退火对大面积CdTe多晶薄膜薄膜的影响

对近空间升华法制备的大面积（30*40cm2）CdTe多晶薄膜用不同方法进行退火处理,用XRD、C～V、I～V等研究了退火条件,退火方式对薄膜结构和器件性能的影响。结果表明：刚沉积的CdTe多晶薄膜呈立方相,沿着（111）方向择优取向而退火后（111）（220）（311）等峰都有不同程度的增加。在纯氧气氛下,400℃退火还出现了新峰。随着退火温度的增加,电导激活能降低。经过连续退火装置在400℃下退火30分钟的电池,1/C2和V成线性关系,具有较高的掺杂浓度、较理想的二极管因子和较高的转换效率。     

Developments and unsolved problems in nano-lubrication

The main achievements in the area of nano liquid film, e.g. the distinction between different lubrication regimes, properties of thin film lubrication, the transition between liquid and solid state, ordered and disordered state, the failure of thin lubricant film, the equivalent viscosity and flowing characteristics of micro-fluid, the influence of solid surfaces on nano-lubrication, thin film lubrication of polymer, superlubricity, have been reviewed and some unsolved problems are discussed.     

纳米La 2O 3/TiO 2复合薄膜的抗凝血性研究

 采用射频磁控溅射方法制备了TiO₂薄膜和La₂O₃掺杂的TiO₂复合薄膜。利用扫描电子显微镜、X射线衍射,紫外可见光谱等材料表征方法研究La₂O₃掺杂对TiO₂薄膜的结构及抗凝血性能的影响。结果表明：La₂O₃掺杂促使TiO₂晶粒沿金红石相(110)晶面择优生长,能细化TiO₂纳米晶粒的大小,使薄膜的光学带隙由2.85 eV提高到3.2 eV。血小板粘附实验表明La₂O₃掺杂的TiO₂复合薄膜具有优良的血液相容性能;分析了复合薄膜的抗凝血机理。     

超临界水氧化水膜反应器的气固两相流分析

基于欧拉-拉格朗日方程的拉格朗日离散相模型,并建立颗粒的受力模型,对超临界水膜反应器内的气固两相流特性进行数值模拟。模拟并分析了颗粒直径、入口速度对超临界水膜反应器内的颗粒运动规律、分布特性以及颗粒接近多孔璧的参数的影响,并且分析了超临界水膜反应器中一定直径的颗粒的流体随体性。对研究和优化超临界水膜反应器的气固两相流特性具有一定的指导意义。     

Preparation and performance of novel LLTO thin film electrolytes for thin film lithium batteries

We prepared a series of lithium lanthanum titanate(LLTO) thin film electrolytes by radio frequency(RF) magnetron sputtering using LLTO targets in a N2 atmosphere.We also deposited the LLTO thin films in an Ar atmosphere under a same condition as references for comparison.The microstructure morphology and the composition of the thin films were investigated by X-ray diffraction(XRD),scanning electron microscopy(SEM) and X-ray photoelectron spectroscopy(XPS),respectively.Results show that the thin film has an amorphous structure with a uniform surface and it is free of pinholes and cracks.Impedance measurements reveal that the ionic conductivity of the electrolytes is beneficial for all solid lithium batteries dependent on the lithium content at room temperature.We found that the amorphous LLTO thin film performs well and it has potential application in microbatteries for use in microelectronic devices.     

油雾喷射碰壁过程中油膜形成的数值模拟分析

利用FLUENT仿真软件对油雾喷射碰壁过程中油膜的形成进行数值模拟;模拟条件如下:喷射速度v分别为30,80,100和120 m/s;油雾颗粒粒径d分别为3,5,7和10μm;喷雾距离D为50和65 mm.在上述条件下得到油膜厚度等高图,从而得出喷射速度、油雾颗粒粒径、喷雾距离对油膜厚度和油膜比率的影响.模拟结果表明:喷雾距离增加时油膜厚度和油膜比率都减少;在喷雾距离为50 mm时,速度为80 m/s的油膜厚度和油膜比率比较理想;同样条件下,油雾颗粒粒径在5μm左右时,油膜厚度和油膜比率较大.     

聚氨酯粉末涂料的制备与固化条件的研究

运用正交试验法研究了制备聚氨酯粉末涂料的工艺条件，讨论了树脂、固化剂、固化 催化剂等对涂膜性能的影响；并对涂料的固化条件进行了研究，得到了理想的固化温度和固化 时间．     

磁场对苯胺电化学聚合特性的影响研究

考察了磁场对苯胺电化学聚合特性的影响。实验结果表明，在磁场存在下，苯胺的循环伏安特性有明显改变。在磁场存在条件下得到的修饰电极的响应特性，如电极科率，电极的重现性等有较明显的改善。电极用于人体血液pH的测定，结果令人满意。