Photocatalytic enhancement of Mg-doped ZnO nanocrystals hybridized with reduced graphene oxide sheets

Hybridization of Mg-doped ZnO and reduced graphene oxide(MZO–RGO) were synthesized through one pot reaction process. Crystallization of MZO–RGO upon thermal decomposition of the stearate precursors was investigated by X-ray diffraction technique. XRD studies point toward the particles size with 10–15 nm,which was confirmed by transmittance electronic microscopy,and also indicates that graphene oxide has been directly reduced into its reduced state graphene during the synthesis. Graphene hybridized MZO photocatalyst showed enhanced catalytic activity for the degradation of methylene blue(MB). The degree of photocatalytic activity enhancement strongly depended both on the coverage of graphene on the surface of MZO nanoparticles and the Mg doping concentration. The sample of 2 wt% graphene hybridized 5 at% Mg-doped ZnO showed the highest photocatalytic activity,which remained good photocatalytic activity after nine cycling runs.     

ZnO的用途及其薄膜的制备方法

1引言近年来,由于光电子器件潜在的巨大市场,使光电材料成为研究的重点。ZnO薄膜是一种光学透明薄膜,纯ZnO及其掺杂薄膜具有优异光电性能,用途广阔,而且原料易得、价廉、毒性小,成为最有开发潜力的薄膜材料之一。目前,研究ZnO材料的性质涉及许多研究领域,其中包括:透明导电膜(T     

Mg2 掺杂ZnO薄膜制备及性能研究

通过溶胶-凝胶法,运用提拉技术在普通玻璃衬底上镀制出掺Mg2+的ZnO薄膜。通过测前驱物的热重-差热(TG-DTA)分析了前驱物的失水和分解的温度分别为100℃和280℃。采用显微照片和粗糙度照片可以看到薄膜质地均匀、致密。通过紫外-可见透射光谱(UV-VIS)可以看出掺镁ZnO薄膜的透过率在80%左右,具有较高的透过率。     

基于工业以太网和现场总线互连的氧化锌生产线网络控制系统

为使分布在不同地域的现场控制设备和控制系统有机地连接成一体,达到宽广地域的远程监视与控制,提出了基于以太网和现场总线互连的氧化锌生产线网络控制系统.该系统设计采用以太网作为企业网的上层设备之间的通信网络,将主控制器、操作员站及管理计算机连接起来.在企业网的最底层采用现场总线的形式.该系统具有成本低、结构简单、可靠性高、控制分散,可实现真正的“全分布式”控制等特点,能够组成开放式自动化控制系统;因而可克服以往集散控制系统和现场总线控制系统的局限性,大大降低控制系统的成本、提高控制系统的性能,并获得优良的性能价格比.     

CdTe/CdS量子点荧光探针测定痕量汞(Ⅱ)

在水溶液中合成巯基乙酸修饰的CdTe/CdS量子点(QDs),再基于Hg2+与CdTe/CdS量子点的荧光猝灭作用,建立用CdTe/CdS量子点作为荧光探针检测微量汞的新方法,并用该方法测定水中汞的含量。研究表明,pH值为6.24的磷酸缓冲溶液中,量子点浓度为3.75×10-4mol/L时,Hg2+离子浓度在2.3～150μg/L范围与CdTe/CdS量子点荧光猝灭强度呈良好的线性关系,相关系数为0.9985,检出限为0.87μg/L,回收率为99.0%～107.5%。该方法检测效果好,可用于实际样品分析。     

溶剂热法制ZnO纳米棒及其气敏性能

以乙酰丙酮锌为原料,采用溶剂热法首次合成了棒状ZnO纳米粉体,并对该材料在不同工作温度下的气敏性能进行了研究。通过XRD、SEM和TEM等测试手段,表征其物相与结构。该粉体为六方晶系的ZnO纳米棒,直径约为30 nm,长度约为100 nm,结晶良好。通过静态配气法发现:采用N型氧化锌纳米棒所制得的元件在270℃下,对体积分数为5×10-4的乙醇有较好的气敏性能,灵敏度为75,响应时间及恢复时间分别为30、60 s,说明制备的ZnO纳米棒是具有潜力的探测乙醇气体的气敏传感器材料。     

Al掺杂对ZnO薄膜晶体结构的影响

采用溶胶-凝胶工艺在Si(111)衬底上制备了ZnO薄膜,利用X射线衍射仪对薄膜的晶体结构进行了分析讨论.结果表明,当掺杂量Al3 浓度增大时,晶体产生的张应力使晶格常数变大,衍射峰向小角度方向移动;相反,当Al3 浓度减小时,压应力使衍射峰向大角度方向移动.     

生长时间对ZnO纳米棒形貌和光学性能的影响

在低温条件下，利用化学溶液沉积法（CBD）成功在Si（100）衬底上生长出近一维ZnO纳米棒阵列．采用X射线衍射（XRD），扫描电子显微镜（SEM）和光致发光谱（PL）对样品进行结构、形貌和光学性能分析．结果表明：产物为结晶良好的六角结构晶体．随着生长时间的增加，ZnO纳米棒的尺寸随之增大．PL测试表明产物有较好的光致发光性能，并且随着纳米棒尺寸的减小，紫外发射峰发生蓝移现象．     

硫化镉纳米粒子荧光淬灭测定柳氮磺吡啶

以硫代乙酰胺(TAA)与Cd2 在碱性溶液中反应制备了CdS荧光纳米粒子,该纳米粒子的荧光强度强烈的被药物成分柳氮磺吡啶所淬灭,建立了一种高选择性的测定柳氮磺吡啶的荧光分析新方法.结果表明,在pH值为11.2时,对于柳氮磺吡啶的检测下限可达到1×10-7g/mL,线性范围为5.0×10-7g/mL~1.0×10-4g/mL.方法已用于药片中柳氮磺吡啶的测定.     

Au/n-ZnO/p-SiC紫外探测器的研制和特性分析

采用宽禁带半导体n-ZnO和金属Au作肖特基接触,n-ZnO和同为宽禁带半导体p-SiC形成异质结,Ti,Ni,Ag合金作背底形成欧姆接触,研制出Au/n-ZnO/p-SiC结构的紫外探测器.测试分析了该器件的光谱响应特性,响应范围为200～400nm,在室温和一定反偏压下,响应峰值为313nm,半宽为65nm.同时测试分析了该器件的I-V特性,室温下,反向工作电压大于5V,反向击穿电压为70V.实验表明,此结构紫外探测器具有良好的紫外响应特性以及较低的反向漏电流和结电容.