Preparation of PVDF/TiO_2 Electrospun Membranes and its Application as Separators for Lithium-ion Batteries

1 Results Microporous PVDF-based membranes could be used as polymer matrix due to its good ionic conductivity and high electrochemical stability in the organic electrolyte[1,2].Fig.1 SEM image of PVDF/TiO2 membraneIt was reported that the ionic conductivity of microporous PVDF-based membranes could be improved by filling with Al2O3 nanoparticles[3].In this paper,electrospinning was employed to prepare microporous PVDF/TiO2 membranes and tetrabutyl titanate was used as original source of TiO2 to improve...     

固含率·三相流化床流体动力学性质的影响因素

描述了载体对内循环三相流化床流体动力学性质的影响，随着载体的加入量增大，气含率（εg), 氧传递系数（Ka），循环时间（Tm)和混合时间（Tc)均有减小的趋势，同时，实验证明还发现气流量对流化床内载体的分布情况影响不大，在分析了固含率对流体动力学性质的影响之后，得出固含率的最佳值为3％－10％之间。     

翅片管热疲劳试验及接触热阻测定

介绍了所建立的以高温导热油为载体的接触热阻试验台，热疲劳的最高温度呆达２８２℃，提出了接近工业操作工况的管内用高温导热油加热，管外在吸风式风洞中冷却的管束整体热疲劳方法及热疲劳试验条件与接触热阻测定条件分开的方法，对国内近年来研制成功的整体轧制双金属翅片管进行了不同极限温度的热疲劳试验，测定了管束平均接触热阻。     

温度循环条件下镀锡引脚的晶须生长

在热循环条件下,对电镀纯Sn覆层的器件引脚的锡须生长进行了评估.当器件经历500与1 000次温度循环后,纯Sn镀层表面会产生致密的热疲劳裂纹,伴随生长出许多锡须.由于镀层表面的SnO2氧化膜与镀层中Sn的热膨胀系数(CTE)存在较大的差异,在温度循环条件下发生SnO2与Sn的热失配,进而在其界面处产生了极大的交变应力,最终导致SnO2氧化膜破裂,为锡须生长提供了条件.此外,在Sn镀层与Cu基板界面处形成的Sn-Cu金属间化合物(IMC),提供了锡须生长的驱动力.镀层中的Sn原子在压应力的驱动下,沿着氧化物表面裂纹位置挤出,从而释放了压应力形成锡须.在锡须生长的初始阶段,阻力较大,故而速率较慢,在锡须突破表面氧化物层后,阻力较小,故加速了锡须的生长.     

热处理对NiAlMn高温形状记忆合金相变行为的影响

研究了热处理和热循环Ni－Al－30Mn高温形状记忆合金相变行为的影响。结果表明：（1）在600－1100℃固溶淬火时，随固溶温度升高，该合金的马氏体相变温度升高；在1000℃固溶淬火后，马氏体相变开始温度和马氏体逆相变结束温度为分别为465℃和549℃，（2）在1000℃固溶处理处理和400℃时效处理后，该合金可获得良好的相变特性；热循环使相变行为的稳定性提高。（3）该合金的淬火组织由马氏体和γ相组成，其中马氏体的体积约占60％，马氏体的硬度高于γ相，时效处理后合金的相组成未变，硬度有所增加。     

中-低温循环对2A14铝合金力学及疲劳性能的影响

国内对航天用2A14铝合金在中-低温循环条件下力学及疲劳性能的变化规律研究不足,为掌握该材料在上述工况下的力学表现及疲劳损伤情况,对2A14铝合金开展了室温—低温（-196 ℃×4 h）—室温,室温—中温（150 ℃/180 ℃×0.5 h）—室温两种工况循环条件下的力学、疲劳性能及组织变化规律研究。结果表明,在上述两种工况下循环5次,2A14铝合金的晶粒尺寸、粗大相形貌及分布均无显著变化,仍保持高强度及良好的塑韧性;随着应力幅值的降低,2A14铝合金的疲劳寿命逐渐延长;应力比为-1时,2A14铝合金的疲劳极限为150～175 MPa,上述两种工况下循环5次,不会改变2A14铝合金的韧性断裂机制。     

酶酸结合法降解植物纤维素新工艺

以麦秸为材料,研究乙酸、盐酸等对纤维素酶降解纤维素的影响;设计出降解纤维素的2个工艺方案:方案1是先酸解后酶解;方案2是先酶解后酸解。在这2种工艺方案基础上,研究一种酶酸循环降解法(CDCA法)。研究结果表明:方案2优于方案1;CDCA法亦明显优于方案1和方案2;以CH3COOH,HCl和纤维素酶为降解剂,在常压、温度低于100℃、反应12～15 h的条件下,CDCA法能使纤维素转化成葡萄糖的转化率达98.68%,反应终液中葡萄糖质量分数达5.38%;与常规技术相比,CDCA法只需25%的醋酸、50%的盐酸和少量的酶,可以大幅度地降低纤维素转化成葡萄糖的成本;本研究的酶酸结合法降解纤维素新工艺具有条件温和、工艺简单、成本低和周期短等特点,该工艺方法可为发酵工业上以纤维素为原料从事乙醇、抗生素、SCP等产品的开发生产及环保上固态生活垃圾的生物处理提供科学依据。     

SrF2颗粒涂覆增强Si/C负极电化学性能

The silicon-based material exhibits a high theoretical specific capacity and is one of the best anode for the next generation of advanced lithium-ion batteries (LIBs). However, it is difficult for the silicon-based anode to form a stable solid-state interphase (SEI) during Li alloy/de-alloy process due to the large volume change (up to 300%) between silicon and Li_4.4Si, which seriously limits the cycle life of the LIBs. Herein, we use strontium fluoride (SrF₂) particle to coat the silicon?carbon (Si/C) electrode (SrF₂@Si/C) to help forming a stable and high mechanical strength SEI by spontaneously embedding the SrF₂ particle into SEI. Meanwhile the formed SEI can inhibit the volume expansion of the silicon?carbon anode during the cycle. The electrochemical test results show that the cycle performance and the ionic conductivity of the SrF₂@Si/C anode has been significantly improved. The X-ray photoelectron spectroscopy (XPS) analysis reveals that there are fewer electrolyte decomposition products formed on the surface of the SrF₂@Si/C anode. This study provides a facile approach to overcome the problems of Si/C electrode during the electrochemical cycling, which will be beneficial to the industrial application of silicon-based anode materials.     

自行车骑行过程中频率及生理节律对下肢肌电的影响研究

通过在不同生理节律下改变踏蹬频率的骑行实验,获得了如下结论:①臀大肌、股二头肌在早晨的肌电爆发点比下午早,腓肠肌在早晨的肌电爆发点比下午晚,而胫骨前肌、股直肌的肌电爆发点与频率有关;股二头肌下午的肌电结束点比早晨早;股直肌及股二头肌的放电区间下午比早晨短.②频率增加引起臀大肌、股直肌、股二头肌、股外肌肌电爆发点、结束点近似同步前移,但频率增加却引起胫骨前肌爆发点前移而结束点延迟.③臀大肌、股外肌、胫骨前肌、腓肠肌放电区域随频率的增加而发生显著波动,当频率处于80～90 r/min之间时,其放电区域较短,超出这个范围,则显著延长.     

焊接热循环参数对大线能量焊接用钢EH40热影响区组织和性能的影响

利用热模拟技术及光学显微镜、透射电镜研究了焊接热循环参数对大线能量焊接用船板钢热影响区组织和性能的影响.发现模拟焊接热影响区组织主要由粒状贝氏体、铁素体和珠光体组成,且随着峰值温度和冷却时间的变化,热影响区的组织发生较大的变化;热影响区的冲击韧性总体水平较高,均在200 J以上,冲击韧性并不随着峰值温度和冷却时间的增加而单调变化;热影响区M-A岛的数量、尺寸、分布和形态影响热影响区的韧性.