗碳体形态对珠光体亚结构组织及性能的影响,制定相关热处理工艺:将试样在880℃奥氏体化15 min后,以70,100,200℃/s的冷速过冷到300℃等温3~15s,之后升温至珠光体区等温1min,最后快冷至室温.通过SEM和TEM观察,以及MTS拉伸试验机得到的数据,结果表明,在过冷时间为3s的前提下,随着冷速的增长,渗碳体由完整片层状发生不同程度的碎化.在200℃/s时,渗碳体已经大面积碎化,并发现大量的纳米级渗碳体,抗拉强度表现为先降低后升高,伸长率持续升高.当冷却速度为70℃/s时,随着过冷时间的延长,抗拉强度和伸长率都表现为先降低后增大的特点.纳米渗碳体随着过冷时间的延长开始减少,到达15s时,开始出现了贝氏体组织.     

w(Co)对CB2钢显微组织和力学性能的影响

为研究w(Co)对CB2钢微观组织和力学性能的影响，调整CB2钢中w(Co)为0.5%，1.0%，1.5%，2.0%和3.0%.利用光学显微镜(OM)、扫描电镜(SEM)、室温拉伸等检测方法研究w(Co)对试验钢微观组织和力学性能的影响规律，结合Thermo-Calc和JMatpro-7.0模拟结果解释其影响机理.研究发现:w(Co)增加提高铬当量的值，使试验钢中δ铁素体含量减少，当w(Co)增加到1.5%时，δ铁素体基本消失;材料的抗拉强度随w(Co)的增加而增加，而延长率则先增加后降低;结果表明，w(Co)为1.5%时综合性能较好，即抗拉强度达到805.13MPa，延长率达到20.4%，布氏硬度为260.