Reductive leaching of low-grade manganese ore with pre-processed cornstalk

Cornstalk is usually directly used as a reductant in reductive leaching manganese. However, low utilization of cornstalk makes low manganese dissolution ratio. In the research, pretreatment for cornstalk was proposed to improve manganese dissolution ratio. Cornstalk was preprocessed by a heated sulfuric acid solution (1.2 M of sulfuric acid concentration) for 10 min at 80°C. Thereafter, both the pretreated solu-tion and the residue were used as a reductant for manganese leaching. This method not only exhibited superior activity for hydrolyzing corn-stalk but also enhanced manganese dissolution. These effects were attributed to an increase in the amount of reductive sugars resulting from lignin hydrolysis. Through acid pretreatment for cornstalk, the manganese dissolution ratio was improved from 50.14%to 83.46%. The pre-sent work demonstrates for the first time the effective acid pretreatment of cornstalk to provide a cost-effective reductant for manganese leaching.     

中锰钢两相区退火奥氏体逆转变的数值分析

根据中锰钢热轧组织结构确立两相区奥氏体化的几何模型和初始条件,利用DICTRA动力学分析软件对中锰钢马氏体基体奥氏体化过程进行计算分析。在奥氏体化初期的形核过程中,马氏体中过饱和的碳锰元素从铁素体迅速转移到奥氏体并在相界面奥氏体一侧聚集。后续的相变过程中,碳在奥氏体中快速均化,但锰在相界面奥氏体一侧的聚集加剧。相变初期奥氏体界面推移速度比中后期高出若干个数量级,但随时间推移迅速衰减。相变初期相界面推移是碳扩散主导,相变后期界面推移受到锰在奥氏体中扩散速度制约。温度升高可显著提高相界面推移速度。达到相同数量奥氏体的情况下,低温长时退火有利于锰从铁素体向奥氏体转移并提高其在奥氏体中的富集度,从而提高奥氏体的稳定性。     

纳米孔壳聚糖接枝四(对-羧基苯基)锰卟啉催化氧化乙苯

为模拟细胞色素P-450酶的催化空腔场所,提高壳聚糖接枝四(对-羧基苯基)锰卟啉(Mn TCPP)的催化活性。采用冷冻干燥法制备纳米孔壳聚糖(np-CTS),并用酰化反应接枝四(对-羧基苯基)锰卟啉获得仿生催化材料―Mn TCPP/np-CTS,同时制备相应的无孔催化材料―Mn TCPP/nonp-CTS。用紫外可见光谱(UV-vis),傅里叶变换红外光谱(FT-IR),X射线(XRD),热重分析(TG)和扫描电镜(SEM)技术对其进行表征,并用于催化空气氧化乙苯研究。催化结果表明:在最佳反应条件下(145℃,0.8 MPa),纳米孔壳聚糖接枝四(对-羧基苯基)锰卟啉比无孔催化材料催化活性提高26%,醇酮收率提高38%。实验结果表明:纳米级空腔有利于充分发挥所固载的锰卟啉催化活性,最大程度地提高固载仿生催化材料的催化效率。     

贵州松桃某电解锰企业锰渣重金属污染特征及对植物生长的毒性效应

为综合评估电解锰渣重金属污染特征及任意堆弃对周边植物生长造成的危害,以贵州松桃某电解锰企业锰渣为研究对象,对渣样的重金属元素组成、含量及锰形态进行了分析测试,同时在实验室模拟研究了电解锰渣、浸出液及浸出残渣对白菜、油菜、黑麦草和紫花苜蓿种子的发芽势、发芽率、根长、芽长、鲜重、干重、发芽指数及活力指数的影响。结果表明:电解锰渣及其浸出液重金属主要为Mn,分别为28 000 mg·kg~(-1)、82.00 mg·L~(-1);电解锰渣及浸出液对植物根伸长的抑制效应明显大于对种子发芽的影响,对根伸长的抑制率达42.5%以上,甚至达到100.0%。     

南县地区用水现状及水质复杂的地下水处理

调查分析南县地区用水现状及地下水水质情况，并对铁、锰含量高，浊度大且轻度污染的地下水提出处理方案．     

磁电阻效应的研究进展

氧化物巨磁电阻效应在物理研究和磁存储、读写等实验应用方面的重要性,使得对该领域的研究成为当今凝聚态物理学和材料科学学中最前沿的领域之一.     

Fe-Cu合金体系中Cu析出规律

利用扫描电镜及能谱分析研究了Fe-7.8%Cu和Fe-2.1%Cu两种合金不同温度下铜的析出分布规律,以及合金中MnS夹杂物对铜析出的影响.部分试样加热到1600℃保温20 min后直接淬火得到;其他试样1 600℃保温20 min,炉冷到特定温度再保温20 min后淬火得到.结果表明:Fe-7.8%Cu合金在1600℃下淬火,含铜相在晶界、晶内均有析出;在1200℃下淬火,含铜相沿晶界析出;而1000℃淬火则有较大尺寸的ε-Cu相沿晶界析出.Fe-2.1%Cu合金在1 600℃和1 000℃下淬火,含铜相都沿晶界析出;而800℃淬火ε-Cu相在晶内析出.合金中MnS夹杂可以作为铜析出的有效形核核心.     

螯合法合成掺杂尖晶石型锂锰氧化物及其电化学性能研究

用螯舍法合成出掺杂镍和氯的尖晶石锂锰氧化物LixMn2-xNixO4-yCly。用能谱和原子吸收光谱分析测试了合成的样品的组成。分析了材料的电化学性能、FT—IR和XRD特性。结果表明：与没有掺杂的锂锰氧化物相比，掺杂量适当的样品其初始放电容量大，循环性能好，且在4．6～4．8V的电压平台较长。这归结于镍离子替换了部分处于16d的锰离子，使结构趋于更加稳定。