碳酸二甲酯研制及合成方法的研究

介绍了碳酸二甲酯（DMC）的研制历程,提出了DMC的合成方法,并指出了DMC的应用方向。     

硅基一维纳米半导体材料的制备及光电性能

硅基一维纳米半导体材料是新型的硅基光电子材料，在硅基光电集成和纳电子领域有重要的应用前景．主要论述了硅基一维纳米半导体材料(纳米硅线、纳米ZnO线)的制备，着重一维纳米材料的阵列化制备，讨论了其生长机理，研究了硅基一维纳米半导体材料的的光学、电学等物理性能．     

2,3-双-(2-吡啶)喹喔啉-CuⅡ配合物的合成、表征及晶体结构

报道了配合物[Cu(DPQ)2(ClO4)](ClO4)·H2O·0.5CH2Cl2·CHCl3(DPQ=2,3-双-(2-吡啶)喹喔啉)的合成及表征(元素分析、电导、红外和紫外光谱).室温X-射线单晶衍射分析结果表明,标题配合物(C37.5H28Cl6CuN8O9,分子量=1010.92)处于正交晶系,Pmmn空间群,a=1.0547(2)nm,b=1.1819(2)nm,c=2.0014(4)nm,V=2.4949(9)nm,Z=2,Dc=1.346g/cm3,F(000)=1024,μ(MoKα)=0.813mm-1.最终精修得到的R及wR因子分别为0.0452和0.1070,独立衍射点个数为2367.配合物由分立的[Cu(DPQ)2(ClO4)] 阳离子,未配位的ClO4-阴离子和溶剂分子组成.中心Cu 离子分别与两个DPQ配体上的4个吡啶氮原子以及高氯酸根上的一个氧原子配位,其配位几何构型为理想四方锥.两个DPQ配体仅通过吡啶氮原子与Cu 离子螯合配位,形成两个七元环.此外,结构中两个平行喹喔啉环之间存在着π…π堆积相互作用.     

三维超分子体系[Cu(C5H4NCOO)2(H2O)2]·H2O的晶体结构及合成机理

Cu(Ⅱ)离子促进双酰胺配体N,N′-双异烟酰咪唑啉-2-硫酮的水解,进一步与水解产物异烟酸根自组装形成超分子配合物[Cu(C5H4NCOO)2(H2O)2]·H2O,通过X射线衍射对其晶体结构进行了测定.该晶体属于三斜晶系,空间群为P-1,所得晶胞参数为:a=0.634 49(13)nm,b=0.689 46(14)nm,c=0.918 33(18)nm,a=99.33(3)°,β=105.23(3)°,γ=108.17(3)°,V=0.354 99(12)nm3,Z=1,Dc=1.777 mg/m3,F(000)=195,μ=1.585 mm-1.最终偏离因子R=0.041 3,Rw=0.107 7.在该超分子化合物的基本结构单元中,中心Cu(Ⅱ)原子处于略微变形的平面四边形配位环境;各个结构单元之间通过氢键O-H…O相互连接,形成了具有层状结构的三维超分子化合物.     

铸造锰白铜合金的时效强化

以淬火态锰白铜合金为参考材料，研究对铸态锰白铜合金直接进行时效处理的可行性。制备成分为Cu20Ni20Mn的合金试样，选取不同的时效温度和时效时间，对铸态锰白铜合金直接进行时效处理，研究不同的时效工艺对锰白铜合金的强化效果。使用SEM、X—ray等观察试样的组织与结构，分析时效强化机理。试验结果表明：锰白铜合金在铸态下可以直接进行时效处理；在最佳时效工艺（时效温度400℃～470℃，时效时间为60～72h）条件下，硬度可达到HV400以上；并且发现MnNi相的析出是合金时效强化的主要原因。     

Er在Al-Cu-Mg-Ag合金中的存在形式及其均匀化工艺

采用扫描电镜观察、X射线衍射物相定性分析,研究元素Er在Al-Cu-Mg-Ag合金中的存在形式及其均匀化工艺。研究结果表明:Er元素主要以Al8Cu4Er相形式存在于铸态合金晶界,少量固溶于-αAl中;Al8Cu4Er相作为Al2Cu相的形核质点,与Al2Cu相共生于晶界,形成典型的枝晶偏析;与Al2Cu相相比,Al8Cu4Er相为难溶相,使得合金均匀化温度升高,成为均匀化过程中工艺的制约因素;采用420℃×6 h+510℃×24 h+520℃×6 h均匀化制度处理后,Al8Cu4Er相回溶至基体,合金晶界变薄,均匀化效果明显。     

Bleaching effect and nonvolatile holographic storage in doubly doped LiNbO<Subscript>3</Subscript>:Fe:Cu crystals

The bleaching effect, i. e. the crystal shows that decoloration after it is illuminated by ultraviolet light, has been observed in congruent LiNbO3:Fe :Cu crystals. Based on this bleaching effect, a new technique including the reco rding phase by two interfering red beams and fixing phase by both UV light and a coherent red beam has been experimentally investigated to realize nonvolatile holographic storage in LiNbO3:Fe:Cu. The results of proof-of-concept experiments confirm that bleaching effect becomes an alternative physical mechanism for nonv olatile holographic storage with high recording sensitivity and weak light-induced scattering noise.     

Cu doping effect on Mn sites of La2/3Ca1/3 MnO3 system

The temperature dependence of resistance and magnetoresistance at 77 K for Cu-doped La 2/3Ca 1/3Mn 1-xCu xO-3 have been investigated. Besides the transition similar to the Cu-free sample at ～260 K, a new transition at lower temperature appears for Cu-doped samples. The new transition moves toward low temperature with increasing of Cu content. A new conductive proceeding related to Cu ion may exist. Magnetoresistance at liquid nitrogen shows that MR increased three orders when x is changed from 0 to 0 15. Moreover, the main variation of magnetoresistance is below the field of 1 T.     

Raney铜催化剂上糠醛气相加氢制2—甲基呋喃

研究了糠醛气相加氢制２－甲基呋喃新型合金催化剂Ｒａｎｅｙ铜的制备方法。通过正交实验及单因素实验得到该催化剂在反应体系中最适宜的工艺条件,即反应温度２２０～２３０℃,氢醛比５∶１,床层高度１２．７ｃｍ左右,空速０．３３～０．４５ｈ－１,氢压０．０３～０．０８ＭＰａ。