Titanium effect on the microstructure and properties of laminated high boron steel plates

High-boron steel is an important material used for thermal neutron shielding. The appropriate amount of added boron must be determined because excessive boron may deteriorate the steel's workability. A uniform microstructure can be formed by adding titanium to boron steel. In this study, casting and hot rolling were used to fabricate laminated high-boron steel plates whose cores contained 2.25wt% boron and 0wt%-7.9wt% titanium. The effects of titanium content and hot-rolling and heat-treatment processes on the microstructure and properties of the laminated plates were studied. The results indicated that the optimum titanium content was 5.7wt% when the boron content was 2.25wt%, and that the best overall properties were obtained after heat treatment at 1100℃ for 4 h. The tensile strength, yield strength, and elongation at the specified temperature and holding time were as high as 526.88 MPa, 219.36 MPa, and 29%, respectively.     

干热岩水力压裂实验室模拟研究

 地壳中干热岩所蕴含的地热能量巨大,已成为世界各国重点研究开发的新能源。干热岩资源开发的增强型地热工程的场地试验研究投资大、周期长、风险大,在现场压裂和人工热储层建造示范工程前,实施干热岩水力压裂实验室研究很有必要。为此,吉林大学深部地热和干热岩研究团队建设了大尺寸高温高压下干热岩水力压裂实验室模拟系统,为现场压裂工艺设计和储层改造提供参数和技术支持。本文介绍模拟系统的实验设备、实验条件和初步的实验研究成果。     

中国干热岩资源主要赋存类型与成因模式

 干热岩资源作为地热资源重要的组成部分,以其清洁、稳定、可再生的资源优势及巨大的高温发电潜力,越来越受到关注。中国自20 世纪90 年代开始对干热岩资源进行调查研究,并在不同地质背景条件预测或勘查到干热岩资源,然而至今仍未对干热岩资源的赋存形式进行分类及开展干热岩资源成因机制研究,阻碍了中国干热岩资源的调查与精细潜力评价。在阐述干热岩资源赋存的指标参数的基础上,通过对国内外已发现干热岩资源的成因模式分析,结合中国地壳结构背景,将中国干热岩资源的赋存类型分为高放射性产热型、沉积盆地型、近代火山型和强烈构造活动带型。并在此基础上研究了不同类型干热岩资源的成因机制,比较不同类型干热岩资源成因机制之间的差别,提出干热岩资源赋存的有利前景区。     

一种带输出谐振倍压的双电感隔离型Boost变换器

传统的燃料电池发电系统用DC/DC变换器拓扑主要是隔离型Boost变换器,其效率、增益和输入电流纹波都有一定瓶颈.为此,提出了一种新颖的带输出谐振倍压的双电感隔离型Boost变换器,变换器的输入侧采用双电感结构,输出侧采用谐振倍压结构实现了整流二极管的零电流关断.相比于传统的隔离型Boost变换器,所提出的拓扑的具有更小的输入电流纹波,同时变换器增益提高了1倍.给出了变换器的工作原理波形并进行了详细的模态分析,在此基础上完成了变换器的增益特性和输入电流纹波分析并给出了一种可行的变换器设计方法.最后研制了1台500 W的样机,满载效率为96.5%,样机实验结果验证了所提出拓扑的可行性和高效率功率变换的优点.     

全球地形影响大气和海洋经圈环流的耦合模式研究

利用气候系统模式(CESM1.0)研究陆地地形改变对大气?海洋经圈环流的影响。模式首先给出真实海陆分布及陆地地形情况下的大气?海洋气候态, 然后给出平板陆地情况下(陆地海拔均匀10 m)的气候态。与真实世界相比, 平板陆地情形下大气?海洋经圈环流发生重大改变: 首先, 年平均大气对流中心南移到赤道附近, 使得大气哈德雷环流相对于赤道对称; 其次, 海洋的经向翻转流变强, 大西洋经向翻转流完全消失, 取而代之的是在太平洋出现强大的经向翻转流及热盐环流。在平板陆地情形下, 北半球中高纬度大气抬升减弱, 向北的大气热量输送减少, 北半球温度降低, 大气对流中心因而向赤道迁移; 同时, 海洋向极地的热量输送也减弱, 中高纬度海洋变冷, 北太平洋海水密度增加很多, 北大西洋海水密度降低, 导致海洋经向翻转流从大西洋转移到太平洋。     

平翅片板翅换热器在混合热边界条件下的传热特性

采用数值模拟的方法研究了板翅式换热器平翅片在混合热边界条件下的传热特性,得到了雷诺数Re=400和Re=1 000的层流流动中,混合热边界条件下的翅片流道的局部努塞尔数和平均努塞尔数沿无量纲轴向距离的分布,并与相同雷诺数下等壁温和等热流边界条件结果进行对比.结果表明:混合热边界条件的平均努塞尔数比等壁温计算条件下平均努塞尔数高出3%~4%,比等热流计算条件下平均努塞尔数低26%~27%.因此在此类换热器传热性能设计时应采用等壁温条件的关联式.     

On-line spheroidization process of medium-carbon low-alloyed cold heading steel

Conventionally manufactured 35CrMo cold heading steel must undergo spheroidization annealing before the cold heading process. In this paper, different types of deformation processes with various controlled cooling periods were operated to achieve on-line spheroidal cementite using the Gleeble-3500 simulation technique. According to the measured dynamic ferrite transformation temperature (A_d3), the deformation could be divided into two types: low temperature deformation at 810 and 780℃; “deformation-induced ferrite transformation” (DIFT) deformation at 750 and 720℃. Compared with the low temperature deformation, the DIFT deformation followed by accelerated cooling to 680℃ is beneficial for the formation of spheroidal cementite. Samples subjected to both the low-temperature deformation and DIFT deformation can obtain granular bainite by accelerated cooling to 640℃; the latter may contribute to the formation of a fine dispersion of secondary constituents. Granular bainite can transform into globular pearlite rapidly during subcritical annealing, and the more the disperse phase, the more homogeneously distributed globular cementite can be obtained.     

河北省承德地区大地热流

地温监测孔长期地温监测资料显示,承德市地区恒温带深度是20m,恒温带温度是9.9℃。结合承德上板城镇CD-01地热地质勘探孔测温资料,本文利用恒温带温度、井底温度数据,通过回归分析方法,获取了钻孔真实地温分布信息。采集CD-01钻孔90块岩心样品,测试了岩石热物性参数。CD-01钻孔大地热流计算结果是46.4 mW/m2,高于早期承德地区大地热流研究成果（44.8 mW/m2和30.1 mW/m2）,但都低于我国大陆地区平均热流值（60.4±12.3 mW/m2）和全球大陆地区平均热流值（65.0±1.6 mW/m2）,为低热流值,反映了承德地区的低热流背景。     

低温等离子体改善义齿基托表面润湿性的研究

使用直流电激发4种工作气体(Ar, Ar/O₂, Ar/O₂/N₂和He/O₂)来产生等离子体, 分别处理热凝树脂样本1, 2, 4, 6, 8, 10分钟, 每组9个样本。使用接触角测量仪测量处理前后各样本的接触角; 利用发射光谱(OES)对等离子体的活性成分进行分析; 采用X射线光电子能谱(XPS)分析其表面的元素价键改变。经过Ar, Ar/O₂, Ar/O₂/N₂和He/O₂等离子体处理后, 热凝树脂表面的润湿性均显著增加, 处理 1 分钟时, 样本表面的接触角与原始值相比, 显著减小(p<0.001), 随着时间的延长, 减小趋势变缓。OES结果显示等离子体的活性成分中包含有大量的?OH; XPS分析表明: 经过等离子体处理后, 热凝树脂表面的C元素与O元素的比例减小, 有新的亲水性基团C?OH产生。大气压低温等离子体处理热凝树脂表面后, 产生新的亲水性基团C?OH, 从而增加表面亲水性。研究结果提示低温等离子体可能为临床上处理义齿基托树脂提供新方法。     

超导金属小粒子的电子比热研究

利用随机矩阵理论中能级统计的方法,考虑能级分布和能级关联的影响,给出适合于金属小粒子的自恰方程,并详细数值计算了无外场作用时超导金属小粒子s=0及s=1/2两个自旋态能隙参量和临界转变温度随金属小粒子粒径的变化规律,以及在不同粒径时的电子比热.并在自旋s=0时理论结果得到了实验上观察到的超导增强效应.