难浸金矿扩大试验研究

对黔西南州高砷高硫难浸金矿进行二段焙烧预处理，采用氧化剂强化氰金进行扩大试验研究。结果表明：该工艺使金的浸出率达到85％以上，该工艺投资省，无环境污染。     

Deep cleaning of a metallurgical zinc leaching residue and recovery of valuable metals

Huge quantities of zinc leaching residues (ZLRs) generated from zinc production are dumped continuously around the world and pose a potential environmental threat because of their considerable amounts of entrained heavy metals (mainly lead). Most ZLRs have not been properly treated and the valuable metals in them have not yet been effectively recovered. Herein, the deep cleaning of a ZLR and recovery of valuable metals via a hydrometallurgical route were investigated. The cleaning process consists of two essential stages:acid leaching followed by calcium chloride leaching. The optimum conditions for extracting zinc, copper, and indium by acid leaching were a sulfuric acid concentration of 200 g·L-1, a liquid/solid ratio of 4:1 (mL/g), a leaching time of 2 h, and a temperature of 90℃. For lead and silver extractions, the optimum conditions were a calcium chloride concentration of 400 g·L-1, a pH value of 1.0, a leaching time of 1 h, and a temperature of 30℃. After calcium chloride leaching, silver and lead were extracted out and the lead was finally recovered as electrolytic lead by electrowinning. The anglesite phase, which poses the greatest potential environmental hazard, was removed from the ZLR after deep cleaning, thus reducing the cost of environmental management of ZLRs. The treatment of chlorine and spent electrolyte generated in the process was discussed.     

水泥基复合固化剂对镉和锌混合污染土的固化试验研究

为了研究水泥基复合固化剂对重金属混合污染土的固化稳定效果及其与单一重金属污染土的固化效果差别,探究锌和镉离子之间是否有协同或拮抗作用,采用水泥、石灰、粉煤灰和蒙脱石等作为复合固化剂,通过开展无侧限抗压强度试验、毒性浸出试验、X射线衍射分析（XRD）以及电镜扫描分析（SEM）,研究锌镉混合污染土在不同固化剂掺量下的强度特性与浸出毒性、pH值与浸出毒性间的关系、重金属混合污染土与单一重金属污染土的固化效果差异,并通过XRD和SEM分别对固化产物的成分和形貌进行微观分析,进而分析固化机理。试验结果表明：用生石灰、粉煤灰、海泡石、蒙脱土替代等量水泥可使固化产物的强度提高;Zn²⁺与Cd²⁺之间不存在拮抗作用,Cd²⁺的存在还会有助于Zn²⁺的固定;重金属离子的浸出浓度随浸出液pH值的增大而明显降低;固化效果好的样品相较于固化效果差的样品有更多的针状、网状等较为致密的结构。     

单一及复合环境友好型淋洗剂修复铅污染土壤

为了探索一种针对重金属铅(Pb)的高效环境友好型淋洗剂,采用水平实验法探究了乙二胺四亚甲基膦酸(EDTMPA)、聚酰胺酸(PAA)、鼠李糖脂三种淋洗剂对Pb污染土壤的淋洗特征,使用响应面法对EDTMPA和PAA进行了淋洗参数优化.首次将这两种螯合剂EDTMPA,PAA与表面活性剂鼠李糖脂复合淋洗.结果表明,单独淋洗时,EDTMPA的效果最佳,最佳淋洗参数为质量分数2.3%,pH 5.7,淋洗时间167 min,对Pb的去除率为57.6%.鼠李糖脂复合EDTMPA对Pb的最大去除率为70.9%,比EDTMPA单独淋洗提高了12%;鼠李糖脂复合PAA的最大去除率为63.3%,比PAA单独淋洗提高了16%.鼠李糖脂复合EDTMPA是一种高效且环境友好型淋洗剂.     

不锈钢酸洗污泥中重金属的浸出试验研究

采用无机酸作为浸出剂对不锈钢酸洗污泥中的重金属进行浸出,在相同条件下,各种酸的浸出效率顺序为：硫酸 >盐酸 >硝酸.讨论了硫酸浸出酸洗污泥时浸出时间、硫酸浓度、液固比和温度等条件对金属浸出率的影响.结果表明,硫酸浓度和液固比对镍铬的浸出率有较大的影响,而温度的影响较小.在液固比为6：1、温度为30℃、硫酸浓度为3 mol/L以及浸出时间为90 min的条件下,污泥中镍、铬、铁和锰的浸出率分别为99.3%,99.2%,99.8%和93.2%,残余污泥中镍铬含量符合排放标准.     

双氧水还原浸出非洲氧化铜钴矿的试验研究

采用双氧水还原浸出非洲氧化铜钴矿,研究了还原剂用量、初始酸浓度、液固比、浸出温度和浸出时间等参数对浸出过程的影响。结果表明：使用双氧水与铜钴矿计量比为0.2 mL/g、浓硫酸与铜钴矿质量比为0.46、液固比为5：1（mL/g）,在温度75℃下浸出2 h,钴、铜的浸出率分别达到了99.50%,99.42%。     

贵州滥木厂废渣浸出液对隆线溞的生物毒性实验研究

本文通过对贵州溢木厂废渣进行不同酸雨条件下的浸取实验，用其浸出液对隆线溞进行急性生物毒性实验。实验结果表明：pH为5、5．5及6、6．5其96h对隆线溞的半致死体积分数LC50分别为3．4914％、2．3883％、1．5222％、2．0850％，说明此废渣浸出液有很强的生物毒性。     

含金矿物的氰化浸取动力学

筛选了一种能强化金浸取反应速率的添加剂——间硝基苯磺酸钠(MS),并进行了浸取反应过程的动力学研究。讨论了MS和氰化钠浓度、温度、搅拌强度及矿物粒度等因素对浸取反应的影响。MS通过改变阴极反应体系强化了金的氰化浸取反应速率,且对浸取液中氰化物无破坏作用。采用收缩未反应芯模型较好地描述了金的浸取过程,金浸取的动力学过程受扩散控制。同时导出了宏观动力学方程。用黄铁矿焙渣在串联式池浸装置中进行工业化模拟试验的结果表明,含MS的浸取液,浸取金含量仅为0.94g/t的矿渣,具有较力满意的结果。     

三相流态化浸出锑精炼渣的研究

本文对锑精炼渣进行了三相流态化浸出的小型及扩大试验研究,探讨了锑精炼渣水浸分离砷锑的控制环节。考察了锑精炼渣浆的流变特性,讨论了温度、粒度、时间液固比等因素对浸出过程的影响。小型及扩大试验均表明,在常温和液固比为2.0的条件下浸出30min,砷浸出率可达97%。三相流态化浸出可在低液固比下进行,能强化浸出过程,缩短浸出时间。     

硼铁矿提硼过程中硼的行为

用渣－金平衡方法研究硼铁矿选择性还原过程中硼在渣－金两相的分配。矿石中的硼大约１４％进入铁液中形成含硼１％左右的生铁，８６％进入渣中富集，使渣中Ｂ２Ｏ３品位提高５％－６％。在高压釜内进行富硼渣碳酸钠水溶液浸出，同时通入ＣＯ２气体，硼的浸出率与富硼渣的结构，浸出温度，粒度等因素有关。在合适的工艺条件下，富硼渣中８８％－９０％的硼形成硼酸钠而进入溶液中，上述提硼工艺过程硼的总收率可达８８％－９０％。