电渣重熔用渣料烘烤过程的失重现象

在实验室条件下采用热重分析方法研究了电渣重熔用渣料在烘烤过程中的失重现象,分析了渣料中易水化成分含量与烘烤时间的关系,并重点研究了在渣料完全失重情况下,渣层厚度与烘烤时间、烘烤温度与烘烤时间之间的关系,并通过数值拟合方法建立了方程.结合固态热分解机理对实验过程进行了分析,烘烤初期热分解过程受晶核形成及长大控制,反应后期主要受扩散反应控制.实验结果将为现场渣料烘烤提供指导.     

酸浸对钙化焙烧提钒工艺钒浸出率的影响

采用稀硫酸浸出法提取钙化焙烧后钒渣中的钒,考察了浸出参数:物料粒度、体系pH值、浸出温度和时间、液固比(L/S)、搅拌速度对钒及杂质元素浸出率的影响.结果表明:物料粒度小于75μm时对提高钒浸出率影响较小;液固比从2∶1增加到7∶1,搅拌速度由100增加到500r/min时,钒浸出率增长幅度均低于3%;钒浸出率在浸出前15min内迅速升高,之后增长变缓;浸出体系pH值对钒及杂质浸出率影响显著,pH值为2~3时钒浸出率达90%,杂质元素Ca,Mn,Mg,Al,Si,P浸出率为10%~30%;在较佳浸出条件下:粒度96～75μm,pH值为25,温度55℃,时间30min,L/S为3,搅拌速度500r/min,钒浸出率超过91%.     

响应曲面法优化钒渣微波钙化焙烧提钒工艺

采用相应曲面法,建立钙化添加剂用量、焙烧温度、焙烧时间与钒浸出率关系的数学模型,对钒渣微波钙化焙烧提钒工艺进行优化,并对试验结果的可靠性进行分析与验证。研究结果表明,采用响应曲面法优化钒渣微波钙化焙烧提钒工艺参数是可行的;微波钙化焙烧工艺参数对钒浸出率的影响从大到小依次为钙化添加剂用量、焙烧温度、焙烧时间;最佳焙烧参数为焙烧温度861.69℃、钙化添加剂用量1.02、焙烧时间106.31 min,此时钒的浸出率可达93.82%。     

某高磷鲕状赤铁矿磷赋存状态及还原焙烧脱磷研究

采用浸出、电渗析等试验方法研究了尼日利亚高磷鲕状赤铁矿中磷的赋存状态并采用XRD和SEM分析添加脱磷剂Na2CO3直接还原焙烧产物的特性.结果表明,含磷矿物主要是呈微细粒包裹体嵌布在铁矿物鲕粒的裂隙或孔洞中的纤磷钙铝石(CaAl3(OH)6(HPO4)(PO4))、蓝磷铝铁矿(FeAl2(PO4)2OH·6H2O)以及均匀分散在铁矿物中的磷.通过添加脱磷剂Na2CO3的还原焙烧磁选可实现高效铁磷分离.磷通过两种方式去除:一部分含磷矿物与金属铁分离,存在于脉石矿物中,通过磨矿磁选可以有效去除,一部分含磷矿物与Na2CO3反应生成溶于水的磷矿物,最终使得还原铁产品中的磷含量降低.     

Comparison of the mechanisms of microwave roasting and conventional roasting and of their effects on vanadium extraction from stone coal

Experiments comparing microwave blank roasting and conventional blank roasting for typical vanadium-bearing stone coal from Hubei Province in central China, in which vanadium is present in muscovite, were conducted to investigate the effects of roasting temperature, roasting time, H₂SO₄ concentration, and leaching time on vanadium extraction. The results show that the vanadium leaching efficiency is 84% when the sample is roasted at 800℃ for 30 min by microwave irradiation and the H₂SO₄ concentration, liquid/solid ratio, leaching temperature, and leaching time are set as 20vol%, 1.5:1 mL·g-1, 95℃, and 8 h, respectively. However, the vanadium leaching efficiency achieved for the sample subjected to conventional roasting at 900℃ for 60 min is just 71% under the same leaching conditions. Scanning electron microscopy (SEM) analysis shows that the microwave roasted samples contain more cracks and that the particles are more porous compared to the conventionally roasted samples. According to the results of X-ray diffraction (XRD) and Fourier-transform infrared (FTIR) analyses, neither of these roasting methods could completely destroy the mica lattice structure under the experimental conditions; however, both methods deformed the muscovite structure and facilitated the leaching process. Comparing with conventional roasting, microwave roasting causes a greater deformation of the mineral structure at a lower temperature for a shorter roasting time.     

高硫铝土矿微波焙烧预处理

为了解决高硫铝土矿马弗炉焙烧脱硫效率不高问题,采用微波加热方式对高硫铝土矿进行焙烧,考察了焙烧温度和焙烧时间对矿物中硫含量的影响。用XRD技术对焙烧矿物晶型结构进行了分析,结果表明,微波焙烧温度400 ℃、焙烧时间2 min时,焙烧矿中硫元素含量已低于0.7%;微波焙烧温度550℃、焙烧时间10 min时,焙烧矿中硫元素含量为0.23%。微波使黄铁矿分离出S 2-,并促使S 2-向表面扩散与氧反应生成SO2气体,加速硫的逸出,提高了脱硫效率。     

赤铁矿石隧道窑直接还原助还原剂的作用及机理

对隧道窑直接还原焙烧--磁选法处理低品位难选赤铁矿石进行了探讨,重点研究助还原剂NCP的作用及机理.以煤作还原剂,质量分数为20%,CCO和NCP为助还原剂,质量分数分别为15%和5%,在焙烧温度为1200℃,焙烧时间为8 h的条件下,可以得到铁品位92.61%、铁回收率92.38%的铁精矿.利用X射线衍射和扫描电镜对助还原剂NCP的作用机理进行分析.结果表明NCP可以与原矿中石英发生反应,生成硅钠石和钠长石,破坏原矿结构,使还原性气体更易与赤铁矿接触发生还原反应生成金属铁.     

刀具低频脉冲磁化处理装置的研制与应用

介绍了脉冲磁化处理的原理，利用所研制的磁化处理装置对高速钢钻头进行了现场正交优化实验。结果表明，脉冲磁化处理能够明显地提高高速钢刀具寿命。     

圆柱型螺线管磁体的最佳形状

提出在给定功率的条件下 ,使均匀电流密度圆柱型螺线管磁体中心附近一定区域内磁场大于某一阈值的螺线管磁体最佳形状问题 ,运用 MATL AB工具给出计算结果 ,并作了讨论 .     

球团用膨润土高温焙烧活化改性试验

探讨了膨润土焙烧活化改性的机理,找到了焙烧活化的最佳工艺参数,即焙烧温度为450℃,焙烧时间为2h。并用改性前后的膨润土进行了对比造球试验,试验结果表明球团的生球落下强度、抗压强度、爆裂温度均有所提高。