溶体超声处理对7050铝合金铸锭微观偏析的影响

采用不施加超声、施加300、1 000 W功率超声三种工艺处理半连铸成形7050铝合金大扁锭,并对不同铸锭的第二相形貌、溶质元素含量变化进行了分析.结果表明:经超声处理的铸锭,非平衡共晶组织变得细小而分散;超声作用下Zn、Mg和Cu元素的成分曲线较常规铸锭平缓,1 000 W超声作用效果更加明显,其Zn、Mg和Cu的晶内相对溶质固溶度分别提高6.36%,19.44%和10.14%;超声处理增大了各溶质元素的有效分配系数k_e值,凝固初期的增幅为0.04~0.24;1 000 W超声作用使铸锭芯部及边部区域的微观偏析得到有效弱化,而芯部距离边部1/2处作用效果相对较差;由于超声加速了凝固前沿的冷却速度,使更多的溶质原子固溶到α-Al中,Zn、Mg和Cu元素在铸锭中的微观偏析得到了改善.      

超硬铝合金作为阴极在锌电积过程中的电化学行为

选取商业纯铝和超硬铝作为锌电积阴极,在ZnSO4-H2 SO4体系中通过电化学测试研究两种阴极的电化学行为,同时利用扫描电镜观察铝合金上电积锌初期形核,X射线衍射分析锌片结晶取向.研究结果表明：500 A·m-2电流密度下纯铝阴极的析出电位和交换电流密度分别为-1.541 V和7.74×10-11 A·cm-2,超硬铝阴极分别为-1.496 V和6.07×10-3 A·cm-2.合金元素的添加会增加初期形核位置,提高形核速率,而形核速率的提高在一定程度上抑制卤族元素对阴极的腐蚀.沉积3h后,锌片结晶取向没有发生变化.超硬铝易发生烧板和鼓泡,电流效率低,只有84.54%;纯铝电流效率达到88.04%,且沉积锌平整、光滑,但阴极板容易被卤族元素腐蚀.     

铝合金大铸锭超声半连铸多场耦合的数值模拟与实验研究

建立了超声场下直径630 mm的铝合金大铸锭热顶半连铸过程中多场耦合的数学模型,采用有限体积法及自定义函数获得超声作用下结晶器内声场、流场和温度场的分布,并进行工业化实验研究。综合工业实验和仿真结果分析超声对热顶半连铸铝合金大铸锭细晶的机理。模拟结果表明,超声波对宏观物理场的影响非常明显,施加超声后,辐射杆端面下方形成向上的回流区,强烈的紊流促进铝熔体的传质传热,减小液穴深度,使液穴更加平缓,同时初始凝壳点下移,过渡带变窄,铸锭中心处过渡带宽度从342 mm减小到120 mm左右。分析实验结果发现,经超声处理,铸锭组织普遍变得细小、均匀,平均晶粒尺寸减小103μm,最大最小晶粒尺寸差从135μm减小到64μm,且凝固组织晶界变细。     

工业纯铝极薄带异步轧制过程中的织构演变

采用异步轧制工艺制备出工业纯铝极薄带,并利用X射线衍射仪(XRD)和透射电子显微镜(TEM)对其织构演变和微观组织进行分析。结果表明,随着变形程度的增加,工业纯铝的晶粒主要向β取向线聚集,形变织构中铜型织构(C){112}〈111〉和黄铜型织构(B){011}〈211〉逐渐增强,轧至100μm厚时试样中晶体取向密度达到最大值26,轧至30μm厚时其取向密度值下降至16,并逐渐形成旋转立方织构(RC){100}〈011〉;形变储能剧烈增加诱发工业纯铝在室温下发生再结晶过程,使系统能量降低,导致织构强度下降。     

低温电解条件下铝电解用NiFe_2O_4-10NiO基金属陶瓷阳极Fe元素腐蚀行为研究

采用粉末冶金技术制备出铝电解用NiFe2O4-10NiO陶瓷基体和30(40Cu-Ni)/(NiFe2O4-10NiO)金属陶瓷阳极,并在低温电解条件下,对NiFe2O4陶瓷相中Fe元素的腐蚀行为进行研究。结果表明,在烧结过程中,NiFe2O4尖晶石陶瓷基体会在氮气中发生离解,在动态化学腐蚀试验和电解试验中,陶瓷相中的Fe元素更容易进入电解质;电解24h后,铝液中Fe、Ni、Cu的含量分别为0.45%、0.13%和0.03%。     

Enhanced photocatalytic activity of electrochemically synthesized aluminum oxide nanoparticles

In this study, aluminum oxide (Al₂O₃) nanoparticles (NPs) were synthesized via an electrochemical method. The effects of reaction parameters such as supporting electrolytes, solvent, current and electrolysis time on the shape and size of the resulting NPs were investigated. The Al₂O₃ NPs were characterized by Fourier transform infrared spectroscopy, X-ray diffraction, transmission electron microscopy, thermogravimetric analysis/differential thermal analysis, energy-dispersive X-ray analysis, and ultraviolet–visible spectroscopy. Moreover, the Al₂O₃ NPs were explored for photocatalytic degradation of malachite green (MG) dye under sunlight irradiation via two processes: adsorption followed by photocatalysis; coupled adsorption and photocatalysis. The coupled process exhibited a higher photodegradation efficiency (45%) compared to adsorption followed by photocatalysis (32%). The obtained kinetic data was well fitted using a pseudo-first-order model for MG degradation.     

Microstructure evolution and thixoforming behavior of 7075 aluminum alloy in the semi-solid state prepared by RAP method

The effects of isothermal treatments on the microstructural evolution and coarsening rate of semi-solid 7075 aluminum alloy produced via the recrystallization and partial remelting (RAP) process were investigated. Samples of 7075 aluminum alloy were subjected to cold extrusion, and semi-solid treatment was carried out for 5–30 min at temperatures ranging from 580 to 605°C. A backward-extrusion experiment was conducted to investigate liquid segregation during the thixoforming process. The results revealed that obvious grain coarsening and spheroidization occurred during prolonged isothermal treatments. In addition, higher soaking temperatures promoted the spheroidization and coarsening process because of the increased liquid fraction and the melting of second phases. Segregation of the liquid phase caused by the difference in fluidity between the liquid and the solid phases was observed in different regions of the thixoformed specimens.     

工艺参数对低铝钛GH600合金显微组织及析出相的影响

利用Gleeble3800热模拟实验机,对低铝钛GH600合金进行热压缩实验;利用金相显微镜研究工艺参数对显微组织演变规律的影响;利用透射电镜及能谱观察分析析出相、位错等微观结构。结果表明:提高变形量可以得到细晶组织,改善合金的使用性能,并且在大变形量下,动态再结晶容易进行,软化效果得到提高,在一定程度上改善合金的加工性能。当变形温度升高时,再结晶比例得到很大的提高,合金动态再结晶体积分数增大,位错密度降低,使加工容易进行。但当变形温度过高时,再结晶组织会出现粗化现象。低铝钛GH600合金的优选热加工工艺参数为:温度1 100~1 150℃,变形量60%。在这种工艺条件下,合金中的再结晶程度最高,再结晶晶粒没有出现粗化现象,并且析出相的成分、尺寸也为理想状态。     

铝阳极极化特性研究

分别测量了在阻挡型和多孔型电解质溶液中,铝阳极的恒电压和恒电流极化曲线.根据铝阳极极化曲线的特点,讨论铝在阳极氧化过程中有关阻挡层的形成、部分溶解,以及转化为多孔层等过程与极化电压和电流的关系.提出了在低极化电压或电流下,孔胚按“慢少成孔”机理在高极化电压或电流下按“快多成孔”机理的观点.     

并行工程在铝型材产品开发中的应用研究

介绍了当前我国铝型材产品开发技术状况及存在的问题,提出了一种新的、基于并行工程的铝型材产品开发模式,该模式为产品质量提高、开发周期缩短和开发成本降低提供了有效保证。讨论了铝型材新产品并行开发工程中的关键技术。