粉末送给率对激光熔覆层组织及性能的影响

在大量实验基础上，研究了激光熔覆过程对熔覆层组织和性能的影响。实验结果表明，随粉末送给率的增加，熔覆层厚度增加，熔覆层组织细化，熔覆层的硬度变化不大。     

粉末冶金Al-10%Ti复合材料的力学和耐磨性能

文章采用“冷压烧结+热挤压”的粉末冶金法制备出Al—10％Ti复合材料,研究了Al—10％Ti复合材料的孔隙率、抗拉强度、伸长率、硬度和耐磨行为。结果表明:与Al相比,Al-10％Ti复合材料的孔隙率较高,抗拉强度和伸长率较低,硬度和耐磨性较高;Al-10％Ti复合材料的磨损体积损失分别是Al的1/22.3及Qsn6.5-0.4的1/14.8,其磨损表面呈Al基体+Ti颗粒+孔隙的耐磨组织。     

化学镀法合成纳米Ag包覆Al_2O_3复合粉

以平均直径约为200nm的Al2O3粉为原料,以氨基溶液为镀液,硝酸银为初始材料,在反应过程中,控制最佳的还原剂浓度、反应时间等参量,使Al2O3表面获得均匀的金属Ag涂层·以HRTEM,XRD,EDS等手段研究了化学镀银所获得的Ag Al2O3复合粉的结构·结果表明,所有的Ag Al2O3复合粉具有壳 核结构,壳层由纳米非晶银和纳米银晶体颗粒构成,尺度分别是5nm和10nm·     

液相还原法制备纳米铜粉

以CuCl2和KBH4为原料采用液相还原法制备了铜粉，经XRD检测确定了反应生成物确为纳米铜粉，且经TEM检测粒径为20—40nm．该方法具有工艺简单，效率高，成本低等优点．并讨论了配位剂、反应温度等对反应结果的影响．     

铁基粉末烧结热锻材料的组织和性能

对比研究了两种不同成分铁基粉末烧结材料和粉末烧结热锻材料的显微组织和机械性能。结果表明，粉末烧结热锻材料综合机械性能显著高于粉末烧结材料。粉末烧结热锻材料的显微组织近似致密组织，密度可达7.60—7.70g/cm^3；表观硬度增加约50%；摩擦学特性显著提高。     

基于银薄膜/荷叶SERS效应直接检测婴儿配方奶粉中三聚氰胺

以天然荷叶为衬底,结合真空磁控溅射法沉积银薄膜,制备出了一种高效的表面增强拉曼散射(SERS)活性基底.研究发现银/荷叶基底对婴儿配方奶粉中掺杂的三聚氰胺(MA)表现出良好的识别能力,而不需作额外的样品预处理.对掺杂不同浓度三聚氰胺的奶粉溶液进行定量分析,在5~50 mg/L质量浓度范围内获得了较好的线性关系(线性相关系数R20.99).根据3σ准则,检测极限估计为1 mg/L.此外,银/荷叶基底具有良好的均匀性和重复性(相对标准偏差为7.64%和10.54%).该方法对婴儿配方奶粉中三聚氰胺的检测具有简单快速、成本低且无损等优点.     

西昌市玉米制种基地发展现状与展望

西昌市具有得到独厚的光、热、水和土地资源,生产的杂交玉米种子商品性好、产量高,是国家级杂交玉米制种基地,是国家西南片区唯一的热带血缘硬粒型玉米制种基地,发展前景广阔。     

水飞蓟种子（果实）形态学及萌发特性研究

系统地对水飞蓟种子进行了形态学和萌发特性的研究,实验结果表明：种子的千粒重分别是18.88 g和21.14 g.长度分别是0.66 cm,0.68 cm,厚度分别是0.16 cm,0.20 cm,宽度分别是0.26 cm,0.28 cm.哈师大植物园的水飞蓟种子在25℃时萌发率较高为90％.绥化中学的水飞蓟种子用赤霉素处理,结果100 ppm处理过的种子在25℃时萌发的比较好,萌发率为48％.     

Studies on induction hardening of powder-metallurgy-processed Fe-Cr/Mo alloys

Induction hardening of dense Fe-Cr/Mo alloys processed via the powder-metallurgy route was studied. The Fe-3Cr-0.5Mo, Fe-1.5Cr-0.2Mo, and Fe-0.85Mo pre-alloyed powders were mixed with 0.4wt%, 0.6wt%, and 0.8wt% C and compacted at 500, 600, and 700 MPa, respectively. The compacts were sintered at 1473 K for 1 h and then cooled at 6 K/min. Ferrite with pearlite was mostly observed in the sintered alloys with 0.4wt% C, whereas a carbide network was also present in the alloys with 0.8wt% C. Graphite at prior particle boundaries led to deterioration of the mechanical properties of alloys with 0.8wt% C, whereas no significant induction hardening was achieved in alloys with 0.4wt% C. Among the investigated samples, alloys with 0.6wt% C exhibited the highest strength and ductility and were found to be suitable for induction hardening. The hardening was carried out at a frequency of 2.0 kHz for 2-3 s. A case depth of 2.5 mm was achieved while maintaining the bulk (interior) hardness of approximately HV 230. A martensitic structure was observed on the outer periphery of the samples. The hardness varied from HV 600 to HV 375 from the sample surface to the interior of the case hardened region. The best combination of properties and hardening depth was achieved in case of the Fe-1.5Cr-0.2Mo alloy with 0.6wt% C.     