EG与APP协同阻燃硬质聚氨酯泡沫塑料燃烧及热降解机理研究

将可膨胀石墨（EG）与聚磷酸铵（APP）复合用于阻燃硬质聚氨酯泡沫（RPUF）,采用极限氧指数及锥形量热仪研究了EG/APP对RPUF燃烧性能的影响;通过扫描电镜、热失重分析及X射线光电子能谱表征了RPUF/EG/APP残炭的微观形貌、热降解行为及化学组成. 结果表明,添加质量分数20%、质量比为7:3的EG/APP阻燃RPUF的协同效果最好,氧指数可达36.0%,热释放速率最小,有一定的抑制产烟和CO释放的作用. 在阻燃RPUF燃烧过程中,EG热解残炭虽松散,但燃烧初期抑制烟气效果突出;APP残炭连续致密,但热稳定性不足,且易于生烟;而RPUF/EG/APP残炭隔热效果显著、抑制烟气效果较好. 其作用机理与多磷酸渗入EG残炭,增加了炭层的耐热性及炭层表面N/C、P/C元素摩尔比的增加有关.      

超临界乙醇制备TiO2/石墨烯纳米复合材料及其表征

以氧化石墨为载体、钛酸异丙酯为前驱体,利用超临界乙醇的超临界性能和还原性,制得了晶型完善的锐钛矿TiO2/石墨烯纳米复合材料.通过红外光谱（FTIR）、X射线光电子能谱（XPS）对采用Hummers法制得的氧化石墨（GO）进行表征;同时利用透射电子显微镜（TEM）、X射线衍射仪（XRD）对TiO2/石墨烯纳米复合材料进行研究.结果表明：成功制得了氧化石墨（GO）和晶型完善的锐钛矿TiO2/石墨烯纳米复合材料,并且发现二氧化钛在石墨烯纳米片层上呈现为有规则的颗粒,分散均匀,平均粒径为8.24 nm.     

石墨纤维表面与孔隙的结构表征及分形性质分析

 
为了研究和分析石墨纤维表面与孔隙的结构和分形性质,采用场发射扫描电子显微镜、电感耦合等离子体发射光谱仪、全自动物理吸附分析仪对其进行测试与表征.研究结果表明：石墨纤维以圆柱状存在,直径约为12～18μm,表面较光滑,缺陷较少,有利于气体吸附;石墨纤维碳的质量分数约为95.86%,还含有少量的N、H、O、S和微量的Ca、Fe、Mg、Si、Al等元素,生产过程中留下的孔道不多;石墨纤维的比表面积较大,其微孔体积占总孔体积的97.98%,平均孔径在微孔区域,且孔径分布较窄,包含大量0.84nm左右和少量1.21nm左右的微孔,较丰富的微孔结构使其具有良好的吸附性能;石墨纤维的表面与孔隙具有较好的分形特性,分形维数分别为2.11和2.99,是一种有工业前景的吸附材料.     

扇形内翅片石墨管层流强化传热性能

利用数值模拟方法对一种高黏度的油类介质在6种不同布置交错角度(0°,30°,45°,60°,75°,90°)的扇形内翅片石墨换热管中层流的强化传热和流动规律进行了研究.结果表明,扇形内翅片的强化换热效果明显.与无翅片的石墨换热管相比,6种布置角度的扇形内翅片对流换热系数分别增大22.69%,42.49%,62.28%,63.44%,65.47%,66.47%.就流动性能而言,扇形内翅片的石墨管6种布置角度下的阻力分别增大了191.88%,252.01%,333.10%,364.33%,385.51%,400.43%.为了明确石墨管内添加扇形内翅片后的强化传热效应,采用了换热性能评价指标(PEC)对6种布置角度进行了评价研究,结果显示45°布置角度时PEC评价准则数的平均值达到最大,为1.265,说明布置角度为45°时强化换热效果最理想.     

再生粗骨料对再生混凝土自生收缩的影响

在测试两种再生粗骨料特性及其再生混凝土基本性能的基础上,系统研究了不同再生粗骨料取代率、不同附着砂浆率的再生粗骨料对再生混凝土自生收缩的影响.结果表明:再生混凝土自生收缩的发展趋势和普通混凝土相似;随着再生粗骨料取代率增加,混凝土自生收缩增大;附着砂浆率大的再生粗骨料对混凝土自生收缩的影响更大;再生粗骨料对混凝土自生收缩的不利影响比对强度的不利影响更大.     

Formation mechanism of the graphite-rich protective layer in blast furnace hearths

A long campaign life of blast furnaces is heavily linked to the existence of a protective layer in their hearths. In this work, we conducted dissection studies and investigated damage in blast furnace hearths to estimate the formation mechanism of the protective layer. The results illustrate that a significant amount of graphite phase was trapped within the hearth protective layer. Furthermore, on the basis of the thermodynamic and kinetic calculations of the graphite precipitation process, a precipitation potential index related to the formation of the graphite-rich protective layer was proposed to characterize the formation ability of this layer. We determined that, under normal operating conditions, the precipitation of graphite phase from hot metal was thermodynamically possible. Among elements that exist in hot metal, C, Si, and P favor graphite precipitation, whereas Mn and Cr inhibit this process. Moreover, at the same hot-face temperature, an increase of carbon concentration in hot metal can shorten the precipitation time. Finally, the results suggest that measures such as reducing the hot-face temperature and increasing the degree of carbon saturation in hot metal are critically important to improve the precipitation potential index.     

迫击炮火力分配建模研究

高寒山地地形复杂、机动困难,迫击炮群将是未来高寒山地战场的重要火力。参战的迫击炮单位和类型比较复杂,不同的迫击炮群具有不同的毁伤效果。如何用最小的代价获得最佳的毁伤效果,是一种火力分配的优化问题。通过仿真迫击炮火力分配模型,模拟指挥员进行射击决策,为作战指挥理论提供了一种新的数学模型。     

基于集成神经网络的球墨铸铁珠光体含量涡流无损智能测定

为了实现球墨铸铁珠光体含量的智能无损测定,制备了具有代表性的球墨铸铁试样并按珠光体粗细程度将其分为三类。首先在分析了影响球墨铸铁电磁性能的主要因素的基础上,同时采用涡流无损检测法与金相法对球墨铸铁珠光体含量进行了测定,对检测数据进行回归分析表明二种方法的测量结果很接近;然后采用集成神经网络处理涡流检测数据并对珠光体含量进行了预测,预测结果表明基于集成神经网络数据处理的涡流检测是一种快速智能识别球墨铸铁中珠光体含量的有效方法。     

石墨渗铜喉衬材料的抗热震性能与烧蚀微观结构研究

对粗粒级高强石墨加压渗铜制备的石墨渗铜喉衬材料的微观结构与抗热震性能的关系进行了研究,结果表明渗铜提高了原石墨的导热系数及整体增韧的综合效果。对热试车后的石墨渗铜喉衬进行烧蚀微观结构及能谱分析研究,得到了铜的分布情况与烧蚀性能的关系。     

水淬铜渣的火山灰活性

就水淬铜渣的火山灰活性进行试验研究,并利用比强度等指标对试验结果进行了系统分析．结果表明,经加工的水淬铜渣具有明显的火山灰活性,可用作水泥或混凝土的矿物掺合料．