稀土硫酸盐对Na_2Mo_(0.1)S_(0.9)O_4离子导电性的影响

为了开发用于SO_2气体传感器的固体电解质材料。对掺杂稀土硫酸盐的Na_2Mo_(0.1)S_(0.9)O_4体系的离子导电性和相关系进行了研究,取得了良好的结果;在掺有4m/oPr_2(SO_4)_3的体系中,280℃时电导率达到10~(-3)Ω~(-1)cm~(-1);差热分析表明,没有相变发生,成功地将Na_2Mo_(0.1)S_(0.9)O_4的高温快离子导电相稳定到了室温。     

掺杂对锰氧化物La_(0.67)Ca_(0.33)Mn_(0.9)A_(0.1)O_3(A:Cr,Co,Fe,Cu)结构的影响

采用固相反应法制备了La0.67Ca0.33Mn0.9A0.1O3(A:Cr,CoFe,Cu)系列样品;利用X射线衍射(XRD)和扫描电镜(SEM)对系列样品进行了表征,结果表明:样品单相性很好;以元素Cr,Fe,Co替代时,样品呈现较均匀的颗粒,而元素Cu替代时样品呈大片状结构,空洞半径按替代元素Cr,Co,Fe,Cu的顺序逐渐变大,说明替代元素与Mn离子的半径之差Δ是影响样品空洞半径及缺陷的重要因素.     

Improving the Characteristic of the LaFeO_3 Alcohol Gas Sensor by Using Doping and Surface-Decorating Technique

采用掺杂和表面修饰技术制备ＬａＦｅＯ３乙醇气体传感器，明显地改善了传感器的特性．元件的灵敏度β≥１０（当乙醇气体浓度为２００×１０－６时），乙醇气体和汽油的分离度α为１４．３，在整个相对湿度变化范围内，元件阻值的相对变化在４％～６％之间，元件不通电存放７ｄ，其初期恢复时间为７０ｓ，不通电贮存２７０ｄ，其初期稳定时间小于３ｄ，在使用环境中连续工作９０ｄ其阻值相对变化率小于５％．     

晶体硅光伏电池的材料优化

介绍了调制阳光频率实现太阳光波上下量子剪裁的两种方式:掺杂稀土离子和微纳米结构化硅基材料.以Lu2O3为基质,采用共沉淀法制备了Tb3+和Yb3+共掺的下转换粉末;以NaYF4为基质,采用热水法制备了Er、Yb和Tm共掺的上转换粉末.实验证明Lu2O3:Tb3+,Yb3+纳米粉末中,一个高能光子可剪裁成2个974 nm的近红外光子.而NaYF4:Er3+,Yb3+,Tm3+共掺的上转换材料也有显著的上转换效果,仅用1 122 nm激光照射0.25 cm2实验硅光电池片可增加电池光电流密度0.06 mA/cm2.设计了具有纳米结构的PIN.简述了通过梯度掺杂制结增强光伏效应的原因.     

0.95K0.47Na0.47Li0.06NbO3—0．05Ba（Zr1-xTix）O3陶瓷的压电铁电性能与微结构

采用传统陶瓷制备技术制备了新型的0.95K0.47Na0.47Li0.06NbO3-0．05Ba（Zr1-xTix）O3体系无铅压电陶瓷,研究了该体系陶瓷的压电性能和微结构．研究结果表明,在1120℃、4h的烧结条件下,获得了致密性良好的陶瓷样品,并在x为0．95时性能达到最佳,其压电常数d33为133pC／N,机电耦合系数kp为0．34,机械品质因素Qm为148,介电常数εr为1138,介质损耗tanδ为0．017．     

GaAs/AlAs异型异质结导带研究

利用泊松方程分析了异质结导带形状，通过数值模拟研究了GaAs/AlAs异型异质结在不同掺杂浓度下的导带图，确定了导带尖峰出现的位置和耗尽区宽度。     

Synthesis and optical properties of turquoise- and green-colored brownmillerite- type Ba2In2-x-yMnxAlyO5+x codoped with manganese and aluminum

Brownmillerite-type oxides Ba₂In_2-x-yMn_xAl_yO_5+x (0 ≤ x ≤ 0.6, 0 ≤ y ≤ 0.5) were prepared at 1300°C through solid-state reaction. X-ray diffraction (XRD) analysis showed that the structure symmetry evolved from orthorhombic to cubic with increasing Mn and Al contents. When y was greater than 0.3, peaks associated with small amounts of BaAl₂O₄ and Ba₂InAlO₅ impurities were observed in the XRD patterns. When substituted with a small amount of Mn (x ≤ 0.3), the Ba₂In_2-x-yMn_xAl_yO_5+x samples exhibited an intense turquoise color. The color changed to green and dark-green with increasing Mn concentration. UV–vis absorbance spectra revealed that the color changed only slightly upon Al doping. The valence state of Mn ions in Ba₂In_2-x-yMn_xAl_yO_5+x was confirmed to be +5 on the basis of X-ray photoelectron spectroscopic analysis. According to this analysis, the intense turquoise color of the Ba₂In_2-x-yMn_xAl_yO_5+x samples is rooted in the existence of Mn5+; thus, the introduction of Al does not affect the optical properties of the compounds.     

制备方法对Ti0.8Zr0.2O2/沸石结构及光催化性能的影响

以酸处理后的信阳上天梯天然斜发沸石作为载体,分别采用浸渍法和溶胶凝胶法制备Ti0.8Zr0.2O2/沸石光催化剂.采用X-射线衍射、红外光谱和扫描电镜分析样品的微观结构和形貌.结果表明,80℃下,4 mol/L盐酸处理10 h后沸石结构发生了显著变化,Al—O—Si骨架结构保持.扫描电镜证明钛锆氧化物在溶胶凝胶法制备的光催化剂上高度分散,以罗丹明B(RhB)为模型污染物考察了该样品的吸附与光催化效果.300 W紫外灯光照1.5 h后,0.2 g该催化剂可使20 mL浓度为80 mg/L RhB溶液的去除率达97.12%,重复使用8次后去除率为89.47%.     

金属碳纳米管多原子掺杂硼氮的输运特性

文章建立了(6,6)碳纳米管模型,并对其掺杂B/N对、B/N3(3个N围绕着1个B)、N/B3(3个B围绕着1个N)3种不同原子团,采用非平衡格林函数法计算了该模型在不同掺杂情况下的透射率谱线及体系总能。发现在多原子掺杂的情况下,电子的透射谱和杂质中的硼氮含量有关,若硼含量较多,则透射谱与单独掺杂硼原子的类似,在费米能级以下有一个透射谷,相应的电子透射率几乎抑制为0;若氮含量较多,在费米能级上方有透射谷,情形与前者相类似。特别地,在对位掺杂B/N3和N/B3时,透射谱线在费米能级两侧一定范围内出现较宽规整的凹陷,在凹陷处的透射率几乎为0。     

The effects of N, F and S doping on electronic structures and optical Properties of TiO2

基于第一性原理的计算方法研究了掺杂N,F,S的锐钛矿相TiO2的晶体结构、电子结构及光学性质。计算结果表明掺杂后晶格发生了变化,同时导带位置下移导致了TiO2的禁带宽度变小。S掺杂使TiO2在紫外光区和可见光区有更强的光吸收特性。