锻热淬火对钢材机械性能的影响因素分析

普通淬火是钢材强化的主要途径，但淬火零件韧性不足，淬透性差，限制了钢材的应用范围．锻热淬火，细化钢材亚结构组织，能有效弥补普通淬火的缺陷，同时节能降耗，为发展少无切削钢材提供了广阔前景。     

弹丸侵彻钢纤维混凝土数值模拟

为了对弹丸侵彻钢纤维混凝土问题进行数值模拟研究,在有限元计算中引入了Holmquist-Johnson-Cook累积损伤材料模型以描述钢纤维混凝土的非线性变形及断裂特性,弹丸作为刚体处理.侵彻深度计算结果与在φ14.5 mm弹道炮上所获得的试验结果相吻合,并很好地模拟了在侵彻过程中钢纤维混凝土靶的成坑、层裂现象.在此基础上分析了钢纤维混凝土这种新型复合材料抗侵彻性能的影响因素.计算结果表明,HJC本构模型用来描述钢纤维混凝土的侵彻问题是可行和有效的.     

A Theoretical Approach for Estimating Fracture Toughness of Ductile Metals

Fracture toughness is very important when applying Damage Tolerance Design and Assessment Techniques. The traditional testing approach for obtaining fracture toughness values is costly and time consuming. In order to estimate the fracture toughness of ductile metals, the fracture mechanics theory, materials plastic deformation theory and materials constructive relationships are employed here. A series of formulae and a theoretical approach are presented to calculate fracture toughness values of different materials in the plane stress and plane strain conditions. Compared with test results, evaluated values have a good agreement.     

聚能射流水中侵爆盖板B炸药仿真研究

为获得聚能射流对水中盖板B炸药侵爆作用能力,开展水层厚度影响规律研究.基于准定常侵彻理论得到了紫铜聚能射流侵彻水介质时射流速度计算式;建立侵爆仿真模型,研究了聚能射流水中成型与运动、侵彻盖板及起爆装药的变化特性,计算给出了射流侵彻盖板前后的速度和直径的变化,结果表明,射流侵爆水中盖板B炸药的临界水层厚度为261 mm,并依据Held判据得出B炸药的起爆阈值为18.598 mm³·μs^-2.研究结果对聚能射流水下毁伤技术的应用提供技术参考.     

激光重熔高速电弧喷涂FeNiCrAl涂层的组织与断裂韧性

采用激光技术对高速电弧喷涂FeNiCrAl涂层进行重熔处理.分析了重熔前后涂层的组织结构、物相成分、显微硬度与断裂韧性.结果表明:重熔后,喷涂层片层状堆叠结构与孔隙得到消除,组织结构变得均匀、致密,涂层与基体由机械结合变为冶金结合.喷涂层物相主要有α-Fe及金属间化合物AlFe₃,AlFe和Al_0.4Fe_0.6,重熔后,生成了新相Fe-Cr,［Fe, Ni］固溶体和碳化物NiC_○x.重熔后涂层的平均显微硬度为7.79GPa,约为基体硬度(2.5GPa)的3倍,约为喷涂层硬度(6.0GPa)的1.3倍.载荷为4.9,9.8N时,喷涂层的压痕尖头出现裂纹,涂层平均断裂韧性为1.20MPa·m^1/2,载荷为2.94~9.8N时,重熔后涂层的压痕尖头均没有观察到裂纹.     

Characteristic investigation of trilayered Cu/Al8011/Al1060 composite: Interface morphology,microstructure, and in-situ tensile deformation

In this work, Cu/Al8011/Al1060 trilayered composite with an ultrathin copper layer was fabricated successfully by the hybrid process of cast-rolling and hot-roll-bonding. The effects of heat treatment were investigated on the microstructure and mechanical behavior of the composite. The results showed that annealing temperatures above 300 ​°C led to the formation of new intermetallic compounds that joined their initial counterparts. Also, the interface growth was fast above 340 ​°C. It was found that the annealing temperature of 320 ​°C led to the optimal tensile properties of the composite. Through rolling, hard-brittle IMCs imposed intense plastic strains on the surrounding regions, resulting in further grain refinement of both metals in the vicinity of the interface. Although the kernel average misorientation of the trilayered composite was almost identical with the Cu/Al8011 bimetal, its amount was considerably decreased after heat treatment, as the distorted structure changed into a nearly strain-free one using the restoration phenomenon. The SEM-based in-situ tensile test showed that crack initiation occurred within the IMCs and propagated into the Cu strip, leading to its early fracture. However, the strength-displacement curve during in-situ tensile deformation did not decrease significantly due to the ultrathin copper layer.     

均匀化退火和锻造对双相耐磨钢强韧性的影响

研究了一种低合金双相耐磨钢经均匀化退火和锻造处理后的微观组织和强韧性能.结果表明:经980℃均匀化退火4,8 h和1 150℃锻造处理后,实验钢显微组织主要为板条状马氏体、针状贝氏体及少量残余奥氏体,锻造处理后的晶粒度最小为7.0~7.5级,均匀化退火处理后的晶粒度最大为6.5~7.0级.均匀化退火的保温时间是影响双相耐磨钢力学性能的主要因素,实验钢保温4 h时的冲击韧性和延伸率值高于保温8 h的值.锻造比均匀化退火更适宜于提高低合金双相耐磨钢的强韧性,优化工艺为始锻温度1 150℃、终锻温度800℃、锻造比2.     

直通型CT试样COD弹塑性换算

基于刚性转动假设和功等效原理,推导了直通型CT试样的裂纹嘴张开位移和加载线张开位移弹塑性换算公式,并采用Cr2Ni2MoV钢对公式进行试验验证.根据弹塑性有限元分析,刚性转动假设得到了很好的验证,刚性转动中心靠近裂尖位置且受材料本构关系的影响甚微,转动半径R仅与裂纹长度和试样宽度之比a/W有关.有限元分析和试验结果表明,直通型CT试样的COD弹塑性换算公式用于塑性功计算具有更好的精度.     

X100直缝埋弧焊管断裂韧性的裂纹尖端张开位移试验研究

为了检验X100直缝埋弧焊管的断裂韧性,采用三点弯曲多试样法,在室温、-10℃和-30℃下对该焊管的母材、热影响区和焊缝部位进行了裂纹尖端张开位移(CTOD)试验.测试结果表明:在同一温度下,CTOD试验的表观启裂值δ0.05、条件启裂值δi和最大载荷值δm的分布规律为母材最好,焊缝次之,热影响区最差;采用裂纹扩展阻力和撕裂模量表征的分布规律为母材最好,热影响区次之,焊缝最差;焊接热影响区组织中含有大量呈块状分布的铁素体,而粒状贝氏体等增强相的含量较少,这会造成其韧性下降,使焊管出现局部失稳现象.     

聚合物乳液对纤维增强轻集料混凝土力学性能的影响

研究了聚合物乳液的掺入对纤维增强轻集料混凝土的强度与弯曲韧性的影响,结果表明,掺入聚合物乳液虽然在一定程度上降低了抗压强度,但可以显著提高轻集料混凝土的劈裂抗拉强度和抗折强度.聚合物乳液的掺入可以有效提高纤维增强轻集料混凝土的韧性、降低其脆性,韧度系数最高可提高32倍.研究发现,聚合物乳液对钢纤维增强轻集料混凝土的强度和韧性的改善效果优于对聚乙烯纤维增强轻集料混凝土的改善效果.