Joint Strength with Soldering of Al2O3 Ceramics After Ni-P Chemical Plating

Ni-P alloy was chemically plated on Al2O3 ceramics to produce uniform alloy coatings at temperatures below 70~C. Cu metal was electroplated onto the Ni-P coating to facilitate the soldering and shorten the chemical plating time. Then, the electroplated ceramic specimens were soldered with 60 wt.% Sn-40 wt.% Pb solder in active colophony. The highest shear strength was acquired after the heat treatment at 170℃ for 15 min. The joint fractures mostly propagated along the interface between the ceramics and the Ni-P coating, with some fracture in both the ceramics and the Ni-P coating near the interface and some along the interface between the Cu and Ni-P coatings. The results show that ceramic surface roughness and the chemical plating parameters influence the coating quality, and that suitable heat treatment before the soldering also improves the adhesion between the ceramics and Ni-P coatings, thus strengthening the joints.     

多环境因素全面正交作用对铜绿微囊藻生长的效应研究

应用全面正交设计试验方案,研究与附生细菌共生时,温度、pH值、氮磷比三因素的不同水平组合与铜绿微囊藻生长的动态关系.结果表明,在环境温度25℃、氮磷比40∶1、初始pH为11时,铜绿微囊藻的最终生长量最大;温度25℃、氮磷比16∶1、初始pH为8.2时次之,微囊藻细胞的比增长速率相差约1.9%.统计分析结果显示,温度和初始pH值是影响铜绿微囊藻生长状况的显著因素.低温(10℃)显著抑制微囊藻的增长,低温时铜绿微囊藻对其他环境因子(pH值和氮磷比)的变化基本无响应;低pH值和较低氮磷比的组合也能明显抑制微囊藻生长,藻细胞不增长甚至处于负增长状态,此时温度对铜绿微囊藻比增长速率和最终生物量的影响程度也相应降低.     

夏秋季中街山列岛养殖海域营养盐水平及有机污染状况评价

根据2009年8月和10月夏、秋季节中街山养殖区调查数据,对该海域的营养盐水平及有机污染现状进行了分析评价。结果表明：中街山列岛养殖区无机氮夏季含量较高,16.7%的站位超四类水质标准,秋季明显下降,符合二类水质标准。活性磷酸盐含量夏、秋季无明显差异,而硅酸盐秋季较夏季明显升高。磷酸盐为该海域的限制因素,夏季尤为明显。该海域已呈富营养化状态,有机污染也已达到轻度污染水平,且夏季高于秋季。     

光限制胁迫协同pH与氮磷比对铜绿微囊藻生长的影响

以铜绿微囊藻为试验材料,应用正交试验法,在培养温度(25℃)及接种量相同的情况下,研究光限制胁迫协同pH与氮磷比对铜绿微囊藻生长的影响.影响铜绿微囊藻生长的因素顺序为:pH>光限制胁迫天数>氮磷比,pH为铜绿微囊藻生长的显著性影响因素(F=63.111 5),且在pH 10.5、氮磷比15∶1及光限制胁迫5 d的条件下正常光照培养4 d后藻细胞数量最大.     

菹草与铜绿微囊藻化感互作及其对藻抗氧化能力的影响

为能寻找到高效抑藻的高等水生植物,本文探讨了大型沉水植物菹草(Potamogeton crispus)在富营养盐条件下与不同密度铜绿微囊藻的互作效应.结果表明,活与死亡菹草均具有良好的抑藻性能,而且,活体菹草在富营养水体能与藻类发生相互化感作用.在藻的起始密度为105cells.mL-1时,菹草可强烈抑制铜绿微囊藻(Microcystis aerugilnosa)的生长;当藻的起始密度为107cells.mL-1时,菹草不仅抑藻效力大幅下降,其生物量也明显减少,表现为藻类对菹草生长的抑制作用.菹草对铜绿微囊藻化感作用的机制之一可能与降低藻细胞抗氧化能力有关,在菹草胁迫下,藻细胞的CAT,POD活力下降,MDA含量增加.该研究提示通过种植菹草有可能对蓝藻水华暴发的预防起到积极作用.     

人工浮岛中处理生活污水的试验研究

通过由美人蕉、灯心草、菖蒲多种植物构建的人工浮岛,试验研究其在动态条件下对生活污水中氮、磷的去除效果。结果表明:停留时间7d时,TN、NH4+-N、TP的去除率平均为66.4%、79.6%、78.1%。试验证明了组合植物的人工浮岛在生活污水处理中具有良好的应用前景。     

菹草腐解对洋河水库水质的影响

为研究菹草在不同营养盐条件下腐解对水质的影响,在贫营养(氮磷比10:1),中度营养(氮磷比15:1),富营养(氮磷比5:1),重度营养(氮磷比2.5:1)的条件下,利用硫酸作为腐解剂,比较了沉水植物菹草在室温下腐解时对洋河水库水质的影响。结果如下:1)各实验组菹草均在初始阶段吸收水中氮磷,当菹草腐解后,水中的氮磷含量增加;2)重富营养和富营养中的变化最大,其中的菹草也是腐解最多;3)在洋河水库中,必须加强菹草收割管理,防止菹草腐解内源污染。     

3-(1-烷氧甲酰基乙基)-2-取代苯氧基-3,4-二氢-2H-2-氧代-1,3,2-苯并氧氮磷杂环己烷的合成和表征

采用"一锅法",以丙氨酸异丙酯盐酸盐(AE)、水杨醛(SD)、硼氢化钠(NB)以及三氯氧磷(TCP)和五氟苯酚(FP)等为原料分别合成了N-(2-羟基苯甲基)丙氨酸异丙酯(1a)和3-(1-异丙氧甲酰基乙基)-2-五氟苯氧基-3,4-二氢-2H-2-氧代-1,3,2-苯并氧氮磷杂环己烷(MTF-2).合成条件是:①AE、SD、三乙胺(TEA)和NB的物质的量之比为1∶1∶2∶1.3时,AE和SD缩合反应温度为30℃、反应时间3 h后,降温至0～5℃再用NB还原反应0.5 h,1a收率为74.3%、纯度99.5%,同样方法合成了N-(2-羟基苯甲基)丙氨酸乙酯(1b)和N-(2-羟基苯甲基)丙氨酸甲酯(1c).②1a、TCP、TEA和FP的物质的量之比为1∶1.2∶2∶1.1时,于0～5℃将TCP滴加到1a与TEA组成的混合物中后升温至50～55℃反应4～6 h,再加入五氟苯酚继续反应10 h,MTF-2收率15.3%,纯度99.2%,同样方法合成了3-(1-异丙氧甲酰基乙基)-2-对硝基苯氧基-3,4-二氢-2H-2-氧代-1,3,2-苯并氧氮磷杂环己烷(MTN-2)和3-(1-甲氧甲酰基乙基)-2-对硝基苯氧基-3,4-二氢-2H-2-氧代-1,3,2-苯并氧氮磷杂环己烷(MTP-2).利用FTIR、~1H NMR、~(13)C NMR和~(31)P NMR方法表征了1a-1c和MTF-2等的结构,采用X-射线单晶结构分析方法证明MTF-2为单斜晶系,P21/n空间群,晶胞参数是a=1.511 57(6) nm,b=0.718 14(3) nm,c=1.904 40(7) nm,α=90.0°,β=95.705(3)°,γ=90.0°,氧氮磷杂环己烷是张力较大的半椅式构象存在.     

三种人工湿地植物处理农村生活污水的净化效果

采用潜流式人工湿地工艺处理农村生活污水,结果表明:不同植物对氨氮、总磷的去除能力差别较大,菖蒲对总磷和氨氮净化效果较好.试验7d后,菖蒲(Acorus calamus Linn)、再力花(Thalia dealbata)和梭鱼草(Pontederia cor-data)对总磷和氨氮的最佳去除率分别达到93.4%和77.6%、72.4%和71.6%、70.4%和70.9%,出水水质达到《广东省水污染物排放标准》(DB44/26-2001)的一级标准.该工艺投资少、处理效果好、操作简单、维护成本低.     

鸟粪石法同步回收发酵液中高质量浓度氮磷

以剩余污泥碱性发酵液为研究对象,考察鸟粪石沉淀法(MAP法)同时回收氮磷的最佳条件及对发酵液中有机物的影响.正交试验结果表明,分别以氨氮(NH4+—N)和正磷酸盐(PO43-—P)回收率为考察标准,四个环境因素的显著性分别依次为:nP∶nN>pH>反应时间>nMg∶nP、pH>nMg∶nP>nP∶nN>反应时间.各个环境因素的优化分析结果表明,最佳的回收条件为:pH=10.0、nMg∶nP=1.8、nP∶nN=1.6、反应时间为5 min,此时NH4+—N和的PO43-—P回收率分别为62.3%和94.1%,同时发酵液中的有机物随着鸟粪石沉淀的析出也略有减少.