氯氧镁凝胶/聚丙烯酸酯复合材料弯曲性能的研究

研究了氯氧镁凝胶／聚丙烯酸酯复合材料配方各组分对弯曲性能的影响。实验结果表明，复合材料的弯曲性能在砂料质量分数为40％时达到最大，砂料质量分数过高则反而下降。粒径小的砂料具有更好的增强效果。砂料质量分数为40％时，20目级的MOC／PAR复合材料的弯曲强度的增加量达到44．3％，弯曲模量的增加量达到79，8％；40目级的MOC／PAR复合材料的弯曲强度的增加量达到75．4％，其弯曲模量的增加量达到109．7％。     

Construct hepatic analog by cell-matrix controlled assembly technology

Living donor liver transplantation has been widely performed since 1989[1]. Unfortunately, the demand for donor livers far outstrips the supply. The severe short- age of donor livers continues to grow, thereby stimu- lating people to develop alternate eff…     

两种酶水解明胶的条件筛选及评价

对中性蛋白酶和胰蛋白酶样品进行了以明胶为底物的酶解反应试验,并对两种酶的水解能力进行了比较,确定了两种酶的反应温度、pH值、底物浓度、加酶量以及酶解时间等条件.     

APS-U 引发丙烯酸丁酯与明胶接枝共聚(Ⅲ)

采用过硫酸铵－尿素新氧化还原体系研究了丙烯酸丁酯与明胶的接枝共聚，分析了共聚参数对接枝率、接枝效率、总转化率的影响，讨论了此体系下的接枝共聚机理。     

明胶的干燥温度,粘度和分子量分布

通过实验探讨明胶干燥温度对明胶粘度的影响，并从分子量分布和数均分子量变化的角度阐明这种影响的内在原因．实验结果表明：经室温干燥的活性胶、惰胶、复合胶和食用胶再经１０５℃干燥与只经室温干燥相比，其粘度上升；经室温干燥的ＰＡ胶再经１０５℃干燥与只经室温干燥相比，粘度下降．明胶经室温干燥后再经１０５℃干燥，随着干保温度的提高，明胶的分子量分布和数均分子量发生变化，导致宏观上明胶粘度的变化．活性胶、惰胶、复合胶和食用胶经１０５℃干燥后分子量分布向分子量大的方向变化，数均分子量变大；而ＰＡ胶经１０５℃干燥后，分子量分布向分子量小的方向变化，数均分子量变小．     

^60Coγ射线辐照明胶的研究

~(60)Coγ射线辐照明胶是解决其细菌污染和粘度下降问题的有效方法。试验结果表明,适宜辐照剂量范围为3—5KGy,生产应用一般可控制在3.5KGy。在适宜剂量范围内,对其营养成分无不良影响,18种氨基酸总量比未辐照的对照微增。九十天动物喂养试验证明,对生长发育无不良影响,并有促进作用。血液化验、内脏器官观察和病理检验结果,均无异常改变。微核、染色体致畸、Ames试验均呈阴性。生产应用证明,经辐射可有效地提高产品质量和档次,社会、经济效益十分显著。     

明胶水溶液静电纺丝成形研究

以水为溶剂制备明胶溶液进行静电纺丝,在60 ℃～65 ℃纺得明胶超细纤维,探讨了溶液质量分数、静电电压及纤网收集距离等因素对明胶/水溶液体系静电纺丝成形的影响。结果表明,在60 ℃及65 ℃时,明胶溶液的黏度随其质量分数的增加而大幅上升,呈2次指数关系;随着明胶溶液质量分数的降低（从25%降到15%）,所得纤维平均直径减少（从266.5 nm降为167.7 nm）;随着静电纺丝电压升高,纤维直径下降,当电压大于17 kV以后其变化趋于平缓;改变静电纺丝收集距离,从11 cm到21cm,电纺所得的纤维直径为165～210 nm,变化幅度不大。     

生物可降解明胶微球的制备及体外降解

以生物可降解明胶为载体, 采用乳化交联法制备明胶微球, 考察了固化剂加入时间对微球质量的影响, 并通过正交实验研究了明胶溶液的浓度、 搅拌速度、 水油相比例对微球粒径的影响. 结果表明, 所制备的明胶微球, 具有粒径均一、 成球率高的特点, 微球表面平滑, 平均粒径为13.72 μm.     

Fabrication of PEI-Liposome Loaded Fish Gelatin Nanofibers Mats by Green Electrospinning

Polyethyleneimine （PEI） and cationic liposomes were widely used for gent delivery and the combination of PEI and liposome was reported to result in a higher efficiency of cell transfection in vitro. In recent years, better transfection was observed for the drug-loaded iiposome fixed on the tissue engineering scaffolds via embedding, surface adsorption or covalent grafting thus protected and bound by the scaffolds. In the present study, a novel PEI-liposome loaded fish gdatin composite nanofiber was successfully fabricated by a green electrosplnning process. The existence of PEI- liposome in the composite nanofibers was determined by Fourier transform infrared （ FTIR ） spectra, transmission electron microscopy （TEM）, and confoeal laser scanning microscopy （CLSM）. As shown by scanning electron microscopy （SEM）, the dectrospun composite nanofibers with uniform diameter were smooth and round, and the morphology of the fish gelatin fibers did not change significantly after the incorporation of PEI-liposomes. The transfection results in vitro suggest PEI-liposome loaded fish gelatin material may have a promising application in non-viral gene delivery systems.     