高铝熔渣物相析出演变规律研究

以改善高铝渣浸出性能为目标,采用DSC实验和SEM-EDS检测方法,研究了高铝渣控温冷却过程中物相析出规律,考察了降温速率、n(CaO)/n(Al₂O₃)和MgO含量对铝酸钙渣物相析出演变规律的影响.结果表明:当降温速率加快时,熔渣凝固过程趋于更大程度的偏析,C₂S相变愈不充分,粒度粗化,劣化了自粉行为和浸出条件;随着调高渣中n(CaO)/n(Al₂O₃),C₁₂A₇的析出温度升高,物相析出活性按照CA→C₁₂A₇→C₃A逐渐增强;当渣中含有MgO时,物相中出现C₂MS₂,不利于C₂S物相转变,更为重要的是MgO富集在含铝物相中形成Q相,显著恶化氧化铝浸出率和收得率.     

航空铝合金预腐蚀疲劳寿命退化规律

航空铝合金材料在服役过程中常因腐蚀损伤而导致疲劳断裂问题,通过采用扫描电镜及疲劳寿命测试等方法,研究了不同预腐蚀损伤对2xxx铝合金在不同应力比下疲劳寿命的影响,探讨了预腐蚀损伤对疲劳裂纹萌生扩展的影响机理.结果表明:预腐蚀损伤对2xxx铝合金材料疲劳寿命的影响显著,材料的疲劳性能随着腐蚀损伤程度的增加而明显下降.同时建立了预腐蚀损伤对材料疲劳极限的影响系数C-T-R模型,材料疲劳极限的影响系数C随着预腐蚀时间的增加或者应力比R的增加而变大.断口分析表明,预腐蚀损伤的存在导致裂纹萌生寿命大大缩短,裂纹萌生由单源转变为多源,并且均萌生于腐蚀坑处.     

成形速度对7075半固态模锻组织均匀性的影响

在半固态模锻过程中,经常会出现液相偏析现象,使零件出现"弱点"或"弱区",这些"弱点"或"弱区"通常又是潜在的裂纹源和服役条件下失效的起因。为了分析研究半固态模锻液相偏析的影响因素,应用DEFORM-3D软件对7075铝合金半固态模锻充型过程进行了模拟,研究了成形速度对7075铝合金杯形件充型过程的影响规律。在模拟的基础上,利用压力机及杯形实验模具,进行了半固态7075铝合金流变模锻成形,研究了成形速度对7075铝合金杯形件半固态模锻组织均匀性的影响。模拟和实验结果表明:成形速度越高,充型越不平稳;在压头温度400℃、成形比压50 MPa、合金温度628℃的条件下,随着成形速度的增加,杯形件的液相偏析度增加,组织越不均匀,当成形速度为5mm/s时,杯形件的液相偏析度高达18.2%。     

Al熔体与非晶SiO2的扩散反应动力学

利用SiO2玻璃尺寸大的特点,研究了Al与SiO2玻璃反应组织和反应动力学.实验发现,长时间反应可以得到Al/Al2O3复合组织,在Al熔体和Al/Al2O3复合组织间存在扩散过渡层.测定了扩散过渡层和Al/Al2O3复合层的生长动力学.分析了扩散过渡层的动力学规律.讨论了Si对扩散过渡层和复合层形成动力学的影响, 发现Al/Al2O3复合层形成的抛物线动力学特征.     

消除7A05铝合金板材各向异性的热处理工艺

为提高7A05铝合金热轧板材的综合力学性能并减少各向异性,对7A05铝合金固溶、预时效、时效和形变处理等工艺对性能的影响进行了系统的研究. 比较了供货态、形变态、回归(RRA)态和采用预时效形变热处理的优化态热处理工艺对综合力学性能的影响. 结果表明:固溶的最佳温度为480 ℃,单级时效最佳工艺为120 ℃,24 h,双级时效中第一级时效最佳工艺为90 ℃,8 h,最佳形变为25%. 通过金相组织和力学性能测试结果表明:由于预时效析出促进形变热处理时亚晶等轴化,优化态强度高,进一步改善了合金性能,减少了轧制板材纵横向力学性能各向异性倾向.     

三种麻醉剂对动物组织器官生理特性影响的探讨

主要探讨了氨基甲酸乙酯、水合氯醛、戊巴比妥钠等3种麻醉剂对动物组织器官生理特性的影响,以寻找动物生理实验过程中更适合某种组织器官的麻醉剂。提出:水合氯醛更适合于对动物心肌收缩力、胃运动等实验的研究;戊巴比妥钠更适合于对动物心率、骨骼肌、坐骨神经、十二指肠、子宫等实验的研究,可供研究动物生理的科研工作者参考。     

Potential release of hydrogen fluoride from domestic coal in endemic fluorosis area in Guizhou,China

Almost half of the total rural area of Guizhou Province and many regions within the 11 adjacent provinces in southwestern China have a long history(at least 70 years) of endemic fluorosis,including dental fluorosis and osteofluorosis along with its associated deformities and disabilities.Over decades of research,this specific type of endemic fluorosis has been defined as coal-burning fluorosis,which is distinct from drinking-water fluorosis.It is generally acknowledged that indoor burning and combustion of high-fluorine coal leads to food contamination,and fluorine then enters the human body.However,the exact chemical form of fluorine during its release and transfer to the body is still unknown.In the present study,21 domestic coal samples from outcrop and semi-outcrop coal collected in five villages with fluorosis were analyzed by time-of-flight secondary ion mass spectrometry(TOF-SIMS).The total mass fraction of sulfur in the samples ranged from 0.24%-5.58% and total fluorine content ranged 90.2-149.2 mg/kg.H3O+,H2SO4+ and HSO4-were detected in the samples by TOF-SIMS,which indicated that sulfuric acid hydrate(H2SO4.H2O) was present in the samples.F-was detected in all of these,which suggested the samples contain ionic fluorine compounds.Under certain circumstances,such as heating or burning,the prevalence and coexistence of the acid(H2SO4.H2O) and base(F-) would lead to a neutralization reaction producing volatile hydrogen fluoride(HF,bp = 19.5℃).This would be the chemical form of fluorine released from the coal.Further studies using HF and SO2 test tubes on headspace gas over coal samples heated to 200℃ in the laboratory and on headspace gas over stoves or chimney tops at rural residences confirmed the release of HF.     

点支式玻璃建筑中铸铝支承件承载性能

为了研究点支式玻璃建筑中铸铝支承件的承载性能,对3种典型铸铝支承件进行了足尺模型试验研究。按照实际工程中支承件的形式与尺寸制造模具,采用ZL105-T1和ZL111-T6这种铝合金材料铸造成足尺模型试件,借助万能试验机对试件进行加载试验,得出了试件的屈服荷载与极限荷载。根据试件的实际几何尺寸与材料属性,建立有限元模型对试验过程进行数值模拟。有限元分析结果与试验数据吻合良好,验证了有限元模型的可靠性。试验研究与有限元分析表明铸铝支承件的承载力较高,可以在实际工程中应用。     

泡沫A1-0．146wt．％Ti合金的制备及耐腐蚀性能研究

采用真空低压渗流铸造法,制备了泡沫A1-0．146wt．％Ti合金．分析了影响渗流法制备泡沫铝合金的主要因素,得到了制备泡沫合金的最佳条件：NaCl填料粒子预热温度300℃,合金液体浇铸温度760℃,填料粒子尺寸1～3mm．不同孔率泡沫AI-O．146wt．％Ti合金的模拟海水全浸实验结果表明：泡沫合金的耐腐蚀性能随着孔率增加显著下降．     

多取代5,6二氢-4-噻喃并咪唑酮类化合物的合成

在α-肉桂酰基二硫缩烯酮类化合物(1)的基础上,由2,3-二氢-4-噻喃酮化合物(2)与水合肼在温和条件下合成了多取代5,6-二氢-4-噻喃并咪唑酮类化合物(3),通过核磁共振、红外光谱、质谱及元素分析对所得化合物进行了表征,并对该反应机理进行了探讨.