混联法生产氧化铝的熟料烧结问题探讨

采用贵州低品位铝土矿和溶出拜耳赤泥、碱、石灰配制的混合料烧结,在A/S=2.84±、[N]/[A]+[F]=0.97±、[C]/[S]=2.11±、t℃=1275±时,可以获得较好的效果。氧化铝标准溶出率η(?)标=94.64%,氧化铝工业溶出率=92.68%。     

真空碳热还原酸浸含钛高炉渣制备TiC分析

含钛高炉渣中含有20%~30%的TiO_2,是一种附加值较高的二次资源,但在综合利用过程中存在氧化物还原难度大,硅钛难分离,二次污染严重等问题。基于热力学理论基础,采用真空碳热还原联合酸浸工艺处理含钛高炉渣制备TiC。结果表明:真空有助于钛氧化物彻底还原,可实现渣中硅钛彻底分离,减少酸耗量,降低二次污染。真空碳热还原联合酸浸工艺处理含钛高炉渣(TiO_2含量23%左右)制备TiC的最佳条件为:炉渣粒度200目,还原温度1 673K,渣碳质量比100∶38。     

Reductive leaching of low-grade manganese ore with pre-processed cornstalk

Cornstalk is usually directly used as a reductant in reductive leaching manganese. However, low utilization of cornstalk makes low manganese dissolution ratio. In the research, pretreatment for cornstalk was proposed to improve manganese dissolution ratio. Cornstalk was preprocessed by a heated sulfuric acid solution (1.2 M of sulfuric acid concentration) for 10 min at 80°C. Thereafter, both the pretreated solu-tion and the residue were used as a reductant for manganese leaching. This method not only exhibited superior activity for hydrolyzing corn-stalk but also enhanced manganese dissolution. These effects were attributed to an increase in the amount of reductive sugars resulting from lignin hydrolysis. Through acid pretreatment for cornstalk, the manganese dissolution ratio was improved from 50.14%to 83.46%. The pre-sent work demonstrates for the first time the effective acid pretreatment of cornstalk to provide a cost-effective reductant for manganese leaching.     

液压及润滑管道循环酸洗、冲洗装置的研制与应用

在安装冶金轧钢设备的液压及润滑系统管道时,原工艺多是采用配管→安装→拆除→酸洗→安装→循环冲洗,现设计了将循环酸洗和冲洗装置合二为一的液压及润滑管道循环酸冲洗装置,提出了该装置的使用方法和配套措施,并用于马钢热轧薄板连铸连轧工程的液压及润滑管道施工,既减少了投资,又缩短了工期.     

高铟闪锌矿在氧压酸浸中铟浸出动力学的研究

铟是一种重要的多用途战略金属,具有较高的工业应用价值,但无独立可供开采的矿床,常伴生于铅锌等硫化矿中.因此,本文在传统电加热条件下进行了高铟闪锌矿氧压酸浸过程中铟浸出动力学实验的研究.结果表明:采用“有固态产物层的液-固相浸出反应动力学模型”对铟浸出动力学进行了研究,可知其浸出速率受到界面化学反应控制,其表观活化能为69.735kJ/mol,以及高铟闪锌矿氧压酸浸过程中铟浸出率随粒度减小、初始酸度增大、氧分压增大、浸出温度增大而增大.     

Alkaline pressure oxidative leaching of bismuth-rich and arsenic-rich lead anode slime

A new alkaline pressure oxidative leaching process(with NaNO3 as the oxidant and NaOH as the alkaline reagent)is proposed herein to remove arsenic,antimony,and lead from bismuth-rich and arsenic-rich lead anode slime for bismuth,gold,and silver enrichment.The effects of the temperature,liquid-to-solid ratio,leaching time,and reagent concentration on the leaching ratios of arsenic,antimony,and lead were investigated to identify the optimum leaching conditions.The experimental results under optimized conditions indicate that the average leaching ratios of arsenic,antimony and lead are 95.36%,79.98%,63.08%,respectively.X-ray diffraction analysis indicated that the leaching residue is composed of Bi,Bi2O3,Pb2Sb2O7,and trace amounts of NaSb(OH)6.Arsenic,antimony,and lead are thus separated from lead anode slime as Na3AsO4·10H2O and Pb2Sb2O7.Scanning electron microscopy and energy-dispersive spectrometry imaging revealed that the samples undergo appreciable changes in their surface morphology during leaching and that the majority of arsenic,lead,and antimony is removed.X-ray photoelectron spectroscopy was used to demonstrate the variation in the valence states of the arsenic,lead,and antimony.The Pb(IV)and Sb(V)content was found to increase substantially with the addition of NaNO3.     

搅拌磨超细粉磨金精矿工艺的优化

研究了搅拌磨超细粉磨金精矿的工艺,考察了主要参数对粉磨效果的影响.结果表明,通过优化磨矿过程中各种影响因素,可以获得细度-20μm＞99%的金精矿产品.     

微咸水淋洗改良对盐碱化旱田豇豆产量及性状影响

松嫩平原西部有苏打盐碱化土地面积373万hm2,其中除了盐碱化草地与碱斑地、盐碱湿地、低洼易涝盐碱地外,约有25%的盐碱低产旱田[1]由于尚无更有效的盐碱化旱田改良利用方法,目前只能种植耐盐碱性较强、耗地力、低效益的向日葵,轻度盐碱地虽能种植甜菜、高梁、糜子及玉米等,但是产量和效益均较低。为此,试验采用本地区20m~30m深具有较好渗透性的微咸水(矿化度1g/L~3g/L)进行豇豆田淋洗灌溉[2-5],进一步探讨微咸水淋洗灌溉对豇豆产量和相关性状的影响,以提供盐碱化旱田改良及高效利用的方法和依据。图1,表2,参5。     

Dissolution behavior and dissolution mechanism of palygorskite in HCl solution

The 1 mol/L, 3 mol/L and 5 mol/L HCl solutions were employed to leach two palygorskites with different trioctahedral contents in their crystal structure for different period of time. The results of the dissolution experiments show that the dissolution process could be divided into three steps, and that this dissolution behavior can be attributed to its higher Mg2+ content, and is restricted by the extraction behavior of Si4+. The preferential extraction for Mg2+ promotes the extraction behavior of Si4+ from Si-O framework. Because the Si4+ in the form of amorphous SiO2 is adsorbed onto the surface of palygorskite fibre, the reaction between palygorskite and acid is obstructed. With the elapsing of time, or the increasing of the acid concentration, the amorphous SiO2 flocculates, and then the channels of chemical reaction are reopened. The ratio value of Mg2+/(Fe3++Al3+) in leaching solution tends to a fixed value, showing that the acid attacks not only the surface but also the structural channels. There are no obvious three steps observed during the acid attack on the palygorskite with a lower trioctahedral content. The differential behavior for two palygorskites is discussed.