山西铝厂赤泥性质的研究

为解决赤泥对环境污染及其综合利用等问题,利用ICP-MS,XRD,激光粒度分析和差热分析方法,对山西铝厂赤泥进行了检测,结果表明:有价金属在赤泥中有明显富集,是提取钛、钪、铌的良好原料;拜耳法赤泥中含有大量的含水化合物,可作为吸附剂用于环境污染治理;而烧结法赤泥的主要矿物是碳酸钙和硅酸二钙,作为道路基层材料的前景很好;同时由于其特有的化学组成,用于PVC填料,能使其具有良好的抗老化性能及热稳定性能。     

基于组态软件的无纺布定量测量系统研制

介绍了无纺布厚度X射线测量系统的研制,给出了具体的设计方案.运用组态软件对采集的脉冲频率进行处理计算,求出测量厚度,根据测量结果对生产工艺进行控制.同时系统具有厚度标定、偏差纠正等功能.应用实践证明,系统界面友好、操作方便、安全稳定,完全满足现场工况要求.     

含联苯结构环氧树脂/蒙脱土纳米复合材料的制备及其固化反应动力学

采用含联苯结构环氧树脂3,3＇,5,5＇-四甲基联苯二酚二缩水甘油醚(TMBP)与层间距为2.33 nm的有机蒙脱土(O-MMT)进行插层复合,并选用芳香型固化剂4,4 ＇-二氨基二苯甲烷(DDM),制备了TMBP/DDM/MMT纳米复合材料.采用非等温差示扫描量热法(DSC)研究该体系的固化反应动力学,求得其表观活化...     

磁控弧光增强等离子体CVD(化学气相沉积)法制备立方氮化硼薄膜

采用一种新的自行设计的磁控弧光增强等离子体化学气相沉积法制备立方氮化硼(c-BN)薄膜.现已成功地在单晶硅上制备出了含量较高的立方氮化硼(c-BN)薄膜.制备出的薄膜用傅立叶红外(FTIR)光谱和X射线衍射(XRD)谱来表征.同时研究了各个沉积参数(基底直流负偏压、弧光等离子体放电电流、气体流量比)对立方氮化硼薄膜制备的影响.     

离子注入减小条形射线探测器表面漏电的研究

选择高阻N型〈10 0〉单晶硅材料 ,X射线探测器为PIN管结构 .为了减少器件表面缺陷对暗电流的影响 ,在器件P区的两侧使用离子注入形成浅层低浓度N区 ,以减小器件的暗电流 .通过对比实验发现 ,当N区的注量增大时 ,在相同反向偏压条件下 ,器件的暗电流密度随之减小 ,同时击穿电压也相应减小 .为了减小器件的工作电压并进一步减小工作时的暗电流密度 ,还将器件的背面进行厚度减薄、抛光和AuSb/Au合金形成欧姆接触 .对减薄后的器件进行I V特性测量 ,由于工作电压大幅降低 ,器件正常工作时的暗电流密度大幅度减小 .同时在实验中发现温度对暗电流的影响非常大 ,将器件温度降低到 - 15℃时 ,暗电流密度可降低到 1nA·mm- 2 以下 .     

基于高频加强变换的焊接缺陷检测方法

根据X射线线阵实时成像检测压力容器的特点,提出焊缝图像处理及快速发现焊接缺陷的方法。利用自适应中值滤波方法和类间、类内方差比分割法及数学形态学方法对原始焊缝图像进行降噪和提取焊缝区域,并对提取的焊缝内部进行频域锐化的高频加强变换.仿真结果表明,自适应中值滤波能够有效去除噪声,并保持焊缝和缺陷的边缘细节;类间、类内方差比分割方法增强了图像目标与背景的对比,与数学形态学方法并用能准确地提取焊缝区域;高频加强变换能够为焊缝缺陷提供清晰的视觉效果,从而根据其显示的特点对焊接缺陷进行提取.     

PMNBP缩氨基酸席夫碱配合物的合成、表征和晶体结构

合成1-苯基-3-甲基-4-对硝基苯甲酰基-5-吡唑啉酮（PMNBP）缩苯丙氨酸甲酯席夫碱及其Ni（Ⅱ）、Co（Ⅱ）金属配合物,并对合成的配合物进行红外光谱的表征.利用X射线单晶衍射法测定配合物的晶体结构,结果表明二者均为六配位同构配合物.     

Structure and corrosion resistance of Al–Cu–Fe alloys

The microstructure and electrochemical properties of Al–Cu–Fe alloys with the atomic compositions of Al_(65)Cu_(20)Fe_(15),Al_(78)Cu_7Fe_(15)and Al_(80)Cu_5Fe_(14)Si_1have been studied.The alloys were produced by induction melting of pure elements with copper mold casting.The microstructure of the alloys was analyzed by X-ray diffraction and high-resolution transmission electron microscopy.The formation of quasicrystalline phases in the Al–Cu–Fe alloys was confirmed.The presence of intermetallic phases was observed in the alloys after crystallization in a form of ingots and plates.The electrochemical measurements were conducted in 3.5%NaCl solution.The electronic structure of the alloys was determined by X-ray photoelectron spectroscopy.The post corrosion surface of the samples was checked using a scanning electron microscope equipped with the energydispersive X-ray detector.It was observed that the Al_(65)Cu_(20)Fe_(15)alloy had the highest corrosion resistance.The improved corrosion resistance parameters were noted for the plate samples rather than those in the as-cast state.And the hardness of the Al_(65)Cu_(20)Fe_(15)alloy was significantly higher than the other alloy samples.     

Wool Surface Modification and Its Adhesion with Nano Finishing Agent

The launderability of wool fabrics treated by nano finishing agent influences directly the functional endurance of the treated wool fabric.In order to investigate the effect of wool fibers surface modification on the functional endurance of nano finishinp wool fibers,in this paper,for the first time wool fibers were chemically modified by using NaClO aqueous and KMnO4 aqueous,and then chemically modified wool fibers and native wool fibers were treated using nano ZnO finishing agent,respectively.The laundera...     

微束X射线荧光分析谱仪及其对松针中元素的分布分析

介绍了一种小型的微束X射线荧光分析谱仪,它是由导管X光透镜和能量色散X射线荧光分析谱仪组成.谱仪具有较高的空间分辨率和能量分辨率.使用本谱仪对松树针叶进行了微区分析,得出各种元素沿松针长度方向和横切面径向的分布规律.结果表明使用X光透镜的微束X射线荧光分析方法可以实现植物样品的微区分析,有助于进一步了解植物的生长与元素迁移的关系.