卷取后冷却速度对高强度热轧带钢组织的影响

采用拉伸实验、电镜观察、能谱分析和硬度测试等方法,研究了700MPa级高强度钢热轧钢卷组织性能分布不均的特点,对造成其组织性能不均的原因进行了分析. 结果表明,钢卷纵向力学性能分布不均,分布规律为成卷后钢卷的中部>内部>外部,内部和外部相差不大. 沿钢卷纵向,中部试样和外部试样的金相组织、碳氮化物析出状态均存在着明显差异,这是造成钢卷力学性能不均的主要原因. 卷取后的冷却速度对金相组织、碳氮化物析出状态有着重要影响.     

机械激活辅助熔盐法制备碳氮化钛研究

文章以氯化铵为氮源,采用机械激活辅助熔盐法制备碳氮化钛,研究结果表明,反应温度的升高和球磨激活时间的延长,均有助于减少副产物含量。所得TiC0.7N0.3颗粒尺寸在0.5μm-2μm之间。同传统固态合成法相比,采用该方法合成TiC0.7N0.3粉体的反应温度大幅降低,反应时间也大幅缩短。     

X80管线钢中氮化物和碳化物析出热力学分析

基于规则熔体理论和平衡反应基础,对连铸工序X80管线钢中碳化物、氮化物析出进行热力学分析,研究Ti、Nb及Al的碳化物、氮化物析出规律。结果表明,固液两相区,TiC0.005N0.995和TiN分别在1785K和1784K时开始析出;奥氏体相区,碳化物、氮化物析出先后顺序为NbC0.64N0.36、NbC、NbN、AlN、TiC,相应析出温度为1457、1404、1354、1267、1226K;γ→α相变过程中,TiC发生相间析出,Nb主要以NbC形式析出,AlN析出量较少。     

不同强度级别帘线钢中Ti(C_xN_(1-x))夹杂分析

在真空感应炉中熔炼出3种Ti、N含量相近但强度级别不同的帘线钢钢锭,研究钢液凝固过程中析出碳氮化钛(Ti(CxN1-x))夹杂的尺寸分布特点及其连续固溶体中TiC所占比例与钢中碳含量之间的关系。结果表明,帘线钢在凝固过程中的固液两相区温度随钢液碳含量的升高而降低,可使Ti(CxN1-x)夹杂析出的过饱和度增大,有利于其在钢液凝固过程中析出与长大。随着帘线钢强度级别的提高,钢样中尺寸大于4μm的钛夹杂的比例增加,其平均尺寸也相应增大;72A亚共析帘线钢中未检测到5μm以上的钛夹杂,而82A、92A过共析帘线钢中尺寸大于5μm的钛夹杂析出比例分别达到4.92%和9.52%;钢液凝固过程中析出的Ti(CxN1-x)夹杂中TiC所占比例也随帘线钢强度级别提高而增大。     

TiO2碳热还原与高炉钛渣提取碳氮化钛分析

总结TiO2的碳热还原法制取碳(氮)化钛的研究成果,并对高炉钛渣中钙钛矿的碳热还原进行了热力学分析。研究结果表明,TiO2的碳热还原可分为三个阶段:TiO2→TinO2n-1,该阶段还原较快;TinO2n-1→TiCxNzOy,该阶段碳的气化反应起中心作用;TiCxNzOy→Ti(C,N)是一个较慢的扩散过程。TiO2的碳热还原氮化反应中难以出现TiO相;N2气的引入,可降低还原温度。通过调整高炉钛渣组成(包括碱度),使之生成CaO.Al2O3.2SiO2,更有利于碳(氮)化钛的生成。     

TiC、TiN、Ti（C、N）粉末制备技术的现状及发展

综述了国内外近年来TiC、TiN、Ti(C、N）粉末的制备技术，分析了这些制备技术的工艺过程和工艺特点，讨论了存在的问题和发展趋势，寻求成本低廉的原材料，利用等离子、微波、激光、电弧等获得高温的新技术，并结合自蔓延合成、机械合金化等手段，低成本规模化制备高质量TiC、TiN、Ti（C、N）超细粉体正成为国内外关注的热点。随着研究深入和制备工艺的改进发展，更简便、经济、有效的制备技术将使TiC、TiN、Ti（C、N）粉末具有更广阔的工业应用前景。     

放电等离子烧结及热处理制备的Fe/316L/430–Ti(C,N)复合材料的滑动磨损行为

A series of novel steel–Ti(C,N) composites was fabricated by spark plasma sintering (SPS) and subsequent heat treatment. The hardness, indentation fracture resistance, and wear behaviour of the steel–Ti(C,N) composites were compared with those of the unreinforced samples, and their potentials were assessed by comparison with traditional cermet/hardmetal systems. The results showed that with the addition of 20wt% Ti(C,N), the wear rates of the newly examined composites reduced by a factor of about 2 to 4 and were comparable to those of cermets and hardmetals. The martensitic transformation of the steel matrix and the formation of in situ carbides induced by heat treatment enhanced the wear resistance. Although the presence of excessive in situ carbides improved the hardness, the low indentation fracture resistance (IFR) value resulted in brittle fracture, which in turn resulted in poor wear property. Moreover, the operative wear mechanisms were investigated. This study provides a practical and cost-effective approach to prepare steel–Ti(C,N) composites as potential wear-resistant materials.     

轧制工艺参数对钒铌微合金钢沉淀强化的影响

应用 Gleeble-1500 热模拟试验机研究了控轧控冷参数对钒铌微合金钢性能的影响。研究结果表明,钒、铌复合加入比单独加入钢中具有更好的沉淀强化效果。对应于最佳强化效果的轧后冷却速度在 3—4℃/S之间。较低的变形速率与变形温度有利于沉淀相析出。钒含量增加,促使铌在更低的温度下析出,因而使高温应力峰移向低温区。     

冷速对钒微合金化钢形变诱导相变组织的影响

通过热模拟实验考察了在连续冷却条件下,不同的冷却速度对钒微合金化钢的形变诱导铁素体相变(DIFT)组织演变的影响规律.结果表明,大变形后的冷却速度越大,实验用钢的铁素体晶粒越细小;在相同的冷却速度下,钢中的钒含量越多,铁素体晶粒越细小.在较低的冷却速度下,钢中的钒含量越多,钒的碳氮化物析出越多;当冷却速度较大时,钒微合金化实验用钢中没有钒的碳氮化物析出.