金属间化合物Ni3Al中的硼晶界偏聚特性的AES研究

本文应用俄歇能谱仪研究了不同化学计量比ＮｉＡｌ金属间化合物硼在晶界偏聚的特性。研究结果表明：硼在Ｎｉ３Ａｌ的各个晶界偏聚存在着不均匀性，硼在晶界的偏聚范围只有几个原子层，晶界结构及晶界化学环境是影响在晶界偏聚的决定因素。     

Fe_3Al的抗高温氧化和耐热腐蚀性能

在７００℃与８５０℃的高温下，Ｆｅ＿３Ａｌ金属间化合物表面形成了Ａｌ＿２Ｏ＿３保护膜，使其抗氧化性能远优于不妨钢，２％Ｃｒ（原子百分比）加入Ｆｅ＿３Ａｌ会导致氧化过程初期氧化速率的增高，在熔融的硫酸盐和高压锅炉的烟气中，Ｆｅ＿３Ａｌ的耐热腐蚀性能优于高温合金ＧＨ１３２．     

稀土在催化中的应用研究进展

稀土在催化中的研究和应用重要而广泛.文章分别从稀土氧化物、稀土金属间化合物及稀土分子筛3个方面对稀土在催化中的应用研究做了综述,并简要地分析了稀土催化剂的发展方向.     

Interface microstructure and formation mechanism of ultrasonic spot welding for Al–Ti dissimilar metals

The present study focuses on interface microstructure and joint formation. AA6061 aluminum alloy (Al) and commercial pure ti-tanium (Ti) joints were welded by ultrasonic spot welding (USW). The welding energy was 1100–3200 J. The Al–Ti joint appearance and in-terface microstructure were observed mainly via optical microscopy and field emission scanning electron microscopy. Results indicated that a good joint can be achieved only with proper welding energy of 2150 J. No significant intermetallic compound (IMC) was found under all con-ditions. The high energy barriers of Al–Ti and difficulties in diffusion were the main reasons for the absence of IMC according to kinetic ana-lysis. The heat input is crucial for the material plastic flow and bonding area, which plays an important role in the joint formation.     

黔西北某地伴生多金属低品位铁矿工艺矿物学研究

以化学分析、化学物相分析、透反射显微镜及EPMA为主要研究手段,对黔西北某地伴生多金属低品位铁矿的工艺矿物学特征进行了详细研究。该区含矿岩石为一套以火山成因为主的火山碎屑岩,矿石中有价元素除铁外,伴生有钛、铜、镓、铌等。载铁矿物工艺矿物学研究结果表明,矿石中铁主要以褐铁矿形式存在,与粘土矿物常常混杂出现,分布不均,团块大小差异也大,矿物间的嵌布关系复杂,提示依靠传统物理选矿难达到有用矿物的富集。除褐铁矿外,矿石中存在少量硅铁钛金属互化物。     

多相Mo-Si-B合金材料的性质

多相Mo-Si-B合金是非常具有吸引力的新型高温结构材料. 它熔点高、抗氧化性、抗蠕变性和室温断裂韧性好.阐述了Mo-Si-B微观结构对多相Mo-Si-B合金性能的影响,举例说明了多相Mo-Si-B合金的抗氧化性及断裂韧性比钼或钼的硅化物有明显提高.指出了存在的问题和今后努力方向.     

全层片组织 TiAl 基合金室温断裂机理的研究

在ＳＥＭ和ＴＥＭ下对Ｔｉ３３Ａｌ３Ｃｒ０．５Ｍｏ合金全层片组织薄板状和薄膜状试样分别进行了动态拉伸，并原位观察了试样中裂纹的形核及扩展过程．发现裂纹遇到内相界面时会发生偏转或裂尖发生钝化；主裂纹主要以使剪切带断裂而与微裂纹相连接的方式扩展并沿曲折路径进行．     

Analysis of EET on Ca increasing the melting point of Mg17Al12 phase

The present investigation showed that the additions of Ca to the alloy AZ91 were mainly dissolved into the Mg17Al12 phase and increased its melting point and thermal stability, which would have great effects on the high- temperature properties of AZ91 alloy. The empirical electron theory (EET) of solid and molecules was used to calculate the valence electron structures (VES) of Mg17Al12 intermetallic compound with and without Ca addition. The results showed that Ca dissolving in Mg17Al12 phase increased the strength of bonds that control the thermal stability of Mg17Al12 phase. Additions of Ca also made the distribution of the valence electrons on the dominant bond network more uniform in the whole unit cell of Mg17Al12. The theoretical conclusions well account for the experimental results.     

Ti-44Al-5V-1Cr-0.3Ni-0.1Hf-0.15Gd 合金的微观组织和拉伸性能

针对变形量达86%的锻造Ti-44Al-5V-1Cr-0.3Ni-0.1Hf-0.15Gd(原子分数,%)合金,对其进行热处理获得近层片组织,研究变形合金及其近层片组织的微观组织特征,并进行了室温、700℃和800℃拉伸实验.组织观察发现,近层片组织由层片团、分布于层片团界的β相以及弥散分布于基体的椭圆状Gd析出物组成.层片团的平均尺寸为40μm,层片组织、β相和Gd析出物的体积分数分别为93.73%、5.25%和1.02%.拉伸结果显示,室温下合金试样的平均抗拉强度为865MPa,平均延伸率可达4.17%,700℃时其平均抗拉强度和延伸率分别为643MPa和22%.Ti-44Al-5V-1Cr-0.3Ni-0.1Hf-0.15Gd合金不仅具有与高β相TiAl合金相当的塑性变形能力,且室温塑性也得到显著提高,这主要归因于β相体积分数的下降和Gd化合物对微观组织室温塑性的贡献.     

金属间化合物RFe8Mn4的结构和磁性

通过X射线衍射和磁测量研究了金属间化合物RFe8Mn4（R＝Y,Gd,Ho和Er)的结构和磁性。所有这些化合物都具有单相ThMn12型结构,其晶格常数a,c和单胞体积V随原子序数增加而减小。HoFe8Mn4和ErFe8Mn4化合物的热磁曲线上出现了补偿点,补偿点温度分别为95K和70K左右。本文还给出了这些化合物的居里温度和饱和磁化强度。