Anabarites belong to small shelly fossils (SSF), which occur widely in the Lower Cambrian strata of Yangtze Platform in South China. They are phosphate shell in composition and represent the earliest stage of the Cambrian bioradiation of Bilateria, the so-called “Cambrian Explosion”. In this study, we attempted to separate Anabarites fossils from Lower Cambrian dolostones, and we obtained samples of both the fossils (SSF) and the granular phosphates (GP). Isotopic analyses were performed on samples of SSF, GP, and matrix dolostone (DH-23). The results showed that the δ³⁰Si values of the quartz filling in fossils celoms, and the siliceous materials in granular phosphates are -0.6‰ and -0.7‰, which is different from normal sedimentary siliceous rocks from the Lower Cambrian strata (0—0.7‰) as reported by Li et al., but is consistent with the data for siliceous rocks and cherts of submarine hydrothermal origin. It is likely that a later hydrothermal replacement could have taken place in the SSF-bearing sedimentary rocks. The oxygen isotope values of the phosphate of SSF and GP are 16.8‰ and 17.0‰, respectively. These are significantly higher than the Neoproterozoic phosphate ores (10.9‰—13.9‰) as reported by Ling et al.， hence, late diagenesis and hydrothermal replacement may not have caused a significant change in the oxygen isotope compositions of the small shelly fossils, and the calculated temperatures (25.4—26.3℃) for palaeo-seawater using a SSF phosphate oxygen isotope thermometer are therefore considered here as the upper limit of seawater temperature in the Early Cambrian ocean of the Yangtze Platform.     

钇对ZrCuNiAl系合金非晶形成能力的影响

利用X射线衍射(XRD)和差示扫描量热分析(DSC)研究了添加钇对Zr55 Cu30Ni5Al10Y(=0,1,2,3,4)非晶合金体系玻璃形成能力的影响。用铜模铸造获得的Zr55 Cu30Ni5Al10Y(=0,1,2,3,4)块体非晶合金的临界尺寸从直径6 mm增加到20 mm。分析认为,微量钇的添加可以与合金中的残留氧形成氧化物,降低氧对合金形成非晶态结构的负面效应。因此添加适量的稀土元素钇有利于提高Zr55 Cu30Ni5Al10Y非晶合金体系的玻璃形成能力。     

二氧化硅气凝胶的常压制备及其特性研究

以正硅酸乙酯为原料,先采用溶胶-凝胶法制备湿凝胶,然后浸泡在反应溶液中进行老化,再利用正己烷进行溶剂交换,三甲基氯硅烷进行表面改性,最终获得轻质多孔二氧化硅气凝胶. 进一步考察了凝胶时间随乙醇和水的不同加入量和pH值的变化,利用FTIR、XRD和SEM等方法对二氧化硅气凝胶表征. 结果表明,所制备的疏水SiO2气凝胶的密度、比表面积和孔隙率分别为77～200 kg·m-3,500～750 m2g-1和85%～95%,其颗粒尺寸为50～200 nm.     

Poly-Si TFT有源驱动OLED单元像素电路的参数设计

根据有机电致发光显示器件(OLED)的发光特性及多晶硅 薄膜晶体管 (Poly-Si TFT)的工作特性, 对Poly-Si TFT有源驱动OLED的源极跟随型双管 单元像素驱动电路进行了理论计算和模拟仿真, 确定了单元像素中的各种器件参数; 通过AI M-Spice的模拟仿真了整个像素电路工作状态, 对器件参数进行了优化.     

考虑损耗时拉曼放大泵浦光的偏振效应

利用高非线性和较大吸收损耗的光子晶体光纤制作光纤拉曼放大器,是当前的一种趋势,这导致泵浦光非线性旋转效应明显增强.本文在考虑吸收损耗条件下,研究了泵浦光的非线性旋转问题,首次得出了连续光条件下的解析解.结果表明,输入线偏振光与圆偏振光都不会产生非线性旋转,只有椭圆偏振光才有非线性旋转.旋转是绕着邦加球的纬线进行,s_3保持不变.随着吸收损耗的增加,有效长度变小,相对的旋转速度变慢.这表明,如果光纤对于泵浦光的吸收越强,越有利于拉曼放大.     

薄带连铸取向硅钢的热轧孪生行为

薄带连铸流程下取向硅钢粗大λ晶粒(〈100〉//ND,normal direction)的“遗传”会导致磁性能恶化.为解决这一问题,针对取向硅钢的热轧孪生行为开展研究,结果表明:凝固组织粗大的取向硅钢在650℃热轧时可产生大量112〈111〉形变孪晶,这与具有高层错能的硅钢在较高温度下难以孪生变形的传统认知不同.热轧过程中复杂的应力状态降低了变形孪晶的取向依赖性,由于具有更高的储存能,孪晶界/孪晶界及孪晶界/晶界交叉点成为再结晶形核的优先位置,大大提高了常化过程中的再结晶率,受沿孪晶界应变分布及孪晶间距离的限制,沿孪晶界形核的再结晶晶粒通常呈“饼状”,最终形成以细小且取向漫散的再结晶晶粒为主的常化组织,消除了初始凝固组织中有害的粗大λ晶粒.     

偏振滤波一维二元光子晶体的实现

用一维时域有限差分方法（1-D FDTD）分析一维二元光子晶体的偏振滤波特性,数值模拟各种因素下一维二元光子晶体的滤波特性.数值结果表明：掺杂层在中间位置时偏振分离度好;掺杂层的厚度与周期层厚度相差越大分离效果越好;2组元折射率相差越大越易形成带隙;入射角越大禁带越窄偏振的分离度越好.     

等离子喷涂铁基非晶/晶体复合涂层的工艺–结构–性能关系

本研究试图通过优化等离子喷涂参数来开发一种Fe基非晶/晶体涂层,该涂层主要成分来自一种贫乏的铁基合金（Fe_92.6C_3.5P_1.4Si₂Mn_0.5）。这种合金是钢铁厂高炉产出的生铁剩余废料。为了经济有效地重新利用这种残留物,这种合金在合成时对成分进行了最少的修改。同时,本研究还探讨了涂层的结构、机械、腐蚀和磨损性能对喷涂参数（等离子功率、主气体流速、送粉速度和间隔距离）的依赖性。X射线衍射表明,在最优的喷涂参数下沉积的涂层存在无定形/晶体相。在较低等离子功率和最高气体流速下沉积的涂层表现出更好的密度、硬度和耐磨性。所有涂层都表现出良好的耐腐蚀性（腐蚀环境:3.5wt% NaCl 溶液）。机械、磨损和摩擦学研究表明,单一的工艺参数优化无法提供良好的涂层性能;相反,所有工艺参数在优化涂层性能都具有独一无二的作用,它们主要通过控制飞行中的颗粒温度和速度分布,以及熔滴撞击基材之前的冷却模式来控制涂层性能。     

铁电液晶的非线性和动态响应

研究了双手性分子铁电液晶３Ｍ２ＣＰＯＯＢ的非线性光学性质。实验发现这种材料具有很大的自发极化强度（〉１０＾－３Ｃ／ｍ＾２），较易获得相位区配及二次谐波的输出。测得二阶非线性光学系数、二次谐波强度与温度和液晶盒厚度的关系。在阶梯电场作用下，二次谐波强度动态响应为几百微秒到几百毫秒。     

缩醛酯在Perkin类反应中的形成及其晶体结构

通过Perkin类反应得到3个新的化合物1,2和3. 利用X-射线单晶衍射仪测定化合物1和2的晶体结构.实验表明:化合物1,(E)-2-{2′-[3″-(1″-乙酰基-吲哚)基]乙烯}基-8-羟基喹啉乙酸酯为单斜晶系,空间群为P2(1)/c,晶胞参数为:a＝2.265 66(9) nm, b＝2.019 90(8) nm,c＝0.794 45(3) nm,α＝90°,β＝90.715(2) °,γ＝90°,V＝3.635 4(2) nm3,Z＝8,Dc＝1.353 mg/m3,μ＝0.091 mm-1,F(000)＝1 552,R1＝0.052 6 and wR2＝0.140 9.化合物2,1-(1′,1′-二乙酰基)甲基苯并噻吩为斜方晶系,空间群为Pccn,晶胞参数为:a＝1.701 16(8) nm,b＝2.001 71(8) nm,c＝0.766 28(3) nm,α＝90°,β＝90°,γ＝90°,V＝2.609 36(19) nm3,Z＝8,Dc＝1.345 mg/m3,μ＝0.251 mm-1,F(000)＝1 104,R1＝0.034 2 and wR2＝0.098 5. 本文报道了这2个化合物的晶体结构.化合物1、2和3的形成表明,在这类Perkin反应中,酸的存在将导致缩醛酯的形成,从而降低了缩合产物的产率.