A study on nano-sized NiO electrodes doping with C and Co prepared by electrochemical deposition-sintering processes and their capacitance performance

In the present work, it was studied that nanoosized NiO electrodes doping with C and Co were prepared by electrochemical deposition in an ethanol solution containing nickel nitrate and cobalt nitrate and sintering processes. The capacitance performance of such electrodes was also studied. The results reveal that samples obtained by electrochemical deposition first on a porous nickel cathode in an ethanol solution contain 0.5 mol/L nitrates, in which Ni(NO3)2 and Co(NO3)2 were mixed in a molar proportion of 8 : 2. After sintering at 300℃ for 2 h, they exhibited the best performance. XRD analysis illustrates that the essential phase of the product is NiO doping with certain content of C and Co. The particles of product imaged a spherical morphology with sizes of 20---30 nm in diameter, and with an average crystal size of 4--5 nm. The capacitance measurement of the simulating C/NiO capacitors indicates that a single electrode can reach as high as 410.0 F/g, and still maintain the value of 323 F/g after 30 recycles showed as a stabilized value with increasing recycles, when it was discharged at a current of 5 mA.     

电化学聚合四氨基钴酞菁修饰一氧化氮超微传感器的研究

用电化学聚合的方法制备了四氨基钴酞菁「Ｃｏ（ＴＡＰＣ）」修饰超微传感器,探讨了一氧化氮在超微传感器上的电化学催化氧化,结果表明,电化学聚合ＰｏｌｙＣｏ（ＴＡＰＣ）修饰超微传感器对一氧化氮具有较好的催化氧化作用;示差脉冲伏安法的结果表明,所研制的微型传感器具有较低的检测限和较高的灵敏度,生物体内常见的共存物质如抗坏血酸、儿茶酚胺类神经递质及其代谢产物、ＮＯ的降解产物ＮＯ２－等对于ＮＯ的测定不干扰,该微型传感器可以用于ＮＯ的活体检测。     

非当量成分Ni3Al基合金的有序——无序转变

利用建立在ＥＡＭ势基础睥和原子模型，计算了模拟非当量的Ｎｉ３Ａｌ基合金结构稳定性与和程有序（ＬＲＯ）度的关系，结果说明：非发量成分下，Ｎｉ３Ａｌ基合金有序无序转变温度随Ａｌ含量的增加而上升；其有序无序转变为形核长大的非均匀转变过程，理论上不存在稳定的均匀部分有序结构；其介稳的部分状态组织为完全有序我和完全无序区的混合组织，该结果能解释实验中所观察到的Ｎｉ３Ａｌ基合金有序无序转变。     

BCO光度法测定含镍铝合金中的铜

针对ＢＣＯ光度法测定含镍铝合金中铜稳定性差的缺点,用ＮＨ３－ＮＨ４Ｃｌ溶液作为缓冲介质对ＢＣＯ法作了改进,测定含镍铝合金中的铜含量,结果稳定、准确,再现性良好,方法简便而实用,特别适用于炉前分析．     

随焊氩气激冷控制铝/钢薄板焊接应力与变形数值模拟

采用有限元分析软件ANSYS,对不同焊接工艺条件下铝/钢异种金属薄板对接熔钎焊接过程进行数值模拟,建立了TIG电弧热源与氩气冷源模型,将常规焊接和随焊氩气激冷焊接的残余应力与变形进行对比分析,研究发现:随焊氩气激冷技术可使焊接纵向残余应力和变形分别降低32.8%和48.1%。为了验证数值模拟结果的准确性,进行了铝/钢异种金属薄板熔钎焊试验,将温度场与应力场的模拟值与试验值进行对比,结果显示两者吻合较好,表明随焊氩气激冷技术可有效控制铝/钢薄板焊接残余应力与变形。     

初始溶液中钴铁摩尔比对钴取代Fe3O4中铁的影响

从实际应用的角度出发,研究了初始溶液中钴铁摩尔比对室温下Co2 进入尖晶石结构的速率和程度的影响,过程中的氧化-还原电位和产物的化学分析、XRD以及IR等光谱分析的结果表明:初始溶液中较小的钴铁摩尔比有利于钴铁酸盐的生成.另外,随Co2 进入尖晶石结构,产物的晶面间距和晶格常数增加,红外振动吸收峰向高波数移动.     

钎焊后自然时效对3003/6xxx/3003复合铝合金性能和组织的影响

以6xxx系铝合金为芯材,3003铝合金为两侧皮材,经熔炼、铸造、复合、热轧、冷轧及成品退火制备了厚度为1.5 mm的3层复合铝合金。在600 ℃下模拟钎焊,经空冷后进行1、5、10、15、20、25、30 d的自然时效。结果显示：复合铝合金的强度、维氏硬度在自然时效初期快速增加,20 d后上升缓慢,30 d时抗拉强度、屈服强度、芯材维氏硬度达到最大,分别为242.3 MPa、122.9 MPa、84.0;芯材晶粒尺寸钎焊后较钎焊前略微长大,经不同自然时效时间的芯材晶粒平均尺寸大小相当,表明自然时效不改变芯材晶粒的大小;钎焊后以及经自然时效之后芯材中标识出的第二相为不规则的AlFeSiMnCu相。     

缺口应力集中对AL6061铝合金超高周疲劳性能的影响

利用超声疲劳试验方法考察了AL6061铝合金缺口试样的疲劳强度,分别对板状光滑试样和缺口试样进行了10~5周次～10~(10)周次范围内的对称疲劳试验。试验载荷为轴向拉压R=-1,加载频率为20 kHz,环境温度为室温,试验结果显示,在10~(10)周次范围内光滑试样和缺口试样的S-N曲线都出现了极限平台型的特征,存在传统疲劳理论定义的疲劳极限,且试样的疲劳性能随着应力集中系数的增加而降低。大多数试样疲劳裂纹萌生于表面,但随着疲劳周次的增加,AL6061铝合金疲劳缺口系数和疲劳缺口敏感系数增加。理论应力集中系数为2.54的试样其疲劳缺口敏感系数为0.89,理论应力集中系数为3.27的试样其疲劳缺口敏感系数为0.82,疲劳缺口敏感系数接近1,表明AL6061铝合金具有非常高的缺口敏感性,在实际工程应用中,须充分考虑应力集中对该材料及相应结构疲劳强度的影响。     

轧制工艺对7050铸轧板组织及性能的影响

为进一步提高含钛7050铸轧板的综合力学性能,探索合理的轧制工艺,本文研究轧制工艺对钛质量分数为0.2%的7050铝合金铸轧板组织和力学性能的影响规律及作用机理。结果表明,在440℃轧制温度且轧制变形量为75%时,合金的组织结构最好,性能最佳,再轧制后宏观微小裂纹明显愈合,板材成形性显著改善。合理的再轧制工艺可以促使铸轧板形成大量细小的再结晶晶粒,均匀化合金组织,显著提高板材的综合性能。     

稀土元素对快凝 AlFeVSi 合金性能和组织的影响

采用力学拉伸试验、透射电镜、扫描电镜等测试手段研究了稀土元素Ｅｒ,Ｙ,Ｃｅ对ＦＶＳ０８１２合金挤压棒材的力学性能和显微组织的影响,并通过考察稀土元素与合金组成元素之间的交互作用强度,定性地分析了稀土元素在快凝ＡｌＦｅＶＳｉ合金中的作用机理．结果表明,Ｅｒ促使粗大块状δ相的形成,加Ｙ则有较粗大的类球形第２相Ａｌ２０（Ｖ,Ｆｅ）２Ｙ的析出,而Ｃｅ没有生成其它相,但是明显细化了Ａｌ１２（Ｆｅ,Ｖ）３Ｓｉ硅化物质点,因此,采用Ｃｅ合金化可以改善合金显微组织,明显改善快凝ＡｌＦｅＶＳｉ合金力学性能．稀土元素对快凝ＡｌＦｅＶＳｉ合金组织性能以及第２相稳定性的影响主要与稀土元素晶体结构、原子半径、电负性等因素有关