We explore nitric oxide (NO) effect on K in channels in Arabidopsis guard cells. We observed NO inhib- ited K in currents when Ca2 chelator EGTA (Ethylene glycol-bis(2-aminoethylether)-N,N,N′,N′-tetraacetic acid) was not added in the pipette solution; K in currents were not sensitive to NO when cytosolic Ca2 was chelated by EGTA. NO inhibited the Arabidopsis stomatal opening, but when EGTA was added in the bath solution, inhibition effect of NO on stomatal opening vanished. Thus, it implies that NO ele- vates cytosolic Ca2 by activating plasma membrane Ca2 channels firstly, then inactivates K in chan- nels, resulting in stomatal opening suppressed subsequently.     

淬火工艺对铬结构钢显微组织和机械性能的影响

本文研究了淬火工艺对低和中碳铬钢的显微组织,冲击韧性和断裂机制的影响,得出了无论是低碳,还是中、高碳钢,当奥氏体长大倾向稍大时,采取提高加热温度进行淬火的工艺均为不可取的结论。     

锌粉置换提金中铜影响的研究

在氰化冶金贵液中，Cu含量高达838．0mg/L，严重影响锌粉置换提金。通过多项研究试验，发现常温下搅拌24h，保持贵液中CaO浓度为400mg/L，可使Au的置换率达到99．83％，Cu只有1．5％。     

Preparation and properties of the SmOx/Rh(100) model surface

The preparation of SmOx/Rh(100) and CO adsorption on this model surface have been investigated with Auger electron spectroscopy (AES), X-ray photoelectron spectroscopy (XPS) and temperature programmed desorption spectroscopy (TDS). The oxygen adsorption on the SmRh alloy surface leads to the aggregation of Sm on the surface. The thermal treatment of this oxidized surface induces the further agglomeration of SmOx on the Rh(100) surface. Compared with CO TDS on the clean Rh(100) surface, three additional CO desorption peaks can be observed at 176, 331 and 600 K on the SmOx/Rh(100) surface. The CO desorption peak at 176 K may originate from CO adsorbed on SmOx islands, while the appearance of the CO adsorption peaks at 331 and 600 K, depending on the oxidation state of Sm, is attributed to CO species located at the interface of SmOx/Rh(100).     

超微粒子－有机聚合物薄膜的研究

我们用离子团束－飞行时间质谱（ＩＣＢ－ＴｏＦＭＳ）系统制备了金（Ａｕ）超微粒子－聚乙烯（ＰＥ）薄膜和Ｃ＿（６０）－聚乙烯薄膜。用透射电子显微镜（ＴＥＭ）分析了所制备的样品。它们的结构是Ａｕ超徽粒子镶嵌在多晶的ＰＥ薄膜中，其中Ａｕ原子团呈球形，直径分布在２．０－５．０ｎｍ窄范围内，当沉积基底温度为９０℃时，Ａｕ原子团相互靠近，几乎连接起来，但仍保持原来大小。基底温度为１４０℃蒸积的Ｃ＿（６０）－ｐＥ薄膜具有晶态结构，其晶格常数为１．４５４ｎｍ。     

化学气相沉积法制备光谱选择性碲膜

用化学气相沉积法制备碲薄膜,其步骤为：通过电化学方法制得碲化氢,碲化氢在室温下分解后在聚乙烯塑料箔上沉积得到碲薄膜.用傅里叶红外光谱仪、紫外/可见/近红外光谱仪、X射线衍射仪及扫描电镜表征碲薄膜的光学性能和结构.结果表明,化学气相沉积法在Mn-O覆盖的聚乙烯塑料箔上沉积得到的碲薄膜在大气窗口（8～13μm）光谱区域具有很高的透过率,同时能阻挡几乎所有的太阳光谱,表明碲薄膜是适用于辐射制冷装置的太阳光辐射屏蔽材料.     

分子间作用力对制备含有机废弃之水泥浆体影响研究

研究以水泥处理固体有机物时，有机物对水泥水化的影响。以膜流模式说明水份在水泥浆体内传输的现象。水膜存在半干之水泥浆体，其厚度小于100nm，膜流由离分压所驱动，而离分压来自分子间作用力。膜拟结果发现，水泥浆体内局部位置可用以进行水化之水量为Q=-Aslv／6vπ。当有机物添加在水泥浆体内时，会影响Hamaker常数，Aslv因此可能使膜流不稳定或完全抑制膜流，因而使水泥浆体内局部缺水，影响水化进行，造成成品强度降低，影响品质。     

关于少数民族音乐教育中复合型架构模式的若干思考

少数民族音乐教育的属性是“复合性”。在人才培养、教师队伍建设等方面应按照复合型架构模式进行建设。即以汉族音乐教育为基础，少数民族音乐教育为特色，并借鉴西方音乐教育的建构模式，使少数民族专业音乐教育在多成分、多层次平衡发展的基础上，力求双向发展的最大值——向民族纵深和现代化尖端的两极扩展。     

高效有机吸附膜吸附数学模型的建立

本文建立了高效有机吸附膜吸附数学模型，并与实验数据进行了比较，发现模型的数值计算结果与实验值基本相符，本模型具有较高的实用价值。     

水滴在撞击不同厚度水膜条件下产生的二次液滴特性

采用高速相机对水滴撞击水膜的飞溅过程进行了详细测量,分析了水滴撞击水膜的飞溅临界值、二次液滴的直径分布和二次液滴的速率等飞溅特性。结果表明,在实验参数范围内,当韦伯数增大时发生飞溅现象。此外,可以使用量纲为一参数K 来描述飞溅临界值,K=We·Oh^-0.4。当K值大于2 100时发生飞溅现象,二次液滴的量纲为一直径和二次液滴的量纲为一速率随着K值的增大而增大。水膜量纲为一厚度对二次液滴直径分布的影响不明显,但由冠状水花产生的二次液滴的平均量纲为一速率随水膜量纲为一厚度的增加而减小。