Al熔体与非晶SiO2的扩散反应动力学

利用SiO2玻璃尺寸大的特点,研究了Al与SiO2玻璃反应组织和反应动力学.实验发现,长时间反应可以得到Al/Al2O3复合组织,在Al熔体和Al/Al2O3复合组织间存在扩散过渡层.测定了扩散过渡层和Al/Al2O3复合层的生长动力学.分析了扩散过渡层的动力学规律.讨论了Si对扩散过渡层和复合层形成动力学的影响, 发现Al/Al2O3复合层形成的抛物线动力学特征.     

三维连通网状SiC陶瓷/Zr基非晶复合材料动态变形特征

利用分离式霍普金森压杆装置,对三维连通网状SiC陶瓷/Zr基非晶复合材料进行不同应变率下的动态压缩实验,采用扫描电子显微镜研究复合材料的动态变形特征和断口形貌.结果表明:复合材料的动态压缩强度随着打击速度的增加而增加;试样发生劈裂和剪切断裂,陶瓷相断口形貌为层片状、台阶式的解理断裂,非晶合金发生粘性流动,断口形貌复杂多样.在应变率＞104 s-1的冲击载荷下,非晶相表现为软化后的多重脊状条带.复合材料断口上大量的非晶球形液滴及非晶软化条带的发现表明,绝热温升在非晶变形与断裂过程中起重要作用.     

Fe76Si7.6B9.5P5C1.9合金带的纵向巨磁阻抗效应

利用单辊快淬法制备宽0.35 mm,厚0.033 mm的Fe76Si7.6B9.5P5C1.9非晶薄带,具有明显的纵向巨磁阻抗效应,最大磁阻比达到754%.氮气保护条件下进行热处理的样品,最大阻抗比和灵敏度都有明显提高,440℃退火1 h的样品最大阻抗比达到1 196%,灵敏度为715%/(A·m-1).     

Influence of B,Al and Nb addition on the glass forming ability and stability of mechanically alloyed Zr-Ni amorphous alloys

We investigated the influence of minor additions of B,Al and Nb that have representative atomic sizes on the glass forming ability (GFA) and stability of Zr-Ni amorphous alloys during mechanical alloying. The results show that the minor addition of B,Al or Nb does not shorten the initial time of the full amorphization reaction or improve the glass forming ability of the Zr-Ni alloys at a low rotation speed. However,B addition can effectively improve the mechanical stability of the amorphous phase against me...     

金属与糖化酶共催化糊精水解加氢制山梨醇的研究

通过考察糖化酶对糊精水解的影响因素,确定了合适的糖化酶水解条件.通过对金属催化剂筛选,寻找出催化性能较好的Ru-P非晶态合金为加氢催化剂.采用超声辅助化学还原法制备了负载型Ru-P非晶态合金催化剂,与糖化酶相结合,用于糊精水解加氢一步法制备山梨醇,得到较高的山梨醇收率.     

Ni7Zr2非晶合金制备及其磁性能研究

采用行星式高能球磨机,通过在室温下球磨纯元素混合粉末制备出Ni7Zr2非晶合金粉末.应用X射线衍射(XRD)、差热分析(DTA)和扫描电子显微镜(SEM)对不同球磨时间的混合粉末进行了研究.结果发现球磨时间对混合粉末的结构及颗粒形貌均存在显著影响.随着球磨时间的增加,Ni、Zr颗粒发生严重塑性变形,并且通过冷焊团聚起来,形成具有层状结构的复合颗粒.由于磨球的剧烈撞击,使得结构发生了严重的畸变,从而破坏了原有的有序结构而形成了无序结构.另外,在进一步球磨过程中,合金的晶粒不断减小,形成高体积分数的晶界,而金属粉末不断地发生塑性变形,形成了点缺陷、位错等高密度缺陷,晶格发生严重的畸变,晶体自由能也相应不断上升,最后产生了非晶转变.磁性能测量表明,该合金粉末具有较好的软磁性能.     

Rapid reductive degradation of azo dyes by a unique structure of amorphous alloys

An Fe-based amorphous alloy was found to significantly enhance the reductive degradation of an azo dye in aqueous solution. The surface-area normalized rate constant was up to 2.0 L m-2 min-1 at room temperature,an order of magnitude larger than any previously reported value. The activation energy of the degradation process was calculated according to the Arrhenius equation,and a much lower value than those previously reported was obtained. Valence band measurement indicated that a depressed valence band maximum and a widened empty band were established in the amorphous ribbon. The unique structure of the amorphous alloy is important-it may reduce the activation energy of the degradation process and enhance the activity of the electrons,thus accelerating the degradation process.     

非晶半导体中 S-W 效应的范氏键模型

本文给出了硅基非晶态半导体 Staeber-Wronski 效应(SWE)的范氏键模型,该模型认为硅基非晶态半导体的光致变化是网络内范氏键光致断裂引入的隙态所致。     

金属／非晶硅势垒低频电容中等价的隙态密度分布

本文证明:在一定条件下,描述非晶硅隙态密度分布的三种基本函数,即均匀分布、指数分布和双曲分布,在计算金属/非晶硅势垒低频电容时也是等价的.并通过测量室温时低频势垒电容,得到了隙态密度分布函数模型等价的标准.     

电沉积Ni-P非晶合金的研究

研究了以NaH_2PO_2为磷的供给剂的Watts电解溶液在电沉积Ni-P合金时,温度和NaH_2PO_2含量对镀层含磷量和沉积速度的影响;非晶镀层在热处理时结构的变化和硬度变化受热处理温度的影响;以及镀层结合力和针孔度随膜厚的变化,Ni-P非晶合金的良好耐蚀性能。