Tea is one of the most popular beverages, consumed by over two thirds of the world's population; but the aluminum accumulation property of tea plant is becoming the focus of many researches because of aluminum's known adverse effect on human health. Investigation of the interactions of catechins with Al(3+) showed that during the interaction of catechins with Al(3+), the UV-vis spectrum of catechins was changed. Absorption of EGCG at 274 nm decreased and increased at 322 nm; EC and C's at 278 nm changed little. The ratio of Al(3+) to EGCG was 1:1 in pH 5.0 buffer solution; in pH 6.2 buffer solution, the ratio in the Al-EGCG complex was 1:1. Interestingly, while the ratio reached to over 2, after the complex of Al-EGCG started polymerization, the ratio in the polymer was 2:1. In pH 6.2 buffer solution, the complex behavior of C with Al(3+) was the same as that of EGCG, with a little difference for EC. When the ratio of Al(3+) to EC was <1, the complex in ratio was 1:2, but, the complex polymerized when the ratio of Al(3+) to EC was >1. It was found that the ratio of Al(3+) to EC in the polymer was 1:1. Polymerization of Al-catechin complexes might reduce aluminum absorption in the intestine. Kow value was also employed to study the properties of aluminum species in tea infusion (at gastric and intestine pH condition) and the effect of catechins and tea polyphenols on Kow in buffer solution. Results showed that Kow value rose much higher at the intestine pH than at the gastric pH. Tea polyphenols and catechins could greatly reduce aluminum Kow value in acetic buffer, indicating that these compounds may reduce aluminum absorption during tea intake.     

HPAM／AlCit交联聚合物溶液微孔膜过滤行为研究

分别采用孔径为1．2μm醋酸纤维素树脂核微孔滤膜及2μm混合纤维素树脂热压滤膜,考察了HPAM／AlGit交联聚合物溶液在恒压并流微过滤条件下的微孔膜过滤行为。结果表明,随反应时间的延长,该交联聚合物溶液中交联聚合物线团的数目逐渐增加,对于核微孔滤膜,其封堵作用遵循表面过滤机理,侧重反映封堵过程中交联聚合物线团的粒子特性;而对于网络型热压滤膜,过滤实验中交联聚合物线团对滤膜的封堵作用逐步由深度过滤过渡到表面过滤,侧重反映交联聚合物线团封堵非均—孔径滤膜所具有的非均匀封堵特征,即遵循大孔到中孔到小孔的封堵过程。     

球墨铸铁热浸镀铝的抗氧化性

为了延长铸铁工件的使用寿命,采用熔剂法将墨铸铁热浸镀铝,对镀层截面进行了形貌观察(SEM)、能谱分析(EDS)和衍射分析(XRD),测试了镀层的抗氧化性.结果表明,镀层由表面富铝层及扩散层构成,富铝层包含降温形成的针状FeAl3相,扩散层由FeAl3,Fe2Al5 物相组成,其形态呈舌状,并嵌入基体;氧化时镀层全部转变为扩散层,并能保持非常缓慢的退化速度,使球墨铸铁的抗氧化性显著提高.     

非贵金属新型催化剂催化松香歧化动力学研究

 以醇盐水解法制备的Ni-Al/MnO_x(Ⅱ)为催化剂催化松香歧化反应,研究了反应的动力学特征,得到其动力学方程为:lnw=kt+1.326 7,其中反应速度常数k与反应温度T间的关系为k=0.103 6 e^-8.854/RT.     

一种轻质高强碳纤维增强铝基复合材料

碳纤维增强铝基复合材料(Cf/Al)因为其潜在的高比强度、高比模量等优异的力学性能,在航空航天等工业领域有着极广泛的应用前景。本文采用挤压铸造法制备了增强相体积分数为50%的Cf/Al复合材料,并对其微观组织、比强度和比模量进行了研究。实验结果表明:复合材料组织致密,增强体分布均匀;Cf/Al复合材料具有较高的比强度和比模量,分别达到302MPa·cm~3/g和104GPa·cm~3/g,高于传统铝合金、镁合金等结构材料。     

反应气氛对铝热还原氧化钛合成氮化钛的影响

研究在流动氮气和埋炭条件下铝热还原氮化TiO2的反应过程,借助于X射线衍射(XRD)和扫描电子显微镜(SEM)分别测试和观察两种气氛中不同温度下处理后产物的物相组成和显微结构。结果显示,与流动氮气氛下一样,在埋炭气氛下采用铝热还原氮化法可以制备氮化钛复相材料,但处理气氛明显影响着铝热反应的程度及产物的形貌,在埋炭条件下处理后的产物中氮化钛含量、晶粒大小、晶格常数明显低于流动氮气氛下处理产物中上述各项值;热力学计算发现埋炭条件下铝除参与铝热还原反应外,还与炭粉床中氧发生反应,使参与铝热反应的金属铝不足,造成产物中有剩余的金红石存在。     

用铝渣和石灰对铁水预脱硫的热力学

通过热力学计算分析了Al在铁水中与氧和硫反应的平衡活度,当CaO和Al同时加入铁水中,适量的Al会提高CaO的脱硫能力.探讨了在Al的参与下,CaO作为脱硫剂时的脱硫热力学反应机理,以及Al2O3和CaF2对铁水脱硫的作用.     

自行车运动员公路训练中补液对血液与尿液中水合状态指标的影响

目的:在热环境下进行公路训练时,观察运动员血液与尿液中水合状态指标的变化,研究液体补充对运动员机体水合状态的影响。方法:选取9名自行车运动员进行2次试验,2次试验的间隔为2周。第1次运动员参加正常的公路训练(训练时间150min,路程为100km),在训练中不允许补液。第2次参加相同的训练,但在训练中允许补液。在训练前、训练后0.5h以及训练后6h,称量体重收集血样和尿样,测试血浆渗透压(Posm)、尿渗透压(U-osm)和尿比重(Usg)。训练后的6h之内,可自由补充水分和进食。结果:不补液时,训练后0.5h运动员平均脱水2.71±1.15%。和训练前相比,训练后0.5h的Posm(P=0.004<0.05)和Uosm(P=0.035<0.05)都显著上升,Usg值也上升但没有显著性。训练后6h,Posm下降,而Uosm和Usg上升,Uosm和训练前相比有显著性差异(P=0.008<0.05)。补液组的运动员训练后0.5h平均脱水0.95±0.51%。和训练前相比,训练后0.5h Posm、Uosm和Usg值虽都有上升,但都没有显著性差异。训练后6h Posm值低于训练前,而Uosm和Usg则继续升高。结论:(1)在运动员训练中Posm是监控运动员机体水合状态的灵敏指标;(2)训练前后运动员的体重差异也是反映运动员身体水合状态变化的简单实用指标;(3)摄入含电解质食物后的尿液指标(Uosm、Usg)不能反映运动员身体水合状态的变化;(4)一旦发生运动脱水,在6h内自由补液不能恢复到正常的水合状态。     

温度对泡沫铝制备过程的影响

讨论了泡沫铝制备过程中温度的影响,理论上分析了温度与熔体黏度、表面张力和发泡剂的关系,并通过实验探讨温度对泡沫铝孔结构和孔隙率的影响。     

Al—Ti—CN细化工业纯铝工艺参数测定

继Al—Ti—C中间合金之后,又开发了Al—Ti—CN中间合金,通过大量细化工业纯铝试验,从中间合金加入量、加热温度、保温时间等工艺试验,找出Al—Ti—CN中间合金细化工业纯铝的最佳工艺.对Al—Ti—CN用于工业生产提供有益参数.