表面活性剂从碱性氰化液中萃取金机理研究第三相的产生

利用Fourier变换红外光谱(FTIR)、核磁共振(³¹P-NMR)、激光光散射(DLS)等方法研究了萃取后负载金有机相的溶液结构。实验结果表明,随着有机相金浓度和表面活性剂浓度逐渐增加,有机相含水量增加,有机相中磷酸三丁酯(TBP)的磷氧基伸缩振动向低频移动,核磁共振(³¹P-NMR)的化学位移向高场移动;同时有机相中开始有直径16nm左右的聚集体形成;随着胶团逐渐长大,有机相分成两相即产生第三相;第三相中有直径4nm左右的胶团存在。     

Microstructural formation of semi-solid AZ91D alloy stirred by electromagnetic field

With the help of an electromagnetic stirring device, alloy melt quenching and EBSD (electron back scatter diffraction)analysis technology, the microstructure of the semi-solid AZ91D magnesium alloy slurry stirred by rotational electromagnetic field under different stirring power conditions has been studied. The results show that the size of primary α-Mg phase is reduced obviously when the solidifying alloy melt is stirred by rotational electromagnetic field, moreover, the primary α-Mg grains are changed to fine rosette grains or spherical grains which are proved to belong to the different grains in three-dimension by the EBSD analysis technology. The results also show that the stirring power is an important processing parameter in the preparation of the semi-solid AZ91D magnesium alloy slurry. The larger the stirring power, the finer the primary α-Mg grains, the less the rosette primary α-Mg grains, and the more the spherical primary α-Mg grains. Theoretical analysis indicates that a stronger flow motion leads to a more even temperature field and solute field and a stronger man-made temperature fluctuation in the alloy melt so that the specially fine rosette and/or spherical primary α-Mg grains are formed in the semi-solid AZ91D magnesium alloy slurry.     

Effect of RE on the ignition-proof,microstructure and properties of AZ91D magnesium alloy

The magnesium alloy is prone to burn during die-casting, which limits its applications severely, so the effect of adding rare earth (RE) on the ignition-proof of AZ91D Mg alloy is studied. The results indicate that the addition of mischmetal RE elements has a remarkable influence on the ignition-proof property of the magnesium alloy. It is found that the ignition temperature of the magnesium alloy can be greatly raised by adding a proper amount of RE. When the amount is 0.1 wt%, the ignition temperature reaches 877°C which is 206°C higher than that of AZ91D without RE and the mechanical properties of the alloy are also improved. However, the amount of RE must be properly controlled because too much RE would induce grain coarsening and reduce the mechanical properties.     

中国省域投资环境的对比评价与分析

采用层次分析（AHP）与主成份分析相结合的方法,对中国大陆31个省市区的投资环境进行了总体性评价;以第三产业为例,采取关键要素评价法结合主成份分析,对省省（市区）域的产业对象性投资环境进行了评价,并就各评价结果作了简要对比分析。     

异步轧制AZ31镁合金板材组织

对不同总变形量、道次压下量、轧制温度以及轧制路径等工艺条件下所制备的AZ31镁合金板材的组织进行研究。研究结果表明：异步轧制有利于板材的晶粒细化,其晶粒粒度约为8．9μm,明显小于常规轧制板材的13．2μm;当总变形量由40％增大到80％时,晶粒粒度从40μm左右减小到30μm左右,出现了较多的孪晶;当道次压下量由5％增加到20％时,晶粒粒度从40μm左右减小到10～20μm,孪晶数量也随之减少;当温度由350℃升高到400℃时,晶粒粒度由20μm左右下降到10μm,且大部分晶粒为等轴晶;轧制路径的改变,使板材中的显微组织和孪晶数量产生改变,C路径中的晶粒细小,粒度约为10μm,D路径中的孪晶数量最少。     

高Zn含量对挤压Mg-Zn-Ca-Y镁合金微观组织和力学性能的影响

制备不同Zn质量分数的Mg-xZn-0.3％Ca-0.1％Y(x=7％,10％,13％)挤压镁合金,研究Zn质量分数对合金组织和力学性能的影响.研究结果表明:随着Zn质量分数增加,挤压合金的第二相体积分数增加,平均晶粒粒径和再结晶程度均先减小再增大,织构强度(极密度)则先升高再降低.与Zn质量分数分别为7％和13％的合...     

镁合金定向凝固技术研究的意义与进展

作为一种先进的材料制备技术与凝固研究技术,镁合金定向凝固技术具有很大的发展潜力与意义。文章分析讨论了镁合金定向凝固技术发展的必要性和研究与发展情况,并提出了该技术继续发展的重点与方向。     

小电流镀铜对阳极氧化AZ31镁合金耐蚀性的 影响

研究了小电流镀铜封孔对阳极氧化AZ31镁合金耐蚀性能的影响.AZ31镁合金阳极氧化后,在传统的镀铜液中进行阴极小电流处理.SEM、EDS和XRD分析结果表明,阴极小电流处理后,在阳极氧化膜的多孔层中发生了铜的沉积.在质量分数为3.5% NaCl水溶液中测试的极化曲线表明,AZ31镁合金阳极氧化后进行小电流镀铜处理,可以提高自腐蚀电位,降低自腐蚀电流密度,使耐蚀性能得到显著提高.     

AZ40镁合金的腐蚀图像识别及腐蚀行为分析

应用计算机图像识别技术研究了AZ40镁合金在模拟海水介质中的腐蚀行为。采用中值滤波、直方图均衡化方法对腐蚀图像进行预处理,通过数学形态学分析和小波分析提取了3个腐蚀图像特征参数：灰度分布方差、二值图像前景面积和能量特征参数用于全面、准确地描述镁合金的腐蚀行为。研究结果表明：腐蚀介质破坏镁合金表面自然氧化膜使腐蚀阻力减小;腐蚀由局部腐蚀开始快速扩展至全部区域;腐蚀产物堆积较慢,短时间不能为合金提供有效的保护,但随着较长时间的堆积则可增大腐蚀阻力,对合金产生一定的保护作用。     

锑对镁空气电池阳极性能的影响

为了探索放电性能更好的镁空气电池阳极,制备了3种镁合金,分别为Mg-6％Al-1％Zn,Mg-6％Al-5％Pb-1％Zn和Mg-6％Al-5％Pb-1％Zn-0.5％Sb,与工业空气阴极、NaCl溶液组成镁空气电池.利用X射线衍射、扫描电镜、电化学工作站和蓝电测试系统,检测镁合金阳极的微观组织和电化学性能.结果表明:在镁合金中加入质量分数为0.5％的Sb后,晶粒尺寸明显减小,第二相 β-Mg17 Al12细化,腐蚀电位负移,腐蚀电流密度减小.Sb元素明显减少了合金的析氢反应,提高了镁阳极的放电电压,使放电产物更容易从合金表面脱落.