AlN／CrN纳米多层膜的制备及性能的研究

采用多弧离子镀技术制备A1N／CrN纳米多层膜,研究了多层膜调制周期对A1N生长结构的影响以及纳米多层膜的机械性能．结果表明：在小调制周期下A1N会以立方结构存在,并与CrN层形成同结构共格外延生长,使纳米多层膜产生较大的晶格畸变;A1N／CrN纳米多层膜硬度和弹性模量随着调制周期的减小呈现上升的趋势,当调制周期小于8nm时其增速明显增大,并在调制周期为3．8nm时达到最高硬度35．0GPa和最高弹性模量405GPaA1N／crN纳米多层膜的硬度和弹性模量在小调制周期时的升高与c-A1N的产生并和CrN形成的共格结构有关．     

微弧氧化生物活性TiO2基纳米结构表面磷灰石诱导能力与药物上载及释放简

钛因优异的力学性能及良好的生物相容性而被用于代骨生物材料,但其生物惰性限制了它的进一步应用。对钛表面进行微弧氧化-水热改性处理生成复合涂层,可以有效提高钛材的生物活性。本文以Ca（H2 PO4）2＋Ca（CH3 COO）2＋EDTA-2Na＋NaOH为电解液,在纯钛表面制备TiO2基含钙磷微弧氧化涂层（CP）,再经后续水热处理改性,得到具有纳米结构的复合改性涂层;通过模拟体液浸泡实验,以研究不同表面结构复合涂层的磷灰石诱导能力。采用X射线衍射、扫描电子显微镜、X射线光电子谱和傅里叶变换红外光谱手段对试样进行详细分析。结果表明,经过水热处理的微弧氧化涂层较CP涂层表现出更好的生物活性,微弧氧化-水热涂层在模拟体液中浸泡3d均能在涂层表面长满磷灰石。此外,为解决植入体导致的炎症问题,进一步分析了涂层表面上载抗生素药物及其缓释机制。     

食品接触材料中含氟涂料的安全性问题研究

概述食品接触材料中含氟涂料的安全性现状,针对含氟涂料中的全氟化合物的危害所涉及的国内外对其相关的法律法规及检测方法进行介绍,对今后的含氟涂料发展方向提出了建议.     

Al含量对TiAlN涂层热稳定性能的影响

采用阴极电弧蒸镀在WC-Co硬质合金基体上沉积Ti1-xAlxN涂层(x=0.5、0.55和0.6),并对涂层试样在900℃下真空退火0.5～4 h.采用X线衍射仪(XRD)和显微维氏硬度计分析比较退火前后TiAlN涂层物相及硬度,研究Al含量对涂层结构、硬度和热稳定性能的影响.研究结果表明:Ti0.5Al0.5N和Ti0.45Al0.55N为单相面心立方结构,Ti0.4Al0.6N为面心立方(fcc)TiAlN和密排六方(hcp)AlN双相结构.涂层退火时发生分解,先析出介稳相fcc-AlN,再转变为稳定相hcp-AlN和fcc-TiN,硬度逐渐下降.Ti0.45Al0.55N涂层高温下能保持较长时间的稳定,退火后仍具有最高的硬度,表现出优异的热稳定性;而Ti0.4Al0.6N涂层中因存在hcp-AlN硬度略低,分解最早,热稳定性最差.当x=0.55时为最佳涂层成分.     

Si掺杂TiSiN涂层的结构特征及力学性能

通过射频磁控溅射在单晶硅(111)和硬质合金衬底上制备Si掺杂的TiSiN纳米复合涂层。采用双靶溅射技术,保持Ti靶功率不变,改变Si靶的功率以获得Si含量不同的TiSiN纳米复合涂层。用X射线衍射仪(XRD)、扫描电子显微镜(SEM)和显微硬度计表征TiSiN涂层的结构、成分、形貌和硬度。研究结果表明,Si靶溅射功率对TiSiN涂层的结构和力学性能影响较大。随着Si靶溅射功率的增加,TiN晶粒特征峰由(111)向(200)转变,在20 W的Si靶溅射功率下(111)面取向最优。涂层厚度随着功率的增大呈现先增大后减小的趋势。Si以非晶相Si_3N_4的形式存在;随着Si含量的增加表面晶粒得到细化,在20 W的Si靶溅射功率下,涂层晶体生长致密光滑,涂层硬度高达2 600 HV。     

稀土Sm_2O_3对Mo_2NiB_2基金属陶瓷微观组织和力学性能的影响

以NiB、Mo、Cr、V、Ni等几种粉末为基本原料,并以稀土Sm_2O_3为添加剂,采用真空液相烧结法制备Mo_2NiB_2基金属陶瓷。利用XRD、SEM、EDS、洛氏硬度计和电子万能试验机等研究添加Sm_2O_3对Mo_2NiB_2基金属陶瓷微观组织和力学性能的影响。结果表明,添加0.3%~0.9%的Sm_2O_3后,金属陶瓷晶粒明显细化,组织分布更加均匀,材料的硬度和抗弯强度也得到提高。当Sm_2O_3添加量为0.6%时,所得试样的晶粒最为细小,晶粒尺寸大致在0.8~3.0μm,材料的力学性能最佳,其硬度和抗弯强度分别达到HRA88.7和1550 MPa。     

Studies on thermally grown oxide as an interface between plasma-sprayed coatings and a nickel-based superalloy substrate

A thermally grown oxide layer formed by hot corrosion was investigated as an interface between plasma-sprayed coatings and a nickel-based superalloy substrate. The hot corrosion mechanism of NiCr-Cr₂O₃ and Al₂O₃-40wt% TiO₂ (A40T) plasma coated Inconel 617 was evaluated. The experiments were carried out at 1000℃ using a combination of Na₂SO₄, NaCl, and ₂O₅ salts to simulate the conditions of a gas turbine in a marine environment. The hot corrosion results revealed the spallation and dissolution of oxides upon prolonged exposure. Optical images and scanning electron micrographs of the exposed samples revealed the formation of oxide scale and provided details of its morphology in NiCr-Cr₂O₃ coated samples. Microstructure characterization of A40T coatings demonstrated a thermally grown oxide (TGO) layer at 1000℃. Increasing the thickness of the TGO layer decreased the corrosion resistance. The elemental analysis and image mapping revealed the migration of active elements from the substrate and coatings toward the corrosive environment.     

金属陶瓷惰性阳极铝电解扩大实验研究

用新研制的铝电解金属陶瓷材料做铝电解阳极,在摩尔分子比为2 8、饱和氧化铝浓度的冰晶石系电解质中进行100A电流电解实验,电解温度为960℃,阳极电流密度为1 0A/cm2·实验结果表明,该金属陶瓷阳极具有优良抗热震性的同时显示出优良的抗氧化耐冰晶石熔盐腐蚀性能,阳极年腐蚀速率为24mm/a,阴极铝的质量达到98%·使用铝参比电极测得在960℃下该阳极的反电动势为2 2V·经奥氏气体分析仪检测表明,释放出的阳极气体中氧气的含量为98%～100%·     

碳纳米管的制备及其在纳米复合镀层中的应用研究

利用化学气相沉积法制备碳纳米管(carbonnanotubes,CNTs),分析了气源、催化剂及温度等因素对CNTs形貌和纯度的影响.利用化学复合镀技术制备了Ni P CNTs纳米复合镀层,并研究了镀层的摩擦性质及电化学性质.研究结果表明:与Ni P镀层相比,Ni P CNTs纳米复合镀层的耐磨性及耐腐蚀性均有较大程度的提高.     

粘结层中的Co对热障涂层界面结合因子的影响

用固体与分子经验电子理论(EET)和改进的TFD理论的结合,计算了热障涂层不同粘结层Co含量下的陶瓷层/粘结层界面的界面结合因子,结果表明:含Co界面的最小电子密度差Δρmin比不含Co时小,Co有利于缓解界面的应力;加Co后使该界面电子密度保持连续的原子状态组数σ′比不加Co至少增加一个数量级,Co有利于使界面稳定,且从σ_equal和σ_super可知这种稳定性不会由于应力的升高受到破坏;当粘结层的表面为(110)时,加Co后电子密度ρ总是提高,有利于提高界面的结合力;当粘结层的表面为(100)和 (111)时,界面的结合力不受Co含量影响。所以,Ni基粘结层中的Co可改善热障涂层的陶瓷层/粘结层的界面结合。