羰基钼化学气相沉积对模具表面改性的研究

以Mo(CO) 6 为物源在刀具钢回火温度以下实施了气相沉积超硬膜涂覆 ,经实验测试、分析 ,结果表明薄膜中含碳量是影响薄膜表观硬度的重要因素 ,并且该薄膜能改善刀具 (钻头 )的表面力学性能 ,增加其使用寿命     

Hydrothermal synthesis,characterization and nonlinear optical effect of orthorhombic phase Ca2B6O11·H2O

Hydrothermal treatment of calcium oxide and boric acid mixtures at temperatures between 234℃ and 300℃ has produced a colorless,transparent,orthorhombic compound Ca2B6O11.H2O.Of the seven known members of the series of hydrated dicalcium hexaborate containing boron-oxygen six-membered ring anionic group (B3O8)7-,only the title compound has been found to have the nonlinear optical effect.The second harmanic generation (SHG) effect of its crystal is larger than that of KH2PO4 (KDP).The reflection spectrum has shown that this compound has no absorption in the experimental wavelength range (800-240 nm).Its crystal structure is favorable for generating the nonlinear optical effect.     

聚氨酯增容PP/PA6共混物的研究

初步探索了在ＰＰ／ＰＡ６挤出共混过程中加入聚氨脂预聚物,通过就地形成ＣＴＣ－ＩＰＮ实现增容,研究结果表明,聚氨酸预聚物可以改善ＰＰ／ＰＡ６共混体系的相容性,使ＰＡ６分散度增加,提高了共混物的力学性能,聚氨酯预聚物在增容的同时,又可作为弹性体增韧使共混物的冲击强度大幅度增加,聚氨酸预聚物增容ＰＰ／ＰＡ６共混物时,预聚物的用量不宜过大且受预聚物结构的影响。     

二[(R-R'-环己烯基)-甲基取代茂]二氯钛和锆化合物的核磁共振和红外光谱研究

The NMR and FT\|IR Spectra of ten (ηC 6H\-9CRR′ Cp)\-2MCl\-2 (M=Ti,Zr) were measured.The constructions of the compounds were identified by 1H NMR and 13 C NMR spectra.All complexes are bonded by M\|Cp through center of Cp.The vibration modes were reasonably assigned,absorption of ν s M\|Cp (A\-1) (M=Ti and Zr) vibration all appear in 310?cm -1 or so,while ν as M\|Cp (B) appear around 410?cm -1 and 360?cm -1 for Ti and Zr respectively.The influence of the center metal atoms and the substituents upon the NMR and FT\|IR spectra were discussed.     

RALNEU计算机标准化考试系统的开发

针对东北大学轧制技术及连轧自动化国家重点实验室(RALNEU)的计算标准化考试系统的开发目标、功能和构成进行了分析,建立了该国家重点实验室的学生标准化考试系统的设计方案,基于客户/服务器模式,利用VisualC++60开发工具和面向对象的编程方法完成了该实验室的计算机标准化考试系统并投以使用·     

有机活性绢云母填充量对尼龙6 力学性能的影响

采用硅烷偶联剂对绢云母表面进行化学处理,并将其作为尼龙6的填充剂,通过改变活性绢云母填充量,研究增强尼龙6的力学性能．探讨硅烷偶联剂对绢云母的影响机理,分析活性绢云母填充量对尼龙6力学性能的影响规律．实验结果表明,活性绢云母填充绢云母填充尼龙6后的力学性能有显著的改善,活性绢云母填充尼龙6的数量存在着一个最佳值．     

2,6-二巯基嘌呤和2,6-二氯嘌呤的工业化合成

2-巯基-6-羟基-4,5-二氨基嘧啶和甲酰胺环化缩合,巯基化后得到2,6-二巯基嘌呤,再经氯化得到2,6-二氯嘌呤。对以上巯基化和氯化两个反应过程,在反应条件上分别采用盐酸代替醋酸和直接在浓盐酸体系中氯化进行改进,并用于工业生产。     

聚酰胺/橡胶复合材料纤维含量对拉伸性能的影响

纤维体积含量是决定纤维增强复合材料各项力学性能的一个重要参数.本文通过理论分析和实验,就纤维体积含量与聚酰胺6(锦纶)帘线/天然橡胶复合材料的拉伸强度、拉伸模量的关系进行了研究,得到了纤维体积含量的理论下界极限和上界极限以及许用的上界极限.实验结果提供了有关参数和影响因素,这将对聚酰胺6帘线/天然橡胶复合材料的细观力学设计提供依据.     

尼龙6与ABS共混物相容特性

尼龙6与聚丙烯腈－丁二烯－苯乙烯（ABS）共混物是在双螺杆挤出机上制备的,用马来酸酐聚合物和固体环氧树脂（双酚A型）作为这些共混物的相容剂。通过研究它们拉伸、扭矩、冲击性质和形态描述添加相容剂后的效果,结果表明,环氧树脂和马来酸酐聚合物的加入增强了尼龙6与ABS之间的相容性。