石墨烯/二氧化锰复合材料的制备及其电化学性能

通过水热法在160℃条件下成功制备了手风琴状石墨烯/MnO2复合材料.通过场发射扫描电镜、透射电镜、X射线衍射、X射线能量色散谱、BET法以及拉曼光谱对材料进行表征.结果表明,手风琴状二氧化锰与层状石墨烯之间具有十分高效的贴合,这种创新性设计有效地利用了石墨烯的高电导率、大比表面积以及二氧化锰的优秀赝电容行为.电化学测试结果给出在0.2 A·g-1时,样品的比电容高达138 F·g-1,数倍增强于单独的二氧化锰或石墨烯样品.     

Mn2+在Ti/SnO2+SbOx/PbO2电极上的电氧化研究

比较了Ｔｉ／ＳｎＯ２＋Ｓｂｘ／ＰｂＯ２电极与Ｔｉ／ＰｂＯ２电极在电解Ｍｎ＾２＋体系中的析氧极化曲线、Ｍｎ＾２＋的氧化极化曲线和电极寿命,发现加入中间层后的Ｔｉ／ＳｉＯ２＋ＳｂＯｘ／ＰｂＯ２电极对Ｍｎ＾２＋的电氧化有更好的催化活性和较长的使用寿命。用正交实验法探讨影响Ｍｎ＾２＋→Ｍｅ＾３＋＋ｅ电极过程的因素,找出以Ｔｉ／ＳｂＯｘ／ＰｂＯ２电极为阳极用无隔膜电解槽电解Ｍｎ＾２＋的最佳工艺条件,在此条件     

Cr和Mn元素强化的α钛合金的制备及其组织性能

在前人已经优化评估的Ti-Al-Cr-Mn四元热力学数据库的基础上,设计了一种新型α钛合金Ti-6Al-3Cr-1Mn,并利用分瓣式水冷铜坩埚成功制得了该合金。该合金在770℃下经轧机轧制成6mm厚的板材,然后于750℃保温90min进行真空退火热处理,出炉后置于空气中冷却。通过组织观察,发现无论是铸锭还是退火后的板材,室温下均为α型钛合金,与设计相符。室温力学性能试验表明,Ti-6Al-3Cr-1Mn合金的力学性能良好,平均屈服强度为894.9MPa,抗拉强度为926.7MPa,断后延伸率为15.2%。Ti-6Al-3Cr-1Mn合金与典型的α型钛合金TA15相比,室温强度相当,但塑性更好,成本更低。Ti-6Al-3Cr-1Mn合金的自腐蚀电位为-0.21V,自腐蚀电流密度为7.7×10-7 A·cm-2,耐腐蚀性能良好。     

明胶包埋壳聚糖/海藻酸钠茶多酚的缓释性能

以海藻酸钠和壳聚糖为壁材制备了茶多酚微胶囊,确定了最佳制备工艺条件为壳聚糖质量分数1．0％、海藻酸钠质量分数2．0％～3．0％、氯化钙质量分数5．0％,所制得的茶多酚微胶囊的包埋率最大,用明胶包埋茶多酚微胶囊,制备了茶多酚缓释复合体系,结果表明,用明胶包埋后的微胶囊可使茶多酚的缓释性能及稳定性有较大的提高。     

饲料中锰对日本沼虾抗氧化酶活性的影响

研究了日本沼虾(Macrobrachium nipponense)饲料中不同含量的Mn对虾体抗氧化酶活性的影响,以及在低氧胁迫下Mn对抗氧化酶的激活效果.结果表明,在投喂Mn的质量分数为150 ?g/g的饲料后,日本沼虾的超氧阴离子(O2·-)值降低,超氧化物歧化酶(SOD)、过氧化氢酶(CAT)和谷胱甘肽过氧化物酶(GPX)活性升高.Mn对虾体内SOD,CAT和GPX的激活作用表现出明显的剂量效应,饲料中Mn的缺乏或过量都使它们的活性受到影响.在低氧胁迫下,饲料中适量的Mn在一定程度上可提高虾体对低氧环境的耐受力.     

Fenton试剂对含锰矿井废水处理实验

为了解决矿井水中锰去除难度较大的问题,使用Fenton试剂对含锰矿井水进行处理。考察了H2O2:Fe2+、反应温度、H2O2的投加量、pH、反应时间对Fenton试剂氧化除锰的影响,并讨论了Fenton试剂高级氧化除锰的机理。研究结果表明:Fenton试剂对含锰矿井水的处理效果很好,原水中Mn2+的初始浓度为2 mg/L,当H2O2:Fe2+摩尔比为3:1,反应温度为25°C,H2O2的投加量为8 mmol/L,pH值为5,反应时间为10 min的时候,Mn2+的去除效率可以达到84%。Fenton试剂生成的具有强氧化性的.OH能有效处理矿井水中的Mn2+。     

PAN负载聚氨酯泡沫塑料富集分光光度法测定微量锰

报导用PAN螯合剂负载的聚氨酯泡沫塑料富集,分光光度法测定微量锰的简单易行方法。2吡啶偶氮—萘酚(PAN)在pH=9.5缓冲溶液中既做为负载剂又做为显色剂。锰离子富集之后,用1mol/L HNO_3洗脱,光度法测定。在0～0.12Mg/1ml锰离子范围符合比尔定律,方法用于麦饭石水和天然水中微量锰离子测定。     

Superior machinability of steel enhanced with BN and MnS particles

The strategy that replacing part of MnS with BN was proposed in order to decrease the sulfur content in sulfur based free-cutting steel. The effects of BN and MnS inclusions on the microstructure and machinability of the steel were systematically investigated. The results show that most of the BN and MnS inclusions exist individually in the steel and only a small amount of them are in a composite state forming either isolated particles or clusters of particles. In the case of multi-phased steel, the theoretical calculation predicts that the volume of large BN particles should be 0.7 times of the volume of large MnS particles. The machinability of this type of BN and MnS alloy steel over a wide range of cutting speeds ranging from a low speed appropriate for drilling to a high speed appropriate for turning is confirmed as being equal to or superior to that of an MnS reference steel, even though the sulfur content in the composite steel is only half that of the MnS steel. The aptitude for cutting effect of 240 ppm nitrogen and 115 ppm boron in the composite steel is demonstrated to be equivalent or even better than 1000 ppm sulfur in MnS free-cutting steel.     

50Mn18Cr4V无磁钢的热变形行为

通过高温压缩热模拟实验,研究了50Mn18Cr4V高锰无磁钢在变形温度为900~1100℃、应变速率为01~10s-1条件下的热变形行为.结果表明,VC第二相的应变诱导析出对50Mn18Cr4V的热变形行为产生重要影响.当变形温度为900~1000℃,应变速率为5s-1时,VC第二相不能充分析出,与应变速率为1s-1相比,对动态再结晶的阻碍作用减弱.应尽量使实验钢在高温段完成热加工,并适当提高应变速率.随着变形温度降低到950℃以下,材料的塑性变差,若以较低的应变速率变形,容易造成晶界开裂;应变速率过高,容易造成流变失稳,因此,以5s-1的应变速率变形,较为适宜.确定了50Mn18Cr4V无磁钢的再结晶激活能为7769kJ/mol.通过实验数据回归,建立了实验钢的高温变形抗力模型.     

高锰铝青铜ZCuAl8Mn14Fe3Ni2最佳熔炼化学成分筛选

运用正交试验设计的方法,筛选出了高锰铝青铜ZCuAl8Mn14Fe3Ni2熔炼的最佳内控化学成分范围,对开发生产该合金铸件具有重要的意义.试验表明:用该高锰铝青铜材料制造冶金备件产品时,锰含量宜以中限控制,铝含量宜以下限控制,镍控制在2%左右为最佳,铁控制在3%左右为最佳.